Zinc Oxide Films Fabricated via Sol-Gel Method and Dip-Coating Technique-Effect of Sol Aging on Optical Properties, Morphology and Photocatalytic Activity.

Zinc oxide layers on soda-lime glass substrates were fabricated using the sol-gel method and the dip-coating technique. Zinc acetate dihydrate was applied as the precursor, while diethanolamine as the stabilizing agent. This study aimed to determine what effect has the duration of the sol aging process on the properties of fabricated ZnO films. Investigations were carried out with the sol that was aged during the period from 2 to 64 days. The sol was studied using the dynamic light scattering method to determine its distribution of molecule size. The properties of ZnO layers were studied using the following methods: scanning electron microscopy, atomic force microscopy, transmission and reflection spectroscopy in the UV-Vis range, and the goniometric method for determination of the water contact angle. Furthermore, photocatalytic properties of ZnO layers were studied by the observation and quantification of the methylene blue dye degradation in an aqueous solution under UV illumination. Our studies showed that ZnO layers have grain structure, and their physical-chemical properties depend on the duration of aging. The strongest photocatalytic activity was observed for layers produced from the sol that was aged over 30 days. These layers have also the greatest porosity (37.1%) and the largest water contact angle (68.53°). Our studies have also shown that there are two absorption bands in studied ZnO layers, and values of optical energy band gaps determined from positions of maxima in reflectance characteristics are equal to those determined using the Tauc method. Optical energy band gaps of the ZnO layer fabricated from the sol aged over 30 days are EgI = 4.485 eV and EgII = 3.300 eV for the first and second bands, respectively. This layer also showed the highest photocatalytic activity, causing the pollution to degrade 79.5% after 120 min of UV irradiation. We believe that ZnO layers presented here, thanks to their attractive photocatalytic properties, may find application in environmental protection for the degradation of organic pollutants.

Sol-Gel Derived Silica-Titania Waveguide Films for Applications in Evanescent Wave Sensors-Comprehensive Study.

Composite silica-titania waveguide films of refractive index ca. 1.8 are fabricated on glass substrates using a sol-gel method and dip-coating technique. Tetraethyl orthosilicate and tetraethyl orthotitanate with molar ratio 1:1 are precursors. Fabricated waveguides are annealed at 500 °C for 60 min. Their optical properties are studied using ellipsometry and UV-Vis spectrophotometry. Optical losses are determined using the streak method. The material structure and chemical composition, of the silica-titania films are analyzed using transmission electron microscopy (TEM) and electron dispersive spectroscopy (EDS), respectively. The surface morphology was investigated using atomic force microscopy (AFM) and scanning electron microscopy (SEM) methods. The results presented in this work show that the waveguide films are amorphous, and their parameters are stable for over a 13 years. The optical losses depend on their thickness and light polarization. Their lowest values are less than 0.06 dB cm-1. The paper presents the results of theoretical analysis of scattering losses on nanocrystals and pores in the bulk and interfaces of the waveguide film. These results combined with experimental data clearly indicate that light scattering at the interface to a glass substrate is the main source of optical losses. Presented waveguide films are suitable for application in evanescent wave sensors.

Optical Thin Films Fabrication Techniques-Towards a Low-Cost Solution for the Integrated Photonic Platform: A Review of the Current Status.

In the past few decades, several methods concerning optical thin films have been established to facilitate the development of integrated optics. This paper provides a brief depiction of different techniques for implementing optical waveguide thin films that involve chemical, physical, and refractive index modification methods. Recent advances in these fabrication methods are also been presented. Most of the methods developed for the realization of the thin-films are quite efficient, but they are expensive and require sophisticated equipment. The major interest of the scientists is to develop simple and cost-effective methods for mass production of optical thin films resulting in the effective commercialization of the waveguide technology. Our research group is focused on developing a silica-titania optical waveguide platform via the sol-gel dip-coating method and implementing active and passive optical elements via the wet etching method. We are also exploring the possibility of using nanoimprint lithography (NIL) for patterning these films so that the fabrication process is efficient and economical. The recent developments of this platform are discussed. We believe that silica-titania waveguide technology developed via the sol-gel dip-coating method is highly attractive and economical, such that it can be commercialized for applications such as sensing and optical interconnects.

Subwavelength Grating Waveguide Structures Proposed on the Low-Cost Silica-Titania Platform for Optical Filtering and Refractive Index Sensing Applications.

The sol−gel dip-coating method is a cost-efficient way for the realization of thin films on a planar substrate. In this work, high-quality, low-loss, and low-surface roughness silica−titania thin films are deposited on a glass substrate with the sol−gel dip-coating method. This platform works in the visible to near-IR wavelength ranges and can be useful for several eye-catching photonic components. The paper is comprised of two parts: the first part deals with the development of a low-cost silica−titania waveguide system, whereas the second part provides detail on the numerical modeling of the SWG waveguide filter and SWG waveguide FP-sensor design. The SWG waveguide NIR-stopband filter can achieve an ER of >40 dB and 3-dB bandwidth of 110 nm designed at optimized parameters. The SWG waveguide-FP structure proposed in this work act as a refractive index sensor where the sensitivity is ~120 nm/RIU by reducing the width of the waveguide. This sensitivity can be further enhanced by reducing the waveguide height. We believe that this work is quite important for the realization of low-cost integrated photonic devices based on the silica−titania platform developed via the sol−gel dip-coating method.

High Refractive Index Silica-Titania Films Fabricated via the Sol-Gel Method and Dip-Coating Technique-Physical and Chemical Characterization.

Crack-free binary SiOx:TiOy composite films with the refractive index of ~1.94 at wavelength 632.8 nm were fabricated on soda-lime glass substrates, using the sol-gel method and dip-coating technique. With the use of transmission spectrophotometry and Tauc method, the energy of the optical band gap of 3.6 eV and 4.0 eV were determined for indirect and direct optical allowed transitions, respectively. Using the reflectance spectrophotometry method, optical homogeneity of SiOx:TiOy composite films was confirmed. The complex refractive index determined by spectroscopic ellipsometry confirmed good transmission properties of the developed SiOx:TiOy films in the Vis-NIR spectral range. The surface morphology of the SiOx:TiOy films by atomic force microscopy (AFM) and scanning electron microscopy (SEM) methods demonstrated their high smoothness, with the root mean square roughness at the level of ~0.15 nm. Fourier-transform infrared (FTIR) spectroscopy and Raman spectroscopy were used to investigate the chemical properties of the SiOx:TiOy material. The developed binary composite films SiOx:TiOy demonstrate good waveguide properties, for which optical losses of 1.1 dB/cm and 2.7 dB/cm were determined, for fundamental TM0 and TE0 modes, respectively.

Mode Sensitivity Exploration of Silica-Titania Waveguide for Refractive Index Sensing Applications.

In this paper, a novel and cost-effective photonic platform based on silica-titania material is discussed. The silica-titania thin films were grown utilizing the sol-gel dip-coating method and characterized with the help of the prism-insertion technique. Afterwards, the mode sensitivity analysis of the silica-titania ridge waveguide is investigated via the finite element method. Silica-titania waveguide systems are highly attractive due to their ease of development, low fabrication cost, low propagation losses and operation in both visible and near-infrared wavelength ranges. Finally, a ring resonator (RR) sensor device was modelled for refractive index sensing applications, offering a sensitivity of 230 nm/RIU, a figure of merit (FOM) of 418.2 RIU-1, and Q-factor of 2247.5 at the improved geometric parameters. We believe that the abovementioned integrated photonics platform is highly suitable for high-performance and economically reasonable optical sensing devices.