Effects of High Temperature on Creep Behaviour of Glazed Hollow Bead Insulation Concrete.

Glazed hollow bead insulation concrete (GHBC) presents a promising application prospect in terms of its light weight and superior fire resistance. However, only a few studies have focused on the creep behaviour of GHBC exposed to high temperatures. Therefore, in this study, the mechanism of high temperature on GHBC is analysed through a series of tests on uniaxial compression and multistage creep of GHBC, exposed from room temperature up to 800 °C. The results show a decrease in the weight and compressive strength of GHBC as the temperature rises. After 800 °C, the loss of weight and strength reach to 9.67% and 69.84%, respectively. The creep strain and creep rate increase, with a higher target temperature and higher stress level, while the transient deformation modulus, the creep failure threshold stress, and creep duration are reduced significantly. Furthermore, the creep of GHBC exhibits a considerable increase above 600 °C and the creep under the same loading ratio at 600 °C increases by 74.19% compared to the creep at room temperature. Indeed, the higher the temperature, the more sensitive the stress is to the creep. Based on our findings, the Burgers model agrees well with the creep test data at the primary creep and steady-state creep stages, providing a useful reference for the fire resistance design calculation of the GHBC structures.

Printing the Ultra-Long Ag Nanowires Inks onto the Flexible Textile Substrate for Stretchable Electronics.

: Printing technology offers a simple and cost-effective opportunity to develop all-printed stretchable circuits and electronic devices, possibly providing ubiquitous, low-cost, and flexible devices. To successfully prepare high-aspect-ratio Ag nanowires (NWs), we used water and anhydrous ethanol as the solvent and polyvinylpyrrolidone (PVP) as the viscosity regulator to obtain a water-soluble Ag NWs conductive ink with good printability. Flexible and stretchable fabric electrodes were directly fabricated through screen printing. After curing at room temperature, the sheet resistance of the Ag NW fabric electrode was 1.5 Ω/sq. Under a tensile strain of 0-80% and with 20% strains applied for 200 cycles, good conductivity was maintained, which was attributed to the inherent flexibility of the Ag NWs and the intrinsic structure of the interlocked texture.