Green separation and decomposition of crystalline silicon photovoltaic module's backsheet by using ethanol.

The treatment and recycling of discarded crystalline silicon photovoltaic modules (c-Si PV modules) has become a research focus, but few research have paid attention to the standardized treatment of c-Si PV module's fluorinated backsheet. Improper management of fluorinated backsheet can pose ecological and human health risks. Therefore, this study presents a novel method for processing the backsheet. The proposed approach entailed the utilization of ethanol (CH3CH2OH) to separate the backsheet from the PV module. Subsequently, the separated backsheet underwent decomposition using an alkaline ethanol (NaOH-CH3CH2OH) solution. Finally, the backsheet was recovered in the form of terephthalic acid (TPA) with a purity of 97.47 %. This recovered TPA can then serve as a valuable raw material for producing new backsheets, fostering a closed-loop material circulation. Experimental results demonstrate that immersing the PV module in a 75 % CH3CH2OH-H2O solution at a temperature of 343 K for 30 min achieved 100 % separation of the backsheet. Furthermore, subjecting the separated backsheet to a 60 min reaction in an NaOH-CH3CH2OH solution with a temperature of 343 K and a NaOH concentration of 1.0 mol/L achieved complete decomposition. The reaction mechanism was analyzed through characterization methods such as SEM/EDS, NMR, FTIR and XRD. This method is efficient, non-toxic organic reagent-free and environmentally friendly, so it holds significant potential for further development in the field of c-Si PV module recycling.

Enhanced removal of Pb from electrolytic manganese anode slime and preparation of chemical MnO2.

Electrolytic manganese anode slime (EMAS) is produced during the production of electrolytic manganese metal. In this study, a method based on vacuum carbothermal reduction was used for Pb removal in EMAS. A Pb-removal efficiency of 99.85% and MnO purity in EMAS of 97.34 wt.% were obtained for a reduction temperature of 950°C and a carbon mass ratio of 10% for a holding time of 100 min. The dense structure of the EMAS was destroyed, a large number of multidimensional pores and cracks were formed, and the Pb-containing compound was reduced to elemental Pb by the vacuum carbothermal reduction. A recovery efficiency for chemical MnO2 of 36.6% was obtained via preparation from Pb-removed EMAS through the 'roasting-pickling disproportionation' process, with an acid washing time of 100 min, acid washing temperature of 70°C, H2SO4 concentration of 0.8 mol·L-1, liquid-solid mass ratio of 7 mL·g-1, calcination temperature of 60°C and calcination time of 2.5 h. Moreover, the crystal form of the prepared chemical MnO2 was found to be basically the same as that of electrolytic MnO2, and its specific surface area, micropore volume and discharge capacity were all higher than that of electrolytic MnO2. This study provides a new method for Pb removal and recycling for EMAS.HighlightsVacuum carbothermal reduction method was used for Pb removal in EMAS.The removal efficiency of Pb was 99.85%.Chemical MnO2 with excellent discharge performance was prepared using treated EMAS.This study provides a new method for EMAS resource utilization.