ABSTRACT
Spherical silver nanoparticles (Ag NPs) and silver nanoprisms (Ag NPrsms) were synthesized and decorated on graphene oxide (GO) nanosheets. The Ag contents were 29% and 23% in the GO−Ag NPs and GO−Ag NPrsms, respectively. The Ag NPrsms exhibited stronger (111) crystal signal than Ag NPs. The GO−Ag NPrsms exhibited higher Ag (I) content (75.6%) than GO-Ag NPs (69.9%). Increasing the nanomaterial concentration from 25 to 100 µg mL−1 improved the bactericidal efficiency, and the antibacterial potency was in the order: GO−Ag NPrsms > GO−Ag NPs > Ag NPrsms > Ag NPs > GO. Gram-positive Staphylococcus aureus (S. aureus) was more vulnerable than Gram-negative Escherichia coli (E. coli) upon exposure to these nanomaterials. The GO−Ag NPrsms demonstrated a complete (100%) bactericidal effect against S. aureus at a concentration of 100 µg mL−1. The GO−Ag composites outperformed those of Ag or GO due to the synergistic effect of bacteriostatic Ag particles and GO affinity toward bacteria. The levels of reactive oxygen species produced in the bacteria−nanomaterial mixtures were highly correlated to the antibacterial efficacy values. The GO−Ag NPrsms are promising as bactericidal agents to suppress biofilm formation and inhibit bacterial infection.
ABSTRACT
A series of graphene oxide (GO) suspensions with different particle sizes (<100 nm, ~100 nm, ~1 µm and >1 µm) were successfully fabricated after 0, 30, 60 and 120 min of sonication, respectively. The antibacterial properties of GO suspensions showed that >1 µm GO size resulted in a loss of nearly 50% of bacterial viability, which was higher than treatment by ~100 nm GO size (25%) towards Escherichia coli (E. coli). Complete entrapment of bacteria by the larger GO was observed in transmission electron microscopy (TEM). Silver nanoparticles (Ag NPs) were doped onto GO samples with different lateral sizes to form GO-Ag NP composites. Resulting larger GO-Ag NPs showed higher antibacterial activity than smaller GO-Ag NPs. As observed by Fourier transform infrared spectroscopy (FTIR), the interaction between E. coli and GO occurred mainly at the outer membrane, where membrane amino acids interact with hydroxyl and epoxy groups. The reactive oxygen species (ROS) and the considerable penetration of released Ag+ into the inner bacterial cell membrane result in loss of membrane integrity and damaged morphology. The present work improves the combined action of GO size effect with constant Ag loadings for potential antibacterial activity.