Article in English | LILACS-Express | LILACS | ID: biblio-1528851

ABSTRACT

The present study analyzed the microhardness and degree of conversion of three Bulk Fill resins (M1 - Filtek Bulk Fill; M2 - Tetric N-Ceram Bulk Fill and M3 - Opus Bulk Fill) polymerized by single peak and polywave Light-emitting Diode Curing Lights. A total 90 test specimens (n=10) were obtained using a Teflon matrix for the purpose of testing microhardness; and for degree of conversion: 135 specimens (n=5) by using a 2 x 6 cm matrix. The specimens were light polymerized using 3 light sources (L1 - Optilight Max, L2 - Bluephase, L3 - VALO). They were kept in artificial saliva om an oven at 37±1°C during the experiment. The degree of conversion was measured by FTIR 24 h after obtaining each test specimen. The microhardness readouts were performed with a microdurometer at the time intervals of 48 hours (T0), 7 days (T1), 14 days (T2) and 21 days (T3). M1L3 was found to show the highest microhardness values in T2, and M1 showed the lowest degree of conversion in the deep third with L1. It was concluded that Filtek Bulk Fill resin showed the best results in comparison with the other resins.


El presente estudio analizó la microdureza y el grado de conversión de tres resinas Bulk Fill (M1 - Filtek Bulk Fill; M2 - Tetric N-Ceram Bulk Fill y M3 - Opus Bulk Fill) polimerizadas por lámparas de curado de diodo emisor de luz de pico único y polionda. Se obtuvieron un total de 90 especímenes de prueba (n=10) utilizando una matriz de teflón con el propósito de probar la microdureza; y para grado de conversión: 135 especímenes (n=5) utilizando una matriz de 2 x 6 cm. Las muestras se fotopolimerizaron utilizando 3 fuen- tes de luz (L1 - Optilight Max, L2 - Bluephase, L3 - VALO). Se mantuvieron en saliva artificial en estufa a 37 ±1°C durante el experimento. El grado de conversión se midió por FTIR 24 h después de obtener cada muestra de prueba. Las lecturas de microdureza se realizaron con un microdurómetro en los intervalos de tiempo de 48 horas (T0), 7 días (T1), 14 días (T2) y 21 días (T3). Se encontró que M1L3 mostraba los valores más altos de microdureza en T2, y M1 mostraba el grado más bajo de conversión en el tercio profundo con L1. Se concluyó que la resina Filtek Bulk Fill mostró los mejores resultados en comparación con las demás resinas.

2.
Braz. j. oral sci ; 22: e230282, Jan.-Dec. 2023. tab
Article in English | LILACS, BBO - Dentistry | ID: biblio-1510253

ABSTRACT

Aim: Evaluate the roughness, microhardness and color change of different Bulk Fill resins when submitted to the condition of gastroesophageal reflux and bulimia. Methods: 60 specimens (n = 10) of Bulk-Fill composite resins were made: M1 ­ Filtek™; M2 ­ Tetric N-Ceram and M3 ­ OPUS, through a matrix 2x6 mm and light cured by the VALO light source. After polishing, initial analyzes (48 hours - T0) of surface roughness (Ra), microhardness (VHN) and color change (ΔE) were performed. To simulate the oral condition of severe gastroesophageal reflux and bulimia, the specimens were immersed in hydrochloric acid (S1) (pH 1.7) 4 minutes a day, for 7 days. Control group specimens were immersed in artificial saliva (S2). Subsequently to immersions, mechanical brushing was performed for 3 minutes, three times a day, simulating 7 days of brushing. And again, the analyzes of Ra, VHN and ΔE were performed (7 days - T1). Thus, hydrochloric acid immersion, mechanical brushing and Ra analysis were repeated at 14 days (T2) and 21 days (T3); and T2, T3 and T4 (3 years) for VHN and ΔE. Results: After Shapiro-Wilk statistical test, ANOVA and Tukey test with Bonferroni adjustment (p>0.05), M3 showed the lowest Ra at all times compared to the other resins, while the highest Ra was at T0. M1 and T1 showed higher VHN. And M2 and T4 showed higher ΔE. Conclusion: Bulk Fill resins can be indicated for patients with Gastroesophageal Reflux and Bulimia, nonetheless, Tetric N-Ceram resin showed the worst results


Subject(s)
Color , Composite Resins , Hardness , Hydrochloric Acid , Gastroesophageal Reflux , Bulimia
3.
Article in English | LILACS-Express | LILACS | ID: biblio-1385887

ABSTRACT

ABSTRACT: The present study analyzed the color change (DE) and surface roughness (Ra) of glass ionomer cements (GICs) subjected to typical herbaceous South American beverage action - Ilex paraguariensis. 90 specimens (n = 10) were made: M1 - GIC Riva Light Cure® (SDI); M2 - GIC Riva Self Cure® (SDI); M3 - GIC Vitremer® (3M ESPE). After light curing/ polymerization of GICs, specimens were divided for being submitted to solutions for one hour a day for 21 days: S1 - Yerba Mate Pajarito Traditional (Pajarito); S2 - Erva Mate Chimarrão (Barão de Cotegipe); S3 - Water (control). Four DE and Ra readings were taken: T0 - initial; T1 - 7 days; T2 - 14 days and T3 - 21 days, with a spectrophotometer and a roughness meter respectively. The obtained data were submitted to ANOVA statistical analysis and Bonferroni. S1 and S2 at T1 and T2 there was no statistical difference between the materials, and at T3 Materials M1=M2, M1=M3, and M2>M3. For S3 at T1, T2 and T3 there was no difference between the materials. Analyzing surface roughness, there was no statistical significance. Concluded that all materials changed color with greater influence of time, but without changing surface roughness.


RESUMEN: En el presente estudio se analizó el cambio de color (DE) y la rugosidad superficial (Ra) de los cementos ionómero de vidrio (CIV) sometidos a la acción típica de las bebidas herbáceas sudamericanas - Ilex paraguariensis. Se realizaron 90 especímenes (n = 10): M1 - GIC Riva Light Cure® (SDI); M2 - GIC Riva Self Cure® (SDI); M3 - GIC Vitremer® (3M ESPE). Después de la fotopolimerización/ polimerización de los CIV, los especímenes se dividieron y fueron sometidos a soluciones durante una hora al día durante 21 días: S1 - Yerba Mate Pajarito Tradicional (Pajarito); S2 - Erva Mate Chimarrão (Barão de Cotegipe); S3 - Agua (control). Se tomaron cuatro lecturas de DE y Ra: T0 - inicial; T1 - 7 días; T2 - 14 días y T3 - 21 días, con espectrofotómetro y rugosímetro respectivamente. Los datos obtenidos fueron sometidos a análisis estadístico ANOVA y Bonferroni. S1 y S2 en T1 y T2 no hubo diferencia estadística entre los materiales y en T3 Materiales M1=M2, M1=M3 y M2>M3. Para S3 en T1, T2 y T3 no hubo diferencia entre los materiales. Al analizar la rugosidad de la superficie, no hubo significación estadística. En conclusion, todos los materiales cambiaron de color con mayor influencia del tiempo, pero sin cambiar la rugosidad de la superficie.

4.
J Conserv Dent ; 24(4): 379-383, 2021.
Article in English | MEDLINE | ID: mdl-35282585

ABSTRACT

Aim: This study evaluates Vickers microhardness and surface roughness in Biodentine cement (M1) and glass-ionomer cement Fuji IX (M2), both immersed in mouthwash. Materials and Methods: Fifty-four samples were randomly distributed in distilled water (S1), Listerine Cool Mint (S2), and Colgate Plax (S3). Each sample was put in a flask with mouthwash for 2 min, under vibration, twice a day for 21 days. Microhardness and surface roughness were assessed at 48 h (T0), 7 days (T1), 14 days (T2), and 21 days (T3). Results: For roughness: time (T), solution (S) and material (M), TxM, and SxM and for microhardness: M, TxS, TxM, and SxM were statistically significant. T3, M1, M1T3, and M1S1 presented the highest surface roughness. M2, M1T0, M1T1, M1T2, M1S1, and M1S2 presented higher microhardness. Conclusion: Biodentine showed higher surface roughness for T1, T2, and T3 and higher microhardness for T0, T1, and T2 against Fuji IX. Biodentine presented higher microhardness independently of solution.

SELECTION OF CITATIONS