ABSTRACT
OBJECTIVES: This study aimed to investigate bond performance of various resin luting cement (RLC) systems on enamel and dentin in different etching modes and to compare the RLC-tooth interface morphology using scanning electron microscopy (SEM). METHODS AND MATERIALS: The self-adhesive RLC systems used in combination with universal adhesives were as follows: Scotchbond Universal Adhesive Plus + RelyX Universal (3M Oral Care) and Clearfil Universal Bond Quick ER + SA Luting Multi (Kuraray Noritake Dental). These RLC systems were also used alone as self-adhesive RLC systems without universal adhesives (self-adhesive mode). The conventional RLC systems for comparison materials were as follows: BeautiBond Xtream + ResiCem EX (Shofu) and Tooth Primer + Panavia V5 (Kuraray Noritake Dental). Twelve specimens were prepared for each group to measure shear bond strength (SBS) in different etching modes. A stainless-steel rod was used as a substitute for indirect restorations. Bonded specimens were allocated to baseline (stored for 24 hours) and artificially aged (thermocycling [TC] for 10,000 cycles) groups. Representative treated tooth surfaces and RLC-tooth interfaces were observed using SEM. RESULTS: Three-way analysis of variance (ANOVA) revealed that all the factors (etching mode, storage period, and RLC system) had a significant influence on the enamel SBS values (p<0.05). Enamel SBS was significantly higher in etch-&-rinse (ER) mode than in self-etch (SE) mode, regardless of RLC system or storage period. Three-way ANOVA showed that all the factors had a significant influence on the dentin SBS values (p<0.001). Most RLC systems showed significantly higher dentin SBS in SE mode than in ER mode, regardless of storage period. However, the combination with Scotchbond Universal Adhesive Plus and RelyX Universal showed no significant difference in SBS values between etching modes at the baseline and showed a significantly higher SBS value in ER mode than in SE mode after TC. CONCLUSIONS: The self-adhesive RLC systems with universal adhesives tended to show higher enamel and dentin bond performance than the self-adhesive RLC systems alone. The morphology of treated tooth surfaces and resin cement-tooth interfaces were dependent on the RLC system and etching mode used. The RLC systems with primer application showed a thin, high-density layer above the intact dentin in both etching modes, suggesting chemical interaction.
Subject(s)
Dental Bonding , Resin Cements , Dental Cements/chemistry , Dentin-Bonding Agents/chemistry , Dental Bonding/methods , Dentin , Materials Testing , Shear StrengthABSTRACT
OBJECTIVE: The aim of this study was to determine the flexural properties and surface characteristics of a structural colored resin composite after different finishing and polishing methods, in comparison to those of conventional resin composites. METHODS AND MATERIALS: A structural color resin composite, Omnichroma (OM, Tokuyama Corp, Chiyoda City, Tokyo, Japan), and two comparison resin composites, Filtek Supreme Ultra (FS, 3M, St Paul, MN, USA) and Tetric EvoCeram (TE, Ivoclar Vivadent, Schaan, Liechtenstein), were used. The flexural properties of the resin composites were determined in accordance with the ISO 4049 specifications. For surface properties, 70 polymerized specimens of each resin composite were prepared and divided into seven groups of 10. Surface roughness (Sa), gloss (GU), and surface free energy (SFE) were investigated after the following finishing and polishing methods. Three groups of specimens were finished with a superfine-grit diamond bur (SFD), and three with a tungsten carbide bur (TCB). After finishing, one of the two remaining groups was polished with a one-step silicone point (CMP), and the other with an aluminum oxide flexible disk (SSD). A group ground with SiC 320-grit was set as a baseline. RESULTS: The average flexural strength ranged from 116.6 to 142.3 MPa in the following order with significant differences between each value: FS > TE > OM. The average E ranged from 6.8 to 13.2 GPa in the following order with significant differences between each value: FS > TE > OM. The average R ranged from 0.77 to 1.01 MJ/mm3 in the following order: OM > FS > TE. The Sa values of the OM groups polished with CMP and SSD were found to be significantly lower than those of the other resin composites, regardless of the finishing method. The GU values appeared to be dependent on the material and the finishing method used. The OM specimens polished with SSD showed significantly higher GU values than those polished with CMP. Most of the resin composites polished with SSD demonstrated significantly higher γS values compared to the other groups. Extremely strong negative correlations between Sa and GU in the combined data from the three resin composites and each resin composite and between Sa and γS in the OM specimens were observed; GU showed a strong positive correlation with γS in the same material. CONCLUSION: These findings indicate that both flexural and surface properties are material dependent. Furthermore, the different finishing and polishing methods used in this study were observed to affect the Sa, GU, and SFE of the resin composites.
Subject(s)
Dental Polishing , Flexural Strength , Aluminum Oxide , Composite Resins , Materials Testing , Surface PropertiesABSTRACT
PURPOSE: The present study evaluated the color-matching ability of a structural colored resin composite to compare it with resin composites employing pigments. METHODS AND MATERIALS: A structural colored resin composite (Omnichroma [OMC]), a supranano-filled resin composite (Estelite ∑ Quick [ELQ]), and a nano-filled resin composite (Filtek Supreme Ultra [FSU]) were used. Each resin composite was packed into a Teflon mold and pressed down with a clear strip under a glass slide. The specimens were light irradiated through the slide with a light-emitting diode curing unit. The thickness of the specimens (n=6) was measured with a digital caliper before being transferred to distilled water and stored at 37°C for 24 hours. The measurements of the optical characteristics of the specimens on a black-and-white background were performed using a spectrophotometer. D65 (CIE D65) was used as a light source for the spectrophotometer. Measurements were repeated three times for each specimen under each color-measurement condition, and average values for three same-shade specimens were calculated. One-way analysis of variance and Tukey post hoc tests were used (α=0.05). To determine its ability to match the color of artificial teeth, each shade of resin composite was placed in a cavity before performing color measurements. Using a spectrophotometer (CMS-35F S/C) with a flexible sensor, L*, a*, and b* values were obtained. RESULTS: The spectral reflectance curve of OMC showed that it reflected light wavelengths from 430-700 nm regardless of the background color and thickness of the specimens. The percentage of reflectance of ELQ decreased near wavelengths of 550-580 nm. Regarding the influence of background color on CIE L*, a*, b* values, the L* level showed significantly higher values for all tested materials with white backgrounds, and OMC was most affected by the difference in background color. However, a* values of ELQ and FSU were significantly higher with a black background than with a white background, and OMC showed a significantly higher value with a white background than with a black background. The b* values were higher with a white background than with a black background and were significantly higher for all three products, and these tendencies were much greater for ELQ and FSU. CONCLUSIONS: The ability of OMC to match the color of artificial teeth showed acceptable color compatibility, regardless of the shade of the artificial teeth and the depth of the cavity. However, ELQ and FSU showed reduced color compatibility, especially for a cavity depth of 3.0 mm. Excellent color matching ability was confirmed for the structural colored resin composite OMC, resulting in reduced color differences and therefore improving the esthetic appearance of the restoration, simplifying shade matching, and compensating for any color mismatch.
Subject(s)
Composite Resins , Dental Caries , Color , Humans , Materials Testing , Spectrophotometry , WaterABSTRACT
This study aimed to evaluate the filler contents (FCs), flexural properties, depth of cure (DOC), wear resistance, and handling properties of different low-viscosity bulk-fill resin composites (LVBRCs) and to determine the correlations between the tested parameters. Six LVBRCs, Beautifil-Bulk (BBF), Bulk Base Hard (BBH), Bulk Base Medium (BBM), Filtek Bulk-Fill Flowable Restorative (FBF), G-ænial Bulk Injectable (GBI), and SDR flow+ Bulk-Fill Flowable (SDR) were used. The DOC and flexural property tests were conducted according to the ISO 4049 specifications. The flexural strength, elastic modulus, and resilience were determined in 12 specimens that were obtained from each of the 6 materials. Sliding-impact-wear testing was conducted by evaluating the wear facets of the specimens using a noncontact profilometer and by confocal laser scanning microscopy. The handling properties of the LVBRC was assessed via extrusion force and thread formation measurements. The DOC for the majority of the LVBRCs was approximately 4 mm. Although the FCs and mechanical properties were material dependent, some LVBRCs exhibited excellent flexural properties and wear resistance. The LVBRCs demonstrated a wide range of extrusion force and thread formation. Regarding the correlations between the tested parameters, extremely strong negative and positive correlations were observed for the DOC versus extrusion force, flexural strength versus elastic modulus, maximum depth versus volume loss, and maximum depth versus thread formation. In addition, strong correlations between FCs and DOC, resilience, wear resistance, and extrusion force were observed.
Subject(s)
Flexural Strength , Mechanical Phenomena , Elastic Modulus , Materials Testing , ViscosityABSTRACT
CLINICAL RELEVANCE: The use of layering techniques is still advisable with many bulk-fill resins and should be the default unless a particular resin is known to not need it. SUMMARY: Objective: The purpose of this study was to investigate how layering techniques affect polymerization shrinkage stresses of high-and low-viscosity bulk-fill resins.Method: Six high-viscosity and six low-viscosity bulk-fill resins were evaluated. Aluminum blocks with a mesial-occlusal-distal (MOD) cavity were machined and randomly divided into groups for different filling techniques (bulk-fill vs horizontal layering vs oblique layering) and further subdivided according to type of resin (high- vs low-viscosity). The cuspal deflection resulting from the polymerization of bulk-fill resin bonded to a MOD cavity within an aluminum block was measured with a digimatic micrometer. Scanning electron microscopy analyses of tested resins were also conducted.Results: In the high-viscosity bulk-fill resins, cuspal deflection of the MOD cavity ranged from 11.2 to 18.2 µm with the bulk-filling technique, from 10.7 to 15.5 µm with the horizontal layering technique, and from 10.9 to 15.2 µm with the oblique layering technique. In the low-viscosity bulk-fill resins, cuspal deflection of the material ranged from 9.2 to 19.8 µm with the bulk-filling technique, from 8.2 to 15.7 µm with the horizontal layering technique, and from 8.4 to 16.4 µm with the oblique layering technique.Conclusion: Cuspal deflections for some high-and low-viscosity bulk-fill resins were significantly reduced by using layering techniques, but the resultant improvement of layering techniques was not applicable to all the bulk-fill resins used in this study.
Subject(s)
Composite Resins , Dental Restoration, Permanent , Materials Testing , Polymerization , ViscosityABSTRACT
CLINICAL RELEVANCE: Some bulk-fill flowable resin composites produce less cuspal deflection than a conventional incrementally filled flowable resin composites. SUMMARY: Objective: This study investigated simulated cuspal deflection and flexural properties of bulk-fill and conventional flowable resin composites.Methods and Materials: Five bulk-fill and six conventional flowable resin composites were evaluated. Aluminium blocks with a mesio-occlusal-distal cavity were prepared and randomly divided into groups for each of the different measurement techniques and were further subdivided according to the type of flowable resin composite. The simulated cuspal deflection caused by the polymerization of resin composite within an aluminium block was measured using a highly accurate submicron digimatic micrometer or a confocal laser scanning microscope (CLSM). In addition, the flexural properties of tested resin composites were measured to investigate the relation between cuspal deflection and flexural properties, and the resin composites were observed using scanning electron microscopy.Results: Simulated cuspal deflection of some bulk-fill flowable resin composites was found to be significantly lower than or similar to those for conventional counterparts, regardless of the measurement method. There were statistically significant differences in flexural properties depending on the material, regardless of the type of flowable resin composite. Pearson correlation analysis did not reveal a statistically significant relationship between flexural properties and cuspal deflection.Conclusion: These results indicate that some bulk-fill flowable resin composites exhibit lower cuspal deflection with the bulk-filling technique than is shown by conventional flowable resin composites using the incremental filling technique. Simulated cuspal deflection can be measured using either a micrometer or CLSM, but this experiment failed to show a significant relationship between cuspal deflection and flexural properties of flowable resin composites.
Subject(s)
Composite Resins , Flexural Strength , Materials Testing , PolymerizationABSTRACT
OBJECTIVE: The purpose of this study was to evaluate whether different enamel etching methods with reduced etching times would improve the bonding effectiveness of universal adhesives. METHODS AND MATERIALS: Three enamel etching methods, phosphoric acid ester monomer (PPM) etching, phosphoric acid (PPA) etching, and polyalkenoic acid (PLA) etching, and three universal adhesives, G-Premio Bond (GP), Prime&Bond elect (PE), and Scotchbond Universal Adhesive (SU), were evaluated. Initial bond strengths and fatigue strengths of universal adhesives to ground enamel and ground enamel etched for less than one, five, 10, and 15 seconds using different etching methods were determined. The bonded fatigue specimens were loaded using a sine wave at a frequency of 20 Hz for 50,000 cycles or until failure occurred with a staircase method. Atomic force micrograph (AFM) observations along with measurements of surface Ra roughness and modified surface area of enamel with different etching protocols were also conducted. RESULTS: The bond fatigue durability of universal adhesives to enamel with PPA etching from less than one to 15 seconds and PLA etching for 15 seconds was significantly higher than that to ground enamel. The bond fatigue durability to enamel with PPM etching was not increased compared with ground enamel. The surface Ra roughness and surface area obtained with AFM of enamel increased after PPA and PLA etching, and those values were significantly higher than those of ground enamel. Furthermore, surface Ra roughness and surface area with PPA etching were significantly higher than those with PLA etching. However, surface Ra roughness and surface area of enamel with PPM etching were similar to those of ground enamel regardless of etching time. CONCLUSION: PPA etching for less than one to 15 seconds and PLA etching for 15 seconds improve universal adhesive bonding, surface Ra roughness, and surface area of enamel. However, PPM etching is not effective, regardless of etching time, in improving bonds strengths, increasing surface roughness, and increasing surface area.
Subject(s)
Acid Etching, Dental , Dental Bonding , Dental Cements , Dental Enamel , Materials Testing , Phosphoric Acids , Resin Cements , Shear Strength , Surface PropertiesABSTRACT
We attempted to determine the effect of universal adhesive application time on dentin bond performance in different etching modes based on shear bond strength (SBS) tests and surface free energy (SFE) measurements. The five universal adhesives used were Adhese Universal (AU), Clearfil Universal Bond Quick (CQ), G-Premio Bond (GP), Scotchbond Universal (SU), and Tokuyama Universal Bond (TU). Bovine dentin specimens were divided into four groups of 10 for each adhesive. SBS and SFE were determined after applying the following surface treatments: 1) self-etch (SE) mode with immediate air blowing after adhesive application (IA treatment), 2) SE mode with prolonged application time (PA treatment), 3) etch-and-rinse (ER) mode with IA treatment, and 4) ER mode with PA treatment. Bonded specimens were subjected to SBS testing. The SFE of adhesive-treated dentin surfaces was measured after rinsing with acetone and water. Three-way analysis of variance revealed that dentin SBS values (p<0.001) were significantly influenced by the factors of adhesive type and application duration, but the factor of pre-etching was not significant (p=0.985). The manufacturer's instructions require longer application times for AU and SU, which showed significantly lower SBS values in IA than in PA treatment in both etching modes. However, the difference in the other adhesives was not significant between the IA and PA treatments in either etching mode. The total SFE (γS) was dependent on the adhesive and etching mode. The γS value of the initial group (SiC paper ground group) at baseline was 69.5 (mN·m-1) and that of the pre-etching group at baseline was 30.6 (mN·m-1). For all the adhesives, γS in SE mode showed significantly higher values than in ER mode, regardless of the application time. In SE mode, almost all universal adhesives tested showed lower γS values in PA treatment than in IA treatment. For ER mode, all the adhesives showed significantly higher γS values than those of the pre-etching baseline, regardless of the application time. Most adhesives did not show any significant differences in γS values between IA and PA treatments, regardless of etching mode.
Subject(s)
Dental Bonding , Dentin-Bonding Agents , Acid Etching, Dental , Adhesives , Animals , Cattle , Dental Cements , Dentin , Materials Testing , Resin Cements , Shear StrengthABSTRACT
The aim of this study was to determine the effect of aluminablasting on the bond durability of universal adhesives and adherent surface characteristics. Adhese Universal (Ivoclar Vivadent), All-Bond Universal (Bisco), Bondmer Lightless (Tokuyama Dental), G-Premio Bond (GC), and Scotchbond Universal (3M ESPE) were used in self-etch mode. The prepared bovine enamel and dentin specimens were divided into two groups based on whether they received an aluminablasting prior to application of the universal adhesives. The resin composite bonded specimens were stored in distilled water at 37°C for 24 hours, following which the shear bond strength (SBS) of half of the specimens was measured (24-hour group). The other half was subjected to 30,000 thermal cycles between 5 and 55°C before SBS measurement (TC group). Surface roughness (Ra) and surface free energy (SFE) of the adherent surfaces were also measured, and scanning electron microscopy observation and scanning electron microscopy/energy-dispersive X-ray analysis were carried out. Most of the adhesives did not show any significant differences in enamel SBS values between the two pretreatment groups, regardless of the storage condition. However, the dentin SBS values were significantly lower in specimens that underwent aluminablasting compared with those that did not, irrespective of their storage conditions. Significantly higher Ra and SFE values were observed in the enamel and dentin of specimens that underwent aluminablasting. Although aluminablasting increased the Ra and SFE values of enamel and dentin, its effect on the SBS value was dependent on the tooth substrate. In addition to C, O, Na, Mg, P, and Ca, the element Al was detected in the enamel and dentin of samples that had undergone aluminablasting. These results suggest that although aluminablasting of the tooth surface is thought to be effective for modification of the adherent surface, it may not enhance enamel bond performance and may also adversely affect the dentin bond effectiveness of the universal adhesives.
Subject(s)
Dental Bonding , Dentin-Bonding Agents , Acid Etching, Dental , Animals , Cattle , Dental Cements , Materials Testing , Resin Cements , Shear Strength , Surface PropertiesABSTRACT
The purpose of this study was to determine the influence of finishing and polishing methods on surface properties of bulk-fill resin composites through surface roughness (Ra) and surface free energy (SFE) measurements, and scanning electron microscopy (SEM) observations. Three bulk-fill resin composites, Tetric EvoCeram Bulk Fill (TB), Filtek Bulk Fill (FB), and Filtek Bulk Fill Flowable Restorative (FF), and two conventional resin composites, Clearfil AP-X (AP) and Estelite ∑ Quick (EQ) were used. Seventy cured specimens of each resin composite were prepared and divided into seven groups of 10 specimens. Ra, SFE measurements, and SEM observations were conducted after finishing and polishing procedures. Three groups of specimens were finished with a fine grit diamond bur (FDB), and three with a tungsten carbide bur (CBB). After finishing, one group from each type of finishing was polished with aluminum oxide flexible disks (SSD) and one group from each type of finishing was polished with diamond particles embedded in a silicone point (CMP). A baseline group of samples that were neither finished nor polished after removing the translucent strips from the surface was examined. Although the baseline group showed significantly lower Ra values than the other groups, most resin composites showed lower Ra values with CBB+SSD than with the other finishing and polishing groups. Among the tested resin composites, EQ showed significantly lower Ra values than the other resin composites, regardless of the finishing and polishing methods. On the other hand, AP showed significantly higher Ra values than the other resin composites in all finishing and polishing groups, apart from FB with FDB. For the finished specimens, most resin composites showed higher SFE values with CBB than with FDB. For the polished specimens, all the tested resin composites with CMP showed lower γS values than those with SSD, regardless of the finishing method. The baseline groups of TB and FB showed significantly lower SFE values than the other finished and polished groups. In the SEM observations, all the examined resin composites showed rougher surfaces after finishing with FDB than with CBB. However, when comparing the different polishing methods (CMP and SSD), surface smoothness appeared to be material dependent.
Subject(s)
Dental Polishing , Dental Restoration, Permanent , Aluminum Oxide , Composite Resins , Diamond , Materials Testing , Microscopy, Electron, Scanning , Surface PropertiesABSTRACT
The purpose of this study was to determine the effect of different adhesive application methods and etching modes on the dentin bond durability of universal adhesives under thermal cycling (TC). All-Bond Universal (Bisco), Adhese Universal (Ivoclar Vivadent), and Scotchbond Universal (3M ESPE) were used as adhesives. In total, 600 bovine teeth with exposed dentin were divided into 12 groups according to the type of adhesive and subjected to the following bonding procedures: 1) etch-and-rinse mode with active application; 2) etch-and-rinse mode with inactive application; 3) self-etch mode with active application; and 4) self-etch mode with inactive application. Bonded specimens were stored in distilled water at 37°C for 24 hours and then subjected to 5000, 10,000, 30,000, or 50,000 TC between 5°C and 55°C before shear bond strength (SBS) testing, creating a division into a total of five different storage conditions. Baseline specimens were stored in distilled water at 37°C for 24 hours. The SBS test was performed at a cross-head speed of 1.0 mm/min. Three-way analysis of variance revealed that all the factors of application mode, adhesive, and thermal cycle period significantly influenced the SBS values ( p<0.001), regardless of the etching mode. In the baseline groups, all of the tested adhesives with active application had higher SBS values than those with inactive application, regardless of etching mode. In the TC groups, significantly lower SBS values were observed at 50,000 TC with inactive application compared to those with active application, regardless of the etching mode. From the scanning electron microscopy observation of demineralized and deproteinized resin/dentin interfaces, dense resin tags longer than 50 µm were observed in the etch-and-rinse with active application group. On the other hand, the resin tags in self-etch mode were sparse, thin, and much shorter than those in etch-and-rinse mode. Comparing the penetration status of the resin tags with active and inactive application in self-etch mode, the resin tag penetration with inactive application was much lower than that with active application. Active application is effective in enhancing the dentin bond durability of universal adhesives. When using universal adhesives with different etching modes, practitioners should select the optimal etching mode and appropriate application method in accordance with the cavity conditions.
Subject(s)
Dental Bonding , Dentin-Bonding Agents , Acid Etching, Dental , Animals , Cattle , Dental Cements , Dentin , Materials Testing , Resin CementsABSTRACT
OBJECTIVE:: The purpose of this study was to evaluate the effect of reduced application times of universal adhesives on enamel bond fatigue and surface morphology of the treated enamel with constant force atomic force microscopy (AFM). METHODS:: Four universal adhesives-Adhese Universal (AU), Clearfil Universal Bond Quick (CU), G-Premio Bond (GP), and Scotchbond Universal Adhesive (SU)-were evaluated in a laboratory for their ability to adhesively bond resin composite to enamel. Shear bond strengths were initially determined using 15 specimens per test group for each adhesive. Shear fatigue strengths were then determined using 20 specimens per test group for each the adhesives. The fatigue specimens were loaded using a sine wave at a frequency of 20 Hz for 50,000 cycles or until failure occurred. AFM observations, surface Ra roughness measurements, and geometric surface area evaluations of enamel surface treated with the adhesive agents were also conducted. RESULTS:: A strong relationship was found between the initial shear bond strength and shear fatigue strength for enamel surface Ra roughness but not for geometric surface area. The initial shear bond strength and shear fatigue strength of CU and GP were not influenced by different application times, unlike those of AU and SU. While the surface area of enamel treated with the adhesive agents was not significantly influenced by different application times and type of adhesive, surface Ra roughness of the enamel in the AU and SU groups significantly increased with increasing application time, unlike CU and GP. CONCLUSIONS:: The results of this study suggest that universal adhesives, used with reduced application times, have adequate Ra surface roughness to provide sufficient resistance to enamel bond fatigue at application times from <1 second to 20 seconds, while the geometric surface area of adhesive-treated enamel did not show any significant changes at these different application times.
Subject(s)
Dental Bonding/methods , Dentin-Bonding Agents/chemistry , Resin Cements/chemistry , Acrylic Resins , Materials Testing , Methacrylates , Microscopy, Atomic Force , Surface Properties , Time FactorsABSTRACT
OBJECTIVE: This study investigated the influence of thermal stress on the simulated localized and generalized wear of nanofilled resin composites. METHODS: Six nanofilled resin composites were evaluated and then subjected to a wear challenge of 400,000 cycles in a Leinfelder-Suzuki (Alabama) wear simulation device after 24 hours of water storage (24-hour group) and 24 hours of water storage and 10,000 thermal cycles (TC group). Simulated localized wear was generated using a stainless-steel ball bearing, and simulated generalized wear was generated using a flat-ended stainless-steel cylinder. Wear testing was accomplished in a water slurry of polymethyl methacrylate beads. Simulated localized and generalized wear was determined using a noncontact profilometer (Proscan 2100) in conjunction with Proscan and AnSur 3D software. RESULTS: Wear was significantly different ( p<0.05) among the resin composites for both simulated localized and generalized wear of either the 24-hour group or the TC group. The simulated localized wear of the TC group was significantly greater than that of the 24-hour group; however, the simulated generalized wear of most of the resin composites of the TC group was not significantly different from that of the 24-hour group. CONCLUSION: The simulated localized and generalized wear of nanofilled resin composites is material dependent. The simulated localized wear of nanofilled resin composites appears to be influenced by thermal stress, whereas this effect is not as apparent in simulated generalized wear testing.
Subject(s)
Composite Resins/chemistry , Dental Materials/chemistry , Dental Restoration Wear , Hot Temperature , Image Processing, Computer-Assisted , Light-Curing of Dental Adhesives , Materials Testing , Surface PropertiesABSTRACT
The aim of this study was to use ultrasonography to evaluate the effect of the self-assembling peptide P11-4 on acid erosion prevention. Curodont Repair (CR), which includes peptide P11-4, was used. Rectangular prisms of bovine enamel (4×1×1 mm) were immersed in pure orange juice for a period of 5 minutes six times per day for 28 days. These samples were divided into four groups of six specimens each and treated differently for an additional period of 28 days: 1) baseline group specimens were stored in artificial saliva; 2) CR group specimens were exposed to curodont without acid challenge; 3) NCRA (no curodont+acid challenge) specimens were treated with orange juice without curodont exposure; and 4) CRA (CR+acid challenge) specimens were treated with curodont before treatment with orange juice. The propagation time of longitudinal ultrasonic velocity (UV) was measured. Ultrastructural observation of each tested enamel surface was carried out using field-emission scanning electron microscopy (SEM). The UV data were analyzed using two-way analysis of variance with time and treatment as confounding factors. Post hoc pairwise tests among groups were performed using the Tukey honestly significant difference test. The average UV in intact bovine enamel for the baseline group ranged from 4,483 to 4,549 m/s and did not vary significantly within the test period. The average ultrasonic velocity (UV) in all samples decreased after the initial erosion. The UV in NCRA decreased further over time. Increased UVs were found for CR and CRA. For CR and CRA, there was no significant difference in UV at the end of the experiment from the initial value before erosion. In the results of SEM observation, the CR and CRA groups had similar morphologic features in that etching patterns were not clearly due to precipitation between the enamel rods. From the results of this in vitro study, it might be concluded that applying enamel matrix derivatives and self-assembling peptides on erosive lesions can improve remineralization.
Subject(s)
Oligopeptides/chemistry , Tooth Erosion/prevention & control , Animals , Cattle , Citrus/chemistry , In Vitro Techniques , Microscopy, Electron, Scanning , Saliva, Artificial/chemistry , Tooth Erosion/diagnostic imaging , Ultrasonography/methodsABSTRACT
The present study determined the mechanical properties and volumetric polymerization shrinkage of different categories of resin composite. Three high viscosity bulk fill resin composites were tested: Tetric EvoCeram Bulk Fill (TB, Ivoclar Vivadent), Filtek Bulk Fill posterior restorative (FB, 3M ESPE), and Sonic Fill (SF, Kerr Corp). Two low-shrinkage resin composites, Kalore (KL, GC Corp) and Filtek LS Posterior (LS, 3M ESPE), were used. Three conventional resin composites, Herculite Ultra (HU, Kerr Corp), Estelite ∑ Quick (EQ, Tokuyama Dental), and Filtek Supreme Ultra (SU, 3M ESPE), were used as comparison materials. Following ISO Specification 4049, six specimens for each resin composite were used to determine flexural strength, elastic modulus, and resilience. Volumetric polymerization shrinkage was determined using a water-filled dilatometer. Data were evaluated using analysis of variance followed by Tukey's honestly significant difference test (α=0.05). The flexural strength of the resin composites ranged from 115.4 to 148.1 MPa, the elastic modulus ranged from 5.6 to 13.4 GPa, and the resilience ranged from 0.70 to 1.0 MJ/m3. There were significant differences in flexural properties between the materials but no clear outliers. Volumetric changes as a function of time over a duration of 180 seconds depended on the type of resin composite. However, for all the resin composites, apart from LS, volumetric shrinkage began soon after the start of light irradiation, and a rapid decrease in volume during light irradiation followed by a slower decrease was observed. The low shrinkage resin composites KL and LS showed significantly lower volumetric shrinkage than the other tested materials at the measuring point of 180 seconds. In contrast, the three bulk fill resin composites showed higher volumetric change than the other resin composites. The findings from this study provide clinicians with valuable information regarding the mechanical properties and polymerization kinetics of these categories of current resin composite.
Subject(s)
Composite Resins/chemistry , Methacrylates/chemistry , Elasticity , Humans , Polymerization , Tensile StrengthABSTRACT
OBJECTIVE: The purpose of this study was to evaluate the effect of the oxygen inhibition layer of universal adhesive on enamel bond fatigue durability and interfacial characteristics with different etching modes. METHODS: The three universal adhesives used were Scotchbond Universal Adhesive (3M ESPE, St Paul, MN, USA), Adhese Universal (Ivoclar Vivadent, Schaan, Lichtenstein), and G-Premio Bond (GC, Tokyo, Japan). The initial shear bond strength and shear fatigue strength to enamel was determined in the presence and absence of the oxygen inhibition layer, with and without phosphoric acid pre-etching. The water contact angle was also measured in all groups using the sessile drop method. RESULTS: The enamel bonding specimens with an oxygen inhibition layer showed significantly higher (p<0.05) initial shear bond strengths and shear fatigue strengths than those without, regardless of the adhesive type and etching mode. Moreover, the water contact angles on the specimens with an oxygen inhibition layer were significantly lower (p<0.05) than on those without, regardless of etching mode. CONCLUSION: The results of this study suggest that the oxygen inhibition layer of universal adhesives significantly increases the enamel bond fatigue durability and greatly changes interfacial characteristics, suggesting that the bond fatigue durability and interfacial characteristics of these adhesives strongly rely on its presence.
Subject(s)
Dental Bonding , Dental Cements/therapeutic use , Dental Enamel/metabolism , Dental Etching , Dental Bonding/methods , Dental Cements/adverse effects , Dental Etching/methods , Dental Stress Analysis , Humans , Oxygen/metabolismABSTRACT
OBJECTIVE: The relationship between the simulated gap wear and generalized wear of resin luting cements was investigated. METHODS: Five resin luting cements, G-Cem LinkForce (GL), Multilink Automix (MA), NX3 Nexus, Panavia V5 (PV), and RelyX Ultimate were evaluated and subsequently subjected to a wear challenge in a Leinfelder-Suzuki (Alabama) wear simulation device. Half of the specimens from each resin luting cement were photo-cured for 40 seconds and the other half were not photo-cured. The simulated gap and generalized wear were generated using a flat-ended stainless steel antagonist. Wear testing was performed in a water slurry of polymethyl methacrylate beads, and the simulated gap and generalized wear were determined using a noncontact profilometer (Proscan 2100) in conjunction with the Proscan and AnSur 3D software. RESULTS: A strong relationship was found between the gap wear and generalized wear simulation models. The simulated gap wear and generalized wear of the resin luting cements followed similar trends in terms of both volume loss and mean depth of wear facets with each curing method. Unlike the simulated gap wear and generalized wear of GL and PV, those of MA, NX, and RU were influenced by the curing method. CONCLUSION: The results of this study indicate that simulated gap wear of resin luting cements is very similar to simulated generalized wear. In most cases, dual curing appears to ensure greater wear resistance of resin luting cements than chemical curing alone. The wear resistance of some resin luting cements appears to be material dependent and is not influenced by the curing method.
Subject(s)
Dental Restoration Wear , Resin Cements/therapeutic use , Composite Resins/therapeutic use , Glass Ionomer Cements/therapeutic useABSTRACT
This study determined the influence of curing mode on polymerization behavior and mechanical properties of dual-cured provisional resins. Three dual-cured bisacryl-based provisional resins were used: Tempsmart (TS; GC Corp), Luxatemp Automix Solar (LX; DMG Chemisch Pharmazeutishe Fabrik GmbH), and Integrity Multi·Cure (IG; Dentsply Caulk). A self-cured bisacryl-based provisional resin, Protemp Plus (PP; 3M ESPE) and a conventional poly(methyl methacrylate) (PMMA) provisional resin, Unifast III (UF; GC Corp) were used as controls. The inorganic filler content and coefficients of linear thermal expansion of the test materials were measured. Six specimens of each material were used to determine the flexural strength, elastic modulus, and resilience. The changes in ultrasound velocity during polymerization were measured. The average inorganic filler contents of the provisional resins, apart from UF, ranged from 24.4 to 39.3 wt%. The highest inorganic filler content was determined for LX, whereas TS showed the lowest value among the tested materials. The average coefficients of thermal expansion of the tested provisional resins ranged from 77.3 to 107.7 (×10-6/°C). TS and IG showed significantly lower thermal expansions than the other tested provisional resins. The mean flexural strengths of the provisional resins ranged from 70.4 to 122.6 MPa, the mean elastic moduli ranged from 1.8 to 3.7 GPa, and the mean resilience of the provisional resins ranged from 1.1 to 2.3 MJ/mm3, respectively. Dual-cured provisional resins showed significantly higher flexural strengths than the PMMA resin. However, in all cases, the light-curing mode showed significantly higher flexural strengths than the self-curing mode. In the initial polymerization phase, dual-cured resins in the light-curing mode showed a rapid increase in the speed of sound (V) during light irradiation, followed by a slower increase. Conversely, the dual-cured resins in the self-curing mode showed a slower initial increase, followed by a rapid increase. Although no significant difference in V was observed between 10 and 15 minutes in the light-curing mode of all tested dual-cured resins, a significantly higher V value was obtained at 15 minutes than at 10 minutes in the self-curing modes for LX and IG. Regardless of the curing mode, tested dual-cured provisional resins showed superior mechanical properties than the conventional PMMA provisional resin. However, dual-cured provisional resin flexural properties and polymerization behavior were affected by the curing mode. This study indicated that the light-curing mode might be recommended for all dual-cured provisional resins because of the enhancement of their mechanical properties and reduction of chair time.
Subject(s)
Self-Curing of Dental Resins/methods , Bisphenol A-Glycidyl Methacrylate/therapeutic use , Dental Stress Analysis , Elasticity , Hardness , Humans , Polymerization , Resins, Synthetic/therapeutic use , Tensile StrengthABSTRACT
OBJECTIVE: This study investigated the interfacial characteristics and bond durability of universal adhesives to various substrates. METHODS AND MATERIALS: Two universal adhesives were used: 1) Scotchbond Universal and 2) G-Premio Bond. The substrates used were bovine enamel and dentin with or without phosphoric acid etching, resin composite, lithium disilicate and leucite-reinforced glass ceramics, zirconia, and metal alloys. The surface free energy and the parameters of various substrates and of substrates treated by adhesive after light irradiation were determined by measuring the contact angles of three test liquids. Resin composite was bonded to the various substrates to determine shear bond strength after 24 hours water storage and 10,000 thermal cycles. A one-way analysis of variance (ANOVA) and the Tukey post hoc test were used for the surface free energy data, and a two-way ANOVA and the Tukey post hoc test were used for analysis of shear bond strength data (α=0.05). RESULTS: The interfacial characteristics of the various substrates show significant differences depending on the type of substrate, but the interfacial characteristics of substrate treated by adhesive after light irradiation did not show any significant differences regardless of the substrate used. The bond durability of two universal adhesives to various substrates differs depending on the type of substrate and the adhesive. CONCLUSIONS: The results of this study suggest that universal adhesives modify the interfacial characteristics of a wide range of substrates and create a consistent surface, but the bond durability of universal adhesive to various substrates differs depending on the type of substrate and the adhesive.
Subject(s)
Composite Resins/chemistry , Dental Bonding/methods , Dentin-Bonding Agents/chemistry , Resin Cements/chemistry , Animals , Cattle , In Vitro Techniques , Light-Curing of Dental Adhesives , Materials Testing , Surface PropertiesABSTRACT
OBJECTIVE: The purpose of this study was to evaluate the influence of thermal cycling on the flexural properties and simulated wear of computer-aided design/computer-aided manufacturing (CAD/CAM) resin composites. METHODS: The six CAD/CAM resin composites used in this study were 1) Lava Ultimate CAD/CAM Restorative (LU); 2) Paradigm MZ100 (PM); 3) CERASMART (CS); 4) Shofu Block HC (SB); 5) KATANA AVENCIA Block (KA); and 6) VITA ENAMIC (VE). Specimens were divided randomly into two groups, one of which was stored in distilled water for 24 hours, and the other of which was subjected to 10,000 thermal cycles. For each material, 15 specimens from each group were used to determine the flexural strength and modulus according to ISO 6872, and 20 specimens from each group were used to examine wear using a localized wear simulation model. The test materials were subjected to a wear challenge of 400,000 cycles in a Leinfelder-Suzuki device (Alabama machine). The materials were placed in custom-cylinder stainless steel fixtures, and simulated localized wear was generated using a stainless steel ball bearing (r=2.387 mm) antagonist in a water slurry of polymethyl methacrylate beads. Simulated wear was determined using a noncontact profilometer (Proscan 2100) with Proscan and AnSur 3D software. RESULTS: The two-way analysis of variance of flexural properties and simulated wear of CAD/CAM resin composites revealed that material type and thermal cycling had a significant influence (p<0.05), but there was no significant interaction (p>0.05) between the two factors. The flexural properties and maximum depth of wear facets of CAD/CAM resin composite were different (p<0.05) depending on the material, and their values were influenced (p>0.05) by thermal cycling, except in the case of VE. The volume losses in wear facets on LU, PM, and SB after 10,000 thermal cycles were significantly higher (p<0.05) than those after 24 hours of water storage, unlike CS, KA, and VE. CONCLUSION: The results of this study indicate that the flexural properties and simulated wear of CAD/CAM resin composites are different depending on the material. In addition, the flexural properties and simulated wear of CAD/CAM resin composites are influenced by thermal cycling.