In vitro remineralization assessment of enamel subsurface lesions using different percentages of surface reaction-type pre-reacted glass-ionomer containing gum-based material.

OBJECTIVE: To identify the remineralization activity of enamel subsurface lesions using different percentages of surface pre-reacted glass-ionomer (S-PRG) filler containing gum-base material. METHODS: Gum extracts from gum-base materials containing 0wt%, 5wt%, and 10wt% S-PRG filler were prepared as GE0, GE5, and GE10, respectively. A total of 50 bovine enamel specimens were used, and the polished enamel surface of a 3 × 3 mm2 window area was exposed. The specimens were then subjected to a demineralization solution for seven days to create a subsurface enamel lesion. Remineralization was then conducted for seven days using a protocol whereby the specimens were immersed three times a day in prepared gum extracts (0wt%, 5wt%, and 10wt%) and artificial saliva of pH 7 (Control) for 20 min at 37 °C. Thereafter, remineralization assessment was performed by using Swept Source Optical Coherence Tomography (SS-OCT) and micro-computed tomography (µCT). Surface morphology and elemental analysis were conducted by scanning electron microscopy (SEM) and energy-dispersive X-ray spectrometry (EDS). RESULTS: The depths of the demineralized lesions in the GE5 and GE10 groups were significantly lower than those of the Control and the GE0 groups. SEM observations of the enamel surface morphology of the GE5 and GE10 groups indicated remineralization with S-PRG filler-related elements present. CONCLUSION: The GE5 and GE10 S-PRG filler containing gum-base materials showed significantly improved surface remineralization and reduced demineralization of the enamel lesions. EDS analysis suggested that the released ions from the S-PRG filler might be responsible for surface remineralization. CLINICAL SIGNIFICANCE: The S-PRG filler containing gum-base material may have a significant remineralization effect and improve the surface morphology of enamel subsurface lesions.

Dentin anti-demineralization potential of surface reaction-type pre-reacted glass-ionomer filler containing self-adhesive resin cement.

OBJECTIVE: To investigate the anti-demineralization potential of a newly developed surface reaction-type pre-reacted glass-ionomer (S-PRG) filler containing self-adhesive resin cement against acidic attacks on the dentin surface. MATERIALS AND METHODS: A total of 32 bovine teeth were used. Cavities were prepared on crown dentin slaps and filled with three self-adhesive resin cement: (1) S-PRG-based cement, (2) Si-based cement, and (3) RelyX cement. Specimens were then subjected to pH cycling for 28 days, and the depth of demineralization was assessed using swept-source optical coherence tomography (SS-OCT) after 7, 14, 21, and 28 days. Sixty-four root dentin blocks were divided into four groups and then subjected to a pH cycling procedure with the aforementioned three material blocks and one negative control. The mineral loss was observed using transverse microradiography (TMR), and the surface microhardness (SMH) test was conducted to investigate the mechanical properties of treated dentin surfaces. RESULTS: The depth of demineralization for the S-PRG-based cement was significantly lower than that of the Si-based cement after 7, 21, and 28 days. Conversely, the RelyX cement was not significantly different from the Si-based cement after 7, 14, and 21 days (p < 0.05). Regarding the TMR and SMH test, the S-PRG-based cement showed the least mineral loss with the highest resistance to acidic challenge. CONCLUSION: The S-PRG filler containing resin cement can reduce mineral loss and promote remineralization of dentin substrate and has the potential to preserve dentin integrity and resist acidic attack. Clinical significance Self-adhesive resin cement containing S-PRG fillers maintained the surface integrity of dentin after exposure to 28 days of acidic challenge with a significant anti-demineralization effect.