Efficient Proton-exchange Membrane Fuel Cell Performance of Atomic Fe Sites via p-d Hybridization with Al Dopants.

Orbital hybridization to regulate the electronic structures and surface chemisorption properties of transition metals is of great importance for boosting the oxygen reduction reaction (ORR) in proton-exchange membrane fuel cells (PEMFCs). Herein, we developed a core-shell rambutan-like nanocarbon catalyst (FeAl-RNC) with atomically dispersed Fe-Al atom pairs from metal-organic framework (MOF) material. Experimental and theoretical results demonstrate that the strong p-d orbital hybridization between Al and Fe results in an asymmetric electron distribution with moderate adsorption strength of oxygen intermediates, rendering enhanced intrinsic ORR activity. Additionally, the core-shell rambutan-like structure of FeAl-RNC with abundant micropores and macropores can enhance the density of active sites, stability, and transport pathways in PEMFC. The FeAl-RNC-based PEMFC achieves excellent activity (68.4 mA cm-2 at 0.9 V), high peak power (1.05 W cm-2), and good stability with only 7% current loss after 100 h at 0.7 V under H2-O2 condition.

Hydroxyl-Terminated Triazine Derivatives Grafted Graphene Oxide for Epoxy Composites: Enhancement of Interfacial and Mechanical Properties.

An effective approach to the fabrication of progressive epoxy nanocomposites by the incorporation of hydroxyl-terminated dendrimers functionalized graphene oxide (GO-TCT-Tris) is reported. The relationship between surface grafting, chemical construction, morphology, dispersion, and interfacial interaction as well as the corresponding mechanical properties of the composites were studied in detail. It was shown that hydroxyl-terminated triazine derivatives have been resoundingly bonded onto the GO surface through covalent bonding, which effectively improved the dispersion and compatibility of GO sheets in epoxy resin. The tensile and flexural tests manifested that the GO-TCT-Tris/epoxy composites exhibited greater tensile/flexural strength and modulus than either the pure epoxy or the GO/epoxy composites. For GO-TCT-Tris (0.10 wt%)/epoxy composite, the tensile strength and elastic modulus increased from 63 ± 4 to 89 ± 6 MPa (41.27%) and from 2.8 ± 0.1 to 3.6 ± 0.2 GPa (28.57%), and the flexural strength and modulus increased from 106 ± 5 to 158 ± 6 MPa (49.06%) and from 3.0 ± 0.1 to 3.5 ± 0.2 GPa (16.67%), respectively, compared to the pure epoxy matrix. Moreover, the fractographic analysis also illustrated the ameliorative interfacial interaction between GO-TCT-Tris and epoxy matrix.