ABSTRACT
OBJECTIVE: To evaluate experimental dimethacrylate-based materials containing calcium orthophosphates or calcium silicate particles in terms of their optical, mechanical and Ca2+ release behaviour. METHODS: Dicalcium phosphate dihydrate (DCPD), hydroxyapatite (HAp), beta-tricalcium phosphate (ß-TCP) or calcium silicate (CaSi) particles were added to a photocurable BisGMA/TEGDMA resin (1:1 in mols) at a 30 vol% fraction. Materials containing silanized or non-silanized barium glass particles were used as controls. Degree of conversion (DC) at the top and base of 2-mm thick specimens was determined by ATR-FTIR spectroscopy (n = 5). Translucency parameter (TP) and transmittance (%T) were determined using a spectrophotometer (n = 3). Biaxial flexural strength (BFS) and flexural modulus (FM) were determined by biaxial flexural testing after 24 h storage in water (n = 10). Ca2+ release in water was determined during 28 days by inductively coupled plasma optical emission spectrometry (n = 3). Statistical analysis was performed using ANOVA/Tukey test (DC: two-way; TP, %T; BFS and FM: one-way; Ca2+ release: repeated measures two-way, α = 5 %). RESULTS: CaSi and ß-TCP particles drastically reduced DC at 2 mm, TP and %T (p < 0.001). Compared to both controls, all Ca2+-releasing materials presented lower BFS (p < 0.001) and only the material with DCPD showed significantly lower FM (p < 0.05). The material containing CaSi presented the highest Ca2+ release, while among materials formulated with calcium orthophosphates the use of DCPD resulted in the highest release (p < 0.001). SIGNIFICANCE: CaSi particles allowed the highest Ca2+ release. Notwithstanding, the use of DCPD resulted in a material with the best compromise between optical behaviour, DC, strength and Ca2+ release.
ABSTRACT
OBJECTIVE: The study aims to evaluate the effect of a glass ionomer cement (GIC; Fuji 9 Gold Label, GC) with added calcium orthophosphate particles and a calcium silicate cement (CSC; Biodentine, Septodont) regarding ion release, degradation in water, mineral content, and mechanical properties of demineralized dentin samples. METHODS: GIC, GIC + 5% DCPD (dicalcium phosphate dihydrate), GIC + 15% DCPD, GIC + 5% ß-TCP (tricalcium phosphate), GIC + 15% ß-TCP (by mass), and CSC were evaluated for Ca2+/Sr2+/F- release in water for 56 days. Cement mass loss was evaluated after 7-day immersion in water. Partially demineralized dentin disks were kept in contact with materials while immersed in simulated body fluid (SBF) at 37 °C for 56 days. The "mineral-to-matrix ratio" (MMR) was determined by ATR-FTIR spectroscopy. Dentin hardness and elastic modulus were obtained by nanoindentation. Samples were observed under scanning and transmission electron microscopy. Data were analyzed by ANOVA/Tukey test (α = 0.05). RESULTS: Ca2+ release from CSC and GIC (µg/cm2) were 4737.0 ± 735.9 and 13.6 ± 1.6, respectively. In relation to the unmodified GIC, the addition of DCPD or ß-TCP increased ion release (p < 0.001). Only the dentin disks in contact with CSC presented higher MMR (p < 0.05) and mechanical properties than those restored with a resin composite used as control (p < 0.05). Mass loss was similar for GIC and CSC; however, the addition of DCPD or ß-TCP increased GIC degradation (p < 0.05). CONCLUSION: Despite the increase in ion release, the additional Ca2+ sources did not impart remineralizing capability to GIC. Both unmodified GIC and CSC showed similar degradation in water. CLINICAL RELEVANCE: CSC was able to promote dentin remineralization.