Optimization of Oligomer Chitosan/Polyvinylpyrrolidone Coating for Enhancing Antibacterial, Hemostatic Effects and Biocompatibility of Nanofibrous Wound Dressing.

A synergistic multilayer membrane design is necessary to satisfy a multitude of requirements of an ideal wound dressing. In this study, trilayer dressings with asymmetric wettability, composed of electrospun polycaprolactone (PCL) base membranes coated with oligomer chitosan (COS) in various concentrations of polyvinylpyrrolidone (PVP), are fabricated for wound dressing application. The membranes are expected to synergize the hygroscopic, antibacterial, hemostatic, and biocompatible properties of PCL and COS. The wound dressing was coated by spraying the solution of 3% COS and 6% PVP on the PCL base membrane (PVP6-3) three times, which shows good interaction with biological subjects, including bacterial strains and blood components. PVP6-3 samples confirm the diameter of inhibition zones of 20.0 ± 2.5 and 17.9 ± 2.5 mm against Pseudomonas aeruginosa and Staphylococcus aureus, respectively. The membrane induces hemostasis with a blood clotting index of 74% after 5 min of contact. In the mice model, wounds treated with PVP6-3 closed 95% of the area after 10 days. Histological study determines the progression of skin regeneration with the construction of granulation tissue, new vascular systems, and hair follicles. Furthermore, the newly-growth skin shares structural resemblances to that of native tissue. This study suggests a simple approach to a multi-purpose wound dressing for clinical treatment.

Characterizations and Antibacterial Efficacy of Chitosan Oligomers Synthesized by Microwave-Assisted Hydrogen Peroxide Oxidative Depolymerization Method for Infectious Wound Applications.

The use of naturally occurring materials with antibacterial properties has gained a great interest in infected wound management. Despite being an abundant resource in Vietnam, chitosan and its derivatives have not yet been intensively explored for their potential in such application. Here, we utilized a local chitosan source to synthesize chitosan oligomers (OCS) using hydrogen peroxide (H2O2) oxidation under the microwave irradiation method. The effects of H2O2 concentration on the physicochemical properties of OCS were investigated through molecular weight, degree of deacetylation, and heavy metal contamination for optimization of OCS formulation. Then, the antibacterial inhibition was examined; the minimum inhibitory concentration and minimum bactericidal concentration (MIC and MBC) of OCS-based materials were determined against common skin-inhabitant pathogens. The results show that the local Vietnamese chitosan and its derivative OCS possessed high-yield purification while the molecular weight of OCS was inversely proportional and proportional to the concentration of H2O2, respectively. Further, the MIC and MBC of OCS ranged from 3.75 to less than 15 mg/mL and 7.5-15 mg/mL, respectively. Thus, OCS-based materials induce excellent antimicrobial properties and can be attractive for wound dressings and require further investigation.

Investigating the effect of multi-coated hydrogel layer on characteristics of electrospun PCL membrane coated with gelatin/silver nanoparticles for wound dressing application.

In this study, the effect of coated hydrogel layer on characteristics of the whole gelatin/silver nanoparticles multi-coated polycaprolactone membrane (PCLGelAg) was investigated through systematic and typical wound dressing characterizations to select the optimal number of layers for practical applications. Scanning electron microscopy, free swell absorptive capacity and tensile test in both wet and dry conditions were conducted to characterize all fabricated membranes of six coating times. In vitro cytotoxicity and agar diffusion evaluation were also carried out to assess the biocompatibility and antibacterial activity of the membranes. The findings illustrated that as the coated layers increase, the absorptive capacity, and degradation rate were higher, the membranes were stiffer in dry state while the tensile strength in wet state, elongation, and cell viability were significantly decreased. PCLGelAg3 was chosen to be the best fit for wound healing since it maintained quite sufficient maximum buffer uptake, elasticity, cell viability along with inducing abnormalities in bacterial morphology and preventing biofilm formation.

Fabrication of chitosan oligomer-coated electrospun polycaprolactone membrane for wound dressing application.

Wound dressings are typically used to provide a favorable environment supporting the intricate process of wound healing. This research aims to fabricate and evaluate an electrospun polycaprolactone (EsPCL) membrane coated with various densities of chitosan oligomers (COS) - a biological agent - for application as bioactive wound dressing. Weight calculation was employed to investigate the density of COS coated onto the electrospun PCL membrane. Physicochemical characteristics of the prepared membranes, such as hydrophilicity and mechanical properties were demonstrated and evaluated through standard experimental methods. In vitro assays and mice model were used to investigate the antibacterial activities, cytocompatibility, hemostasis and the in vivo interaction of the membranes. The results showed that COS was coated successfully on the surface of the polymeric membrane, altering its morphology and associated characteristics. The greater concentration of COS led to an increase in the thickness of the membrane, which resulted in stronger antibacterial activities. Moreover, the increase of chitosan oligomers density in the membrane induced faster hemostasis and affected the re-epithelialization and wound healing in mice. Thus, the membrane as a whole and particularly chitosan oligomers were shown to be potential for further studies regarding wound dressing.

The effect of oxidation degree and volume ratio of components on properties and applications of in situ cross-linking hydrogels based on chitosan and hyaluronic acid.

The purpose of this research is to investigate the effect of different oxidation degrees and volume ratios of components on the physical properties and biocompatibility of an in situ cross-linking chitosan-hyaluronic acid-based hydrogel for skin wound healing applications. Carboxymethyl groups (-CH2COOH) were introduced to the polymer chain of chitosan, producing N,O - Carboxymethyl Chitosan (NOCC). Hyaluronic acid was oxidized to obtain aldehyde hyaluronic acid (AHA) with three oxidation degrees (AHA40, AHA50 and AHA60). The gelation was induced by forming Schiff base linkage between aldehyde groups of AHA and amino groups of NOCC. Then, the polysaccharide derivatives were combined at three NOCC:AHA volume ratios (3:7, 5:5 and 7:3) to form composite hydrogels without using any additional cross-linker. FT-IR analysis, surface morphology observation and wettability test, in vitro degradation test and rheological analysis were carried out to characterize the hydrogels. Additionally, in vitro cytotoxicity and in vivo wound healing evaluations were also conducted to study the biocompatibility of the composite. Our findings showed that when increasing the volume of NOCC, the homogeneity and hydrophobicity of the resulting hydrogels were also improved and their pore walls became thicker, leading to slower degradation rate. On the other hand, when raising the oxidation degree of AHA, the hydrophilicity of the gels decreased and less time was required to form the gel matrix. Besides, the obtained in vitro and in vivo results indicated that lower oxidation degree of AHA supports cell proliferation, cell attachment and wound healing process better. It is also concluded that NOCC-AHA40 5:5 hydrogel is most suitable for skin wound healing applications since it possesses superior morphology with high uniformity, favorable pore size and suitable density along with appropriate wettability. The NOCC-AHA gel matrix is expected to be used as a delivery system for other factors and employed as an effective bio-glue in further tissue engineering applications.