ABSTRACT
InGaN/GaN multi-quantum wells (MQWs) are grown on (0001) sapphire substrates by metal organic chemical vapor deposition (MOCVD) with special growth parameters to form V-shaped pits simultaneously. Measurements by atomic force microscopy (AFM) and transmission electron microscopy (TEM) demonstrate the formation of MQWs on both (0001) and ([Formula: see text]) side surface of the V-shaped pits. The latter is known to be a semi-polar surface. Optical characterizations together with theoretical calculation enable us to identify the optical transitions from these MQWs. The layer thickness on ([Formula: see text]) surface is smaller than that on (0001) surface, and the energy level in the ([Formula: see text]) semi-polar quantum well (QW) is higher than in the (0001) QW. As the sample temperature is increased from 15 K, the integrated cathodoluminescence (CL) intensity of (0001) MQWs increases first and then decreases while that of the ([Formula: see text]) MQWs decreases monotonically. The integrated photoluminescence (PL) intensity of (0001) MQWs increases significantly from 15 to 70 K. These results are explained by carrier injection from ([Formula: see text]) to (0001) MQWs due to thermal excitation. It is therefore concluded that the emission efficiency of (0001) MQWs at high temperatures can be greatly improved due to the formation of semi-polar MQWs.
ABSTRACT
Strong localization effect in self-assembled InGaN quantum dots (QDs) grown by metalorganic chemical vapor deposition has been evidenced by temperature-dependent photoluminescence (PL) at different excitation power. The integrated emission intensity increases gradually in the range from 30 to 160 K and then decreases with a further increase in temperature at high excitation intensity, while this phenomenon disappeared at low excitation intensity. Under high excitation, about 40% emission enhancement at 160 K compared to that at low temperature, as well as a higher internal quantum efficiency (IQE) of 41.1%, was observed. A strong localization model is proposed to describe the possible processes of carrier transport, relaxation, and recombination. Using this model, the evolution of excitation-power-dependent emission intensity, shift of peak energy, and linewidth variation with elevating temperature is well explained. Finally, two-component decays of time-resolved PL (TRPL) with various excitation intensities are observed and analyzed with the biexponential model, which enables us to further understand the carrier relaxation dynamics in the InGaN QDs.