Sorafenib Nanomicelles Effectively Shrink Tumors by Vaginal Administration for Preoperative Chemotherapy of Cervical Cancer.

To investigate the potential of sorafenib (SF) in preoperative chemotherapy for cervical cancer to reduce tumor volume, sorafenib micelles (SF micelles) with good stability and high drug loading were designed. SF micelles were prepared by film hydration followed by the ultrasonic method. The results showed that the SF micelles were spherical with an average particle size of 67.18 ± 0.66 nm (PDI 0.17 ± 0.01), a considerable drug loading of 15.9 ± 0.46% (w/w%) and satisfactory stability in buffers containing plasma or not for at least 2 days. In vitro release showed that SF was gradually released from SF micelles and almost completely released on the third day. The results of in vitro cellular intake, cytotoxicity and proliferation of cervical cancer cell TC-1 showed that SF micelles were superior to sorafenib (Free SF). For intravaginal administration, SF micelles were dispersed in HPMC (SF micelles/HPMC), showed good viscosity sustained-release profiles in vitro and exhibited extended residence in intravaginal in vivo. Compared with SF micelles dispersed in N.S. (SF micelles/N.S.), SF micelles/HPMC significantly reduced tumor size with a tumor weight inhibition rate of 73%. The results suggested that SF micelles had good potential for preoperative tumor shrinkage and improving the quality life of patients.

Coaxial Electrospun PLLA Fibers Modified with Water-Soluble Materials for Oligodendrocyte Myelination.

Myelin sheaths are essential in maintaining the integrity of axons. Development of the platform for in vitro myelination would be especially useful for demyelinating disease modeling and drug screening. In this study, a fiber scaffold with a core-shell structure was prepared in one step by the coaxial electrospinning method. A high-molecular-weight polymer poly-L-lactic acid (PLLA) was used as the core, while the shell was a natural polymer material such as hyaluronic acid (HA), sodium alginate (SA), or chitosan (CS). The morphology, differential scanning calorimetry (DSC), Fourier transform infrared spectra (FTIR), contact angle, viability assay, and in vitro myelination by oligodendrocytes were characterized. The results showed that such fibers are bead-free and continuous, with an average size from 294 ± 53 to 390 ± 54 nm. The DSC and FTIR curves indicated no changes in the phase state of coaxial brackets. Hyaluronic acid/PLLA coaxial fibers had the minimum contact angle (53.1° ± 0.24°). Myelin sheaths were wrapped around a coaxial electrospun scaffold modified with water-soluble materials after a 14-day incubation. All results suggest that such a scaffold prepared by coaxial electrospinning potentially provides a novel platform for oligodendrocyte myelination.

Sequential Release of Paclitaxel and Imatinib from Core-Shell Microparticles Prepared by Coaxial Electrospray for Vaginal Therapy of Cervical Cancer.

To optimize the anti-tumor efficacy of combination therapy with paclitaxel (PTX) and imatinib (IMN), we used coaxial electrospray to prepare sequential-release core-shell microparticles composed of a PTX-loaded sodium hyaluronate outer layer and an IMN-loaded PLGA core. The morphology, size distribution, drug loading, differential scanning calorimetry (DSC), Fourier transform infrared spectra (FTIR), in vitro release, PLGA degradation, cellular growth inhibition, in vivo vaginal retention, anti-tumor efficacy, and local irritation in a murine orthotopic cervicovaginal tumor model after vaginal administration were characterized. The results show that such core-shell microparticles were of spherical appearance, with an average size of 14.65 µm and a significant drug-loading ratio (2.36% for PTX, 19.5% for IMN, w/w), which might benefit cytotoxicity against cervical-cancer-related TC-1 cells. The DSC curves indicate changes in the phase state of PTX and IMN after encapsulation in microparticles. The FTIR spectra show that drug and excipients are compatible with each other. The release profiles show sequential characteristics in that PTX was almost completely released in 1 h and IMN was continuously released for 7 days. These core-shell microparticles showed synergistic inhibition in the growth of TC-1 cells. Such microparticles exhibited prolonged intravaginal residence, a >90% tumor inhibitory rate, and minimal mucosal irritation after intravaginal administration. All results suggest that such microparticles potentially provide a non-invasive local chemotherapeutic delivery system for the treatment of cervical cancer by the sequential release of PTX and IMN.

Synergistic Antitumor Effects on Drug-Resistant Breast Cancer of Paclitaxel/Lapatinib Composite Nanocrystals.

Drug resistance presents serious difficulties for cancer treatment. A combination of paclitaxel (PTX) and lapatinib (LAPA) shows potentials in multiple drug resistant cancers in the clinic, but it is almost impossible to deliver these two drugs to the tumor at the same time with the best proportion by simple co-administration of the respective current formualtions for their different pharmacokinetic profiles. Here composite nanocrystals of PTX and LAPA (cNC) were designed with a ratio of 2:1 (w/w), which was their intracellular ratio at the best synergistic efficacy on a drug-resistant cancer cell line (MCF-7/ADR). Such cNC were prepared using a bottom-up method to achieve a nearly spherical appearance and a narrow size distribution of 95.1 ± 2.1 nm. For nanocrystal stabilization, Polyethylene glycol (PEG) coating was introduced into the cNC via polydopamine (PDA) coating in order to get a PEGylated composite nanocrystal (cNC@PDA-PEG) with nanoscale size (170.5 ± 1.4 nm), considerable drug loading (PTX: 21.33 ± 1.48%, LAPA: 10.95 ± 1.24%) and good stability for at least 4 days in plasma-containing buffers. Differential scanning calorimeter (DSC) and XRD data both indicated the different crystalline states of the cNC as well as the cNC@PDA-PEG in comparison with bulk drugs. In vitro release data showed that PTX and LAPA were gradually and completely released from cNC@PDA-PEG in 3 days, while drug release from bulk drugs or cNC was only 30%. cNC@PDA-PEG also showed negligible hemolysis in vitro. Cellular uptake experiments in the MCF-7/ADR cell line showed that the nanocrystals entered the cells in a complete form through endocytosis and then released the drug in the cell. cNC@PDA-PEG inhibits the growth of this drug-resistant cell more effectively than the unmodified version (cNC). In summary, PEGylated PTX and LAPA composite nanocrystals showed the potential for treament of drug-resistant tumors by simultaneously delivering two drugs to tumor cells with the best proportion.