ABSTRACT
The effective reuse of waste glass fiber-reinforced plastic (GFRP) is desired. We previously produced porous ceramics by firing mixtures of crushed GFRP and clay in a reducing atmosphere and demonstrated their applicability as adsorbents for the removal of basic dyes from dyeing wastewater. However, the primary influencing factors and the dye adsorption mechanism have not been fully elucidated, and the adsorption of acidic and direct dyes has not been clarified. In this study, adsorption tests were conducted, and the effects of the firing atmosphere, specific surface area, type of dye, and individual components were comprehensively investigated. The results showed that reductively fired ceramics containing plastic carbide residue adsorbed basic dye very well but did not adsorb acidic dye well. The clay structure was the primary factor for the dye adsorption rather than the GFRP carbide. The mechanism for the basic dye adsorption appears to have been an increase in specific surface area due to the plastic carbide residue in the ceramic structure, which increased the ion exchange between the clay minerals and the dye. By adjusting the pH of the aqueous solution, the GFRP/clay ceramic also adsorbed considerable amounts of direct dye, so the mechanism was determined to be ion exchange with the calcium component of the glass fibers.
ABSTRACT
To reuse waste glass fiber-reinforced plastics (GFRPs), porous ceramics (i.e., GFRP/clay ceramics) were produced by mixing crushed GFRP with clay followed by firing the resulting mixture under different conditions. The possibility of using ceramics fired under a reducing atmosphere as adsorbent materials to remove NOx and SOx from combustion gases of fossil fuels was investigated because of the high porosity, specific surface area, and contents of glass fibers and plastic carbides of the ceramics. NO2 and SO2 adsorption tests were conducted on several types of GFRP/clay ceramic samples, and the gas concentration reduction rates were compared to those of a clay ceramic and a volcanic pumice with high NO2 adsorption. In addition, to clarify the primary factor affecting gas adsorption, adsorption tests were conducted on the glass fibers in the GFRP and GFRP carbides. The reductively fired GFRP/clay ceramics exhibited high adsorption performance for both NO2 and SO2. The primary factor affecting the NO2 adsorption of the ceramics was the plastic carbide content in the clay structure, while that affecting the SO2 adsorption of the ceramics was the glass fiber content.