ABSTRACT
Epoxy resins are widely used adhesives in industrial fields. To use epoxy resin as an adhesive, it is necessary to mix the epoxy resin with a hardener. Hardeners have various functional groups and skeletons, and the properties of epoxy resins vary depending on the hardener. Although the adhesion of epoxy resins has been extensively studied using density functional theory (DFT) calculations, few studies have evaluated the effect of hardener molecules. Therefore, in this study, DFT calculations of adhesion energies and bonding structures on Cu (111) and Cu2O (111) surfaces are performed for model molecules of adducts of epoxy resin with hardeners having various functional groups and skeletons to evaluate the influence of the hardeners on the adhesion of epoxy resin to the metal surface. The adhesion energy to the Cu (111) surface is governed by the energy due to dispersion forces. Hardeners of the thiol type, which contain relatively heavy sulfur atoms, and hardeners with aromatic rings, displaying high planarity, enable the entire molecule to approach the metal surface, resulting in a relatively high adhesion strength. The calculations for the Cu2O (111) surface show the adhesion strength is more strongly influenced by interactions such as hydrogen bonds between the surface and adhesive molecules than by dispersion forces. Therefore, in adhesion to Cu2O (111), the benzylamine-epoxy adduct with hydrogen bonding and OH-π interactions with the surface, in addition to having a relatively flexible framework, shows a high adhesion strength.
ABSTRACT
Flat layers are usually considered as structurally rigid motifs in two-dimensional (2D) materials. In this work, we demonstrate that a flat honeycomb-layer composed of distorted tri-coordinate copper ions bridged with cyanidos in (tetraethylammonium)Cu2(CN)3 exhibits high in-plane flexibility. This resulted in an extremely large anisotropic 2D-thermal expansion.
ABSTRACT
The adhesion of epoxy adhesives to aluminum materials is an important issue in assembling parts for lightweight mobility. Aluminum surfaces typically possess an oxide layer, which readily adsorbs water. In this study, the aggregation states of water and its effect on the curing reaction were examined by placing a water layer between an amorphous alumina surface and a mixture of epoxy and amine components. This study used molecular dynamics simulations and density functional theory calculations. Before the reaction, water molecules strongly adsorbed onto the alumina surface, aggregating excess water. Some water diffused into the epoxy/amine mixture, accelerating the diffusion of unreacted substances. This led to faster reaction kinetics, particularly in proximity to the alumina surface. The adsorption of water molecules onto the alumina surface and the aggregation of excess water were similarly observed even after the curing process. Subsequently, the interaction between the alumina surface and various functional groups of the epoxy/amine mixture was evaluated before and after the reaction. Epoxy monomers had little interaction with the alumina surface before the reaction, whereas hydroxy groups formed by the ring-opening reaction of epoxy groups exhibited notable interaction. Conversely, sulfonyl and amino groups in amine compounds formed hydrogen bonds with OH groups on the alumina surface before the reaction. However, after the reaction, amino groups weakened their interaction with the alumina OH groups as they transformed from primary to tertiary during the curing reaction. Both epoxy and amine monomers/fragments similarly interacted with water molecules, both before and after the reaction. The insights gained from this study are expected to contribute to a better understanding of the impact of moisture absorption on the application of epoxy resins.
ABSTRACT
In the development of adhesives, an understanding of the fracture behavior of the bonded joints is inevitable. Two typical failure modes are known: adhesive failure and cohesive failure. However, a molecular understanding of the cohesive failure process is not as advanced as that of the adhesive failure process. In this study, research was developed to establish a molecular understanding of cohesive failure using the example of a system in which epoxy resin is bonded to a hydroxyl-terminated self-assembled monolayer (SAM) surface. Adhesive failure was modeled as a process in which an epoxy molecule is pulled away from the SAM surface. Cohesive failure, on the other hand, was modeled as the process of an epoxy molecule separating from another epoxy molecule on the SAM surface or breaking of a covalent bond within the epoxy resin. The results of the simulations based on the models described above showed that the results of the calculations using the model of cohesive failure based on the breakdown of intermolecular interactions agreed well with the experimental results in the literature. Therefore, it was suggested that the cohesive failure of epoxy resin adhesives is most likely due to the breakdown of intermolecular interactions between adhesive molecules. We further analyzed the interactions at the adhesive failure and cohesive failure interfaces and found that the interactions at the cohesive failure interface are mainly accounted for by dispersion forces, whereas the interactions at the adhesive failure interface involve not only dispersion forces but also various chemical interactions, including hydrogen bonds. The selectivity between adhesive failure and cohesive failure was explained by the fact that varying the functional group density affected the chemical interactions but not the dispersion forces.
ABSTRACT
A better understanding of the aggregation states of adhesive molecules in the interfacial region with an adherend is crucial for controlling the adhesion strength and is of great inherent academic interest. The adhesion mechanism has been described through four theories: adsorption, mechanical, diffusion, and electronic. While interfacial characterization techniques have been developed to validate the aforementioned theories, that related to the electronic theory has not yet been thoroughly studied. We here directly detected the electronic interaction between a commonly used thermosetting adhesive, cured epoxy of diglycidyl ether of bisphenol A (DGEBA) and 4,4'-diaminodiphenylmethane (DDM), and copper (Cu). This study used a combination of density functional theory (DFT) calculations and femtosecond transient absorption spectroscopic (TAS) measurements as this epoxy adhesive-Cu pairing is extensively used in electronic device packaging. The DFT calculations predicted that π electrons in a DDM molecule adsorbed onto the Cu surface flowed out onto the Cu surface, resulting in a positive charge on the DDM. TAS measurements for the Cu/epoxy multilayer film, a model sample containing many metal/adhesive interfaces, revealed that the electronic states of excited DDM moieties at the Cu interface were different from those in the bulk region. These results were in good accordance with the prediction by DFT calculations. Thus, it can be concluded that TAS is applicable to characterize the electronic interaction of adhesives with metal adherends in a nondestructive manner.
ABSTRACT
Regulatory T cells (Tregs) are lymphocytes that play a central role in peripheral immune tolerance. Tregs are promising targets for the prevention and suppression of autoimmune diseases, allergies, and graft-versus-host disease, and treatments aimed at regulating their functions are being developed. In this study, we created a new modality consisting of a protein molecule that suppressed excessive immune responses by effectively and preferentially expanding Tregs. Recent studies reported that tumor necrosis factor receptor type 2 (TNFR2) expressed on Tregs is involved in the proliferation and activation of Tregs. Therefore, we created a functional immunocytokine, named TNFR2-ICK-Ig, consisting of a fusion protein of an anti-TNFR2 single-chain Fv (scFv) and a TNFR2 agonist TNF-α mutant protein, as a new modality that strongly enhances TNFR2 signaling. The formation of agonist-receptor multimerization (TNFR2 cluster) is effective for the induction of a strong TNFR2 signal, similar to the TNFR2 signaling mechanism exhibited by membrane-bound TNF. TNFR2-ICK-Ig improved the TNFR2 signaling activity and promoted TNFR2 cluster formation compared to a TNFR2 agonist TNF-α mutant protein that did not have an immunocytokine structure. Furthermore, the Treg expansion efficiency was enhanced. TNFR2-ICK-Ig promotes its effects via scFv, which crosslinks receptors whereas the agonists transmit stimulatory signals. Therefore, this novel molecule expands Tregs via strong TNFR2 signaling by the formation of TNFR2 clustering.
Subject(s)
Single-Chain Antibodies , T-Lymphocytes, Regulatory , Carrier Proteins/metabolism , Mutant Proteins/metabolism , Receptors, Tumor Necrosis Factor, Type II/genetics , Receptors, Tumor Necrosis Factor, Type II/agonists , Single-Chain Antibodies/genetics , Single-Chain Antibodies/pharmacology , Single-Chain Antibodies/metabolism , Tumor Necrosis Factor-alpha/metabolism , Humans , Animals , MiceABSTRACT
The adhesion mechanism of epoxy resin to the γ-alumina (110) surface was investigated using first-principles density functional theory (DFT). Aluminum materials are lightweight and are used in a wide range of industrial fields. Its surface is oxidized to alumina, and the stable surface is known as the γ-alumina (110) surface. The coverage of hydroxy groups by chemisorbed water molecules on this surface varied depending on the pretreatment temperature. In this study, we investigated the adhesive interactions of epoxy resin on four alumina surfaces with different densities of surface hydroxy groups (0, 3, 6, and 9 OH/nm2) and have discussed their effects. At each interface, the energy curves of the vertically displaced epoxy resin were calculated and the adhesive forces were estimated by differentiating these curves. As the coverage of the surface hydroxy groups increased from 0 to 6 OH/nm2, the adhesive strength gradually decreased. However, the adhesive strength at 9 OH/nm2 was relatively large and almost equal to that at 3 OH/nm2. This inverse volcano-type behavior was analyzed via the decomposition of adhesive forces and the crystal orbital Hamilton population (COHP). The decomposition of adhesive forces into DFT and dispersion components revealed that the inverse volcano-type behavior is derived from the DFT component, and the interfacial interactions owing to the DFT component are accompanied by charge transfer. These were investigated using a COHP analysis, which revealed that this behavior was caused by changes in the activity of the aluminum atoms on the surface and surface reconstruction by chemisorbed water molecules. It is noteworthy that the adhesive strength for 9 OH/nm2 was only 6.9% lower than that for 0 OH/nm2 wherein the chemisorbed water molecules were completely removed from the surface. These results are expected to provide a guideline for the adhesion of epoxy resin to aluminum materials.
ABSTRACT
Face-to-face stacking of aromatic compounds leads to stacked antiaromaticity, while that of antiaromatic compounds leads to stacked aromaticity. This is a prediction with a long history; in the late 2000s, the prediction was confirmed by high-precision quantum chemical calculations, and finally, in 2016, a π-conjugated system with stacked aromaticity was synthesized. Several variations have since been reported, but essentially, they are all the same molecule. To realize stacked aromaticity in a completely new and different molecular system and to trigger an extension of the concept of stacked aromaticity, it is important to understand the origin of stacked aromaticity. The Hückel method, which has been successful in giving qualitatively correct results for π-conjugated systems despite its bold assumptions, is well suited for the analysis of stacked aromaticity. We use this method to model the face-to-face stacking systems of benzene and cyclobutadiene molecules and discuss their stacked antiaromaticity and stacked aromaticity on the basis of their π-electron energies. By further developing the discussion, we search for clues to realize stacked aromaticity in synthesizable molecular systems.
ABSTRACT
This paper details the use of computational and informatics methods to design metal nanocluster catalysts for efficient ammonia synthesis. Three main problems are tackled: defining a measure of catalytic activity, choosing the best candidate from a large number of possibilities, and identifying the thermodynamically stable cluster catalyst structure. First-principles calculations, Bayesian optimization, and particle swarm optimization are used to obtain a Ti8 nanocluster as a catalyst candidate. The N2 adsorption structure on Ti8 indicates substantial activation of the N2 molecule, while the NH3 adsorption structure suggests that NH3 is likely to undergo easy desorption. The study also reveals several cluster catalyst candidates that break the general trade-off that surfaces that strongly adsorb reactants also strongly adsorb products.
ABSTRACT
Recently, TNF receptor type 2 (TNFR2) signaling was found to be involved in the proliferation and activation of regulatory T cells (Tregs), a subpopulation of lymphocytes that suppress immune responses. Tregs mediate peripheral immune tolerance, and the disruption of their functions causes autoimmune diseases or allergy. Therefore, cell expanders or regulators of Tregs that control immunosuppressive activity can be used to treat these diseases. We focused on TNFR2, which is preferentially expressed on Tregs, and created tumor necrosis factor-α (TNF-α) muteins that selectively activate TNFR2 signaling in mice and humans, termed R2agoTNF and R2-7, respectively. In this study, we attempted to optimize the structure of muteins to enhance their TNFR2 agonistic activity and stability in vivo by IgG-Fc fusion following single-chain homo-trimerization. The fusion protein, scR2agoTNF-Fc, enhanced the expansion of CD4+CD25+ Tregs and CD4+Foxp3+ Tregs and contributed to their immunosuppressive activity ex vivo and in vivo in mice. The prophylactic administration of scR2agoTNF-Fc suppressed inflammation in contact hypersensitivity and arthritis mouse models. Furthermore, scR2-7-Fc preferentially expanded Tregs in human peripheral blood mononuclear cells via TNFR2. These TNFR2 agonist-Fc fusion proteins, which have bivalent structures, are novel Treg expanders.
Subject(s)
Arthritis , T-Lymphocytes, Regulatory , Animals , Humans , Mice , Immunosuppressive Agents , Leukocytes, Mononuclear , Receptors, Tumor Necrosis Factor, Type II/genetics , Tumor Necrosis Factor-alphaABSTRACT
Recent studies have theoretically and experimentally demonstrated that antiaromatic molecules with 4n π electrons exhibit stacked aromaticity according to π-π stacking when arranged in a face-to-face manner. However, the mechanism of its occurrence has not been clearly studied. In this study, we investigated the mechanism of stacked aromaticity using cyclobutadiene. When the antiaromatic molecules are stacked in a face-to-face manner, the orbital interactions between the degenerate singly occupied molecular orbitals (SOMOs) of the monomer unit cause a larger energy gap between the degenerate highest-occupied molecular orbitals (HOMOs) and the lowest-unoccupied molecular orbitals (LUMOs) of the dimer. However, the antiaromatic molecules are more stable in less symmetric conformations, mainly because of pseudo-Jahn-Teller distortions. In the case of cyclobutadiene, the two SOMOs of the monomer unit split into HOMO and LUMO because of the bond alternation. When the molecules are stacked in a face-to-face manner, the HOMO-LUMO gap of the dimer is smaller than that of the monomer due to the interactions between the HOMOs and LUMOs of the two monomer units. When the monomer units are within a specific distance of each other, the HOMO and LUMO of the dimer, which correspond to antibonding and bonding between the units, respectively, are interchanged. This alternation of molecular orbitals may result in an increase in the bond strength between the monomer units, exhibiting stacked aromaticity. We demonstrated that it is possible to control the distance exhibited by stacked aromaticity by engineering the HOMO-LUMO gap of the monomer units.
ABSTRACT
Numerous biomimetic molecular catalysts inspired by methane monooxygenases (MMOs) that utilize iron or copper-oxo species as key intermediates have been developed. However, the catalytic methane oxidation activities of biomimetic molecule-based catalysts are still much lower than those of MMOs. Herein, we report that the close stacking of a µ-nitrido-bridged iron phthalocyanine dimer onto a graphite surface is effective in achieving high catalytic methane oxidation activity. The activity is almost 50 times higher than that of other potent molecule-based methane oxidation catalysts and comparable to those of certain MMOs, in an aqueous solution containing H2O2. It was demonstrated that the graphite-supported µ-nitrido-bridged iron phthalocyanine dimer oxidized methane, even at room temperature. Electrochemical investigation and density functional theory calculations suggested that the stacking of the catalyst onto graphite induced partial charge transfer from the reactive oxo species of the µ-nitrido-bridged iron phthalocyanine dimer and significantly lowered the singly occupied molecular orbital level, thereby facilitating electron transfer from methane to the catalyst in the proton-coupled electron-transfer process. The cofacially stacked structure is advantageous for stable adhesion of the catalyst molecule on the graphite surface in the oxidative reaction condition and for preventing decreases in the oxo-basicity and generation rate of the terminal iron-oxo species. We also demonstrated that the graphite-supported catalyst exhibited appreciably enhanced activity under photoirradiation owing to the photothermal effect.
ABSTRACT
Hole-collecting monolayers have drawn attention in perovskite solar cell research due to their ease of processing, high performance, and good durability. Since molecules in the hole-collecting monolayer are typically composed of functionalized π-conjugated structures, hole extraction is expected to be more efficient when the π-cores are oriented face-on with respect to the adjacent surfaces. However, strategies for reliably controlling the molecular orientation in monolayers remain elusive. In this work, multiple phosphonic acid anchoring groups were used to control the molecular orientation of a series of triazatruxene derivatives chemisorbed on a transparent conducting oxide electrode surface. Using infrared reflection absorption spectroscopy and metastable atom electron spectroscopy, we found that multipodal derivatives align face-on to the electrode surface, while the monopodal counterpart adopts a more tilted configuration. The face-on orientation was found to facilitate hole extraction, leading to inverted perovskite solar cells with enhanced stability and high-power conversion efficiencies up to 23.0%.
ABSTRACT
To increase chemical reaction rates, general solutions include increasing the concentration/temperature and introducing catalysts. In this study, the rate constant of an electrophilic metal coordination reaction is accelerated 23-fold on the surface of layered aluminosilicate (LAS), where the reaction substrate (ligand molecule) induces dielectric polarization owing to the polar and anionic surface. According to the Arrhenius plot, the frequency factor (A) is increased by almost three orders of magnitude on the surface. This leads to the conclusion that the collision efficiency between the ligands and metal ions is enhanced on the surface due to the dielectric polarization. This is surprising because one side of the ligand is obscured by the surface, so the collision efficiency is expected to be decreased. This unique method to accelerate the chemical reaction is expected to expand the range of utilization of LASs, which are chemically inert, abundant, and environmentally friendly. The concept is also applicable to other metal oxides which have polar surfaces, which will be useful for various chemical reactions in the future.
ABSTRACT
The low-temperature activation of methane is highly important as a reaction that can dissociate the strongest C-H bond and convert it into useful compounds. This study demonstrated that supported platinum oxide was found to activate methane near room temperature and selectively afford methanol in the presence of oxygen.
ABSTRACT
A coordination-induced trigger for catalytic activity is proposed on an N-heterocyclic carbene (NHC)-decorated ceria catalyst incorporating Cr and Rh (ICy-r-Cr0.19Rh0.06CeOz). ICy-r-Cr0.19Rh0.06CeOz was prepared by grafting 1,3-dicyclohexylimidazol-2-ylidene (ICy) onto H2-reduced Cr0.19Rh0.06CeOz (r-Cr0.19Rh0.06CeOz) surfaces, which went on to exhibit substantial catalytic activity for the 1,4-arylation of cyclohexenone with phenylboronic acid, whereas r-Cr0.19Rh0.06CeOz without ICy was inactive. FT-IR, Rh K-edge XAFS, XPS, and photoluminescence spectroscopy showed that the ICy carbene-coordinated Rh nanoclusters were the key active species. The coordination-induced trigger for catalytic activity on the ICy-bearing Rh nanoclusters could not be attributed to electronic donation from ICy to the Rh nanoclusters. DFT calculations suggested that ICy controlled the adsorption sites of the phenyl group on the Rh nanocluster to promote the C-C bond formation of the phenyl group and cyclohexenone.
ABSTRACT
Binary alloy catalysts have the potential to exhibit higher activity than monometallic catalysts in nitrogen activation reactions. However, owing to the multiple possible combinations of metal elements constituting binary alloys, an exhaustive search for the optimal combination is difficult. In this study, we searched for the optimal binary alloy catalyst for nitrogen activation reactions using a combination of Bayesian optimization and density functional theory calculations. The optimal alloy catalyst proposed by Bayesian optimization had a surface energy of â¼0.2 eV/Å2 and resulted in a low reaction heat for the dissociation of the N≡N bond. We demonstrated that the search for such binary alloy catalysts using Bayesian optimization is more efficient than random search.
ABSTRACT
Adhesive strength varies greatly with direction; various adhesion tests have been conducted. In this study, the shear and tensile adhesive strength of epoxy resin for copper (Cu) and copper oxide (Cu2O) surfaces were estimated based on quantum chemical calculations. Here, density functional theory (DFT) calculations with dispersion correction were used. In the tensile process, the entire epoxy resin is peeled off vertically, whereas in the shear process, a force parallel to the adhesive surface is applied. Then, a bending moment acts on the adhesive layer, and a total force (stress) inclined at an angle θ with respect to the adherend surface is applied to the adhesive interface. We computed adhesive stress-displacement curves for each θ exhaustively and discussed the changes. When θ equals 90°, it corresponds to a tensile process. As θ decreases from 90°, the shear adhesive stress on both surfaces decreases slowly. When θ is less than 30°, the constraint to the surface causes periodic changes in the adhesive stress curves. The constraint to the Cu2O surface is especially strong, and this change is large. This periodicity is similar to the stick-slip phenomenon in tribology. To further understand the shear adhesive forces, force decomposition analysis was performed, revealing that the periodicity of the adhesive stress originates from the DFT contribution rather than the dispersion one. The procedure proposed in this study for estimating shear adhesive strength is expected to be useful in the evaluation and prediction of adhesive and adherend properties.
ABSTRACT
Oxidative addition of CH4 to the catalyst surface produces CH3 and H. If the CH3 species generated on the surface couple with each other, reductive elimination of C2H6 may be achieved. Similarly, H's could couple to form H2. This is the outline of nonoxidative coupling of methane (NOCM). It is difficult to achieve this reaction on a typical Pt catalyst surface. This is because methane is overoxidized and coking occurs. In this study, the authors approach this problem from a molecular aspect, relying on organometallic or complex chemistry concepts. Diagrams obtained by extending the concepts of the Walsh diagram to surface reactions are used extensively. C-H bond activation, i.e., oxidative addition, and C-C and H-H bond formation, i.e., reductive elimination, on metal catalyst surfaces are thoroughly discussed from the point of view of orbital theory. The density functional theory method for structural optimization and accurate energy calculations and the extended Hückel method for detailed analysis of crystal orbital changes and interactions play complementary roles. Limitations of monometallic catalysts are noted. Therefore, a rational design of single atom alloy (SAA) catalysts is attempted. As a result, the effectiveness of the Pt1/Au(111) SAA catalyst for NOCM is theoretically proposed. On such an SAA surface, one would expect to find a single Pt monatomic site in a sea of inert Au atoms. This is desirable for both inhibiting overoxidation and promoting reductive elimination.
ABSTRACT
Adhesive strength is known to change significantly depending on the direction of the force applied. In this study, the peel and tensile adhesive forces between the hydroxylated silica (001) surface and epoxy resin are estimated based on quantum chemical calculations. Here, density functional theory (DFT) with dispersion correction is used. In the peel process, the epoxy resin is pulled off from the terminal part, while in the tensile process, the entire epoxy resin is pulled off vertically. As a result of these calculations, the maximum adhesive force in the peel process is decreased to be about 40% of that in the tensile process. The adhesion force-displacement curve for the peeling process shows two characteristic peaks corresponding to the process where the adhesive molecule horizontally oriented to the surface shifts to a vertical orientation to the surface and the process where the vertical adhesive molecule is dissociated from the surface. Force decomposition analysis is performed to further understand the peel adhesion force; the contribution of the dispersion force is found to be slightly larger than that of the DFT force. This feature is common to the tensile process as well. Each force in the peel process is about 40% smaller than the corresponding force in the tensile process.