ABSTRACT
In this study, we report the modification of flexible copper films via the spontaneous reduction of aryldiazonium gold salts [X-4-C6H4N≡N]AuCl4 (XâCOOH, NO2). The electroless modification involves dipping of flexible copper films in the aryldiazonium gold solutions for a few seconds, under ambient conditions, followed by a washing step with deionized water to obtain a mechanically robust gold-aryl coating. The chemical composition, morphology, electronic structure, and optical properties of the gold-aryl layer and the flexibility of the modified copper films are supported by the results from X-ray photoelectron spectroscopy (XPS), electrochemistry, contact angle, scanning electron microscopy (SEM), and ultraviolet photoelectron spectroscopy (UPS). XPS surface analysis showed metallic gold in addition to C-C, C-O/C-N, and CâO functional groups from the grafted aryls. Cu 2p showed metallic copper as a major component and a small amount of Cu(II) ions. Wettability studies showed that Au-COOH@Cu increased the contact angle of the bare copper films from 68.0 ± 0.7° to 82.0° ± 0.7°, while Au-NO2@Cu increased the contact angle to 134.0° ± 0.3°. UPS energy profile analysis of [HOOC-4-C6H4N≡N]AuCl4 (valence band maximum = 1.91 eV) exhibited greater reducibility than [O2N-4-C6H4N≡N]AuCl4 (valence band maximum = 2.91 eV). The lower ionization potential of [HOOC-4-C6H4N≡N]AuCl4 (IP = 4.33 eV) enhanced the reactivity upon copper film contact, potentially inducing efficient energy level alignment, compared with [O2N-4-C6H4N≡N]AuCl4 (IP = 5.62 eV). UPS results were further supported by electrochemistry investigation which revealed that [HOOC-4-C6H4N≡N]AuCl4 is easily reducible compared with [O2N-4-C6H4N≡N]AuCl4. The findings presented here hold significant implications for developing flexible copper films and pave the way for future advancements in electronic material modification for industrial applications.
ABSTRACT
In the present study, high purity copper oxide nanoparticles (NPs) were synthesised using Tridax procumbens leaf extract. Green syntheses of nano-mosquitocides rely on plant compounds as reducing and stabilising agents. Copper oxide NPs were characterised using X-ray diffraction (XRD) analysis, Fourier transform infrared (FT-IR), Field-emission scanning electron microscopy with energy dispersive spectroscopy, Ultraviolet-visible spectrophotometry and fluorescence spectroscopy. XRD studies of the NPs indicate crystalline nature which was perfectly matching with a monoclinic structure of bulk CuO with an average crystallite size of 16â nm. Formation of copper oxide NPs was confirmed by FT-IR studies and photoluminescence spectra with emission peaks at 331, 411 and 433â nm were assigned to a near-band-edge emission band of CuO in the UV, violet and blue region. Gas chromatography-mass spectrometry studies inferred the phytochemical constituents of the leaf extract. Larvicidal activity of synthesised NPs using T. procumbens leaf extract was tested against Aedes aegypti species (dengue, chikungunya, zika and yellow fever transmit vector).