Self-assembly of CdSe 3D urchins and their photocatalytic response.

Photocatalysis is found to be one of the best suited processes that respond to the purification of water systems and the semiconductor nanomaterials are learned to be incredible materials which carry out the photocatalytic process as they readily decompose the pollutants effectively. In this present work, CdSe nanoparticles belonging to II-VI group semiconductor compounds were synthesized using a facile hydrothermal process with different precursor concentrations and were analysed for various characterization studies such as X-ray diffraction (XRD), Transmission electron microscopy (TEM), UV-vis absorption spectroscopy, Fourier transform infrared spectroscopy (FTIR) and Photoluminescence (PL) studies. The XRD study of the synthesized CdSe nanostructures revealed that the average crystallite size was ranging from 18.5 nm to 24 nm pointing out the increase in size with increase in molar concentrations. The morphological structure of synthesized CdSe samples exhibited urchin-like structure for a lower concentration with several rod-like projections appearing in diverse directions. These CdSe nano-urchins synthesized with lower concentrations are found suitable to carry out the process of photocatalytic activity. The process was carried out under visible light radiation for 180 min with aqueous solution of methylene blue (MB) as the ideal toxin to be degraded. The attained degradation efficiency was nearly 80% clearly displaying that the synthesized samples are good photocatalysts. By tuning the bandgap, through the optimization of the precursor concentrations, greater efficiency can be achieved in future.

Photocatalytic degradation effect of CdSe nanoparticles for textile wastewater effluents at low cost and proves to be efficient method.

Semiconductor nanoparticles and nanocrystals have a great impact due to its contribution in the diverse fields including electronics, solar energy, biological imaging, and photonics. Among these semiconductor nanoparticles, cadmium selenide of II-VI group binary semiconductor nanoparticles were synthesized using solvothermal process for the different reaction temperatures. The XRD pattern of the synthesized samples confirms the crystalline nature of the samples and showed increase in its crystallite size with rise in temperature. The morphology of the samples was analysed with TEM images and found that the nanoparticles synthesized at different temperatures were varied in size and shape indicating the increase in the size of the particles with the raise in temperature. The optical properties of the samples pointed out that they exhibit a blue shift owing to quantum confinement. Photocatalytic activity was carried out for the synthesized samples under visible light radiation using methylene blue (MB) as a model pollutant and it proved to be a good photocatalyst achieving the efficiency of 75% which is promising for future application with good optimization. The efficiency could be increased when these semiconductor CdSe nanoparticles are doped with metal particles due to an increase in the absorption edge wavelength and a decrease in bandgap energy were reported in detail.

Regeneration study of MB in recycling runs over nickel vanadium oxide by solvent extraction for photocatalytic performance for wastewater treatments.

Recently, researchers are concentrating on the synthesis of composite materials to enhance the efficiency of the materials in various applications. In this work, nickel vanadium oxide (NiV2O6) nanocomposite material is prepared via two methods and the prepared samples have been characterized with basic studies to analyse the effect of preparation method and the reaction time. The XRD studies reveal a polycrystalline growth in both the methods. The broad XRD peaks obtained for samples prepared via hydrothermal method suggests the size reduction and 1D nanostructure formation. The SEM analysis shows the formation of 1D structures in hydrothermal and 3D microsphere structures in solvothermal methods. The possible formation mechanism behind this formation has been discussed in this manuscript. The FTIR peaks in the fingerprint region confirm the formation and vibration of metal-oxygen bonds. The large optical bandgap values obtained from Tauc plot again confirms the formation of nanostructures of the synthesized samples. The photocatalytic activity of nickel vanadium oxide on methylene blue dye under halogen light were performed and, the recyclability of the sample is investigated. It was found from the photocatalytic spectrum that, the samples prepared from both the methods shows a degradation efficiency of more than 80% within 150 min. It was confirmed that the prepared NiV2O6 photocatalyst samples does not lose their degradation ability even after five cycles of repeated usage.

Photocatalytic effect of CuO nanoparticles flower-like 3D nanostructures under visible light irradiation with the degradation of methylene blue (MB) dye for environmental application.

The present research work focuses on preparing 3D transition metal doped copper oxide nanostructures through sonication method and to investigate the effect of doping different transition metal into copper oxide (CuO) on the basic properties of CuO nanoparticles and, to study the photocatalytic behaviour of the doped CuO samples. The morphological studies performed with the help of SEM revealed the formation of flower like CuO 3D nanostructures for all the doped samples. The slight shift in the position of peaks in the x-ray diffraction (XRD) pattern confirms that doping has been successfully done into CuO. Also, the sharp diffraction peaks suggest the polycrystalline nature of the sample with monoclinic structure. The UV-vis absorption analysis reveals a bandgap of 2.26, 2.12 and 2.15 eV for the CuO samples doped with nickel, zinc, and iron respectively via Tauc plot. The photocatalytic performance of the samples tested through the degradation of methylene blue (MB) dye suggests that samples doped with Zn shows better degradation. Thus, it is evident that the morphology and the optical properties of the CuO can be tailored by doping transition metal into it.