Formulation, preparation and in vitro - in vivo evaluation of compression-coated tablets for the colonic-specific release of ketoprofen

ABSTRACT The aim of this study was to formulate and prepare compression-coated tablets for colonic release (CR-tablets), and to evaluate the bioavailability of ketoprofen following the administration of a single dose from mini-tablets with immediate release (IR-tablets) compared to CR-tablets. CR-tablets were prepared based on time-controlled hydroxypropylmethylcellulose K100M inner compression-coating and pH-sensitive Eudragit® L 30D-55 outer film-coating. The clinical bioavailability study consisted of two periods, in which two formulations were administered to 6 volunteers, according to a randomized cross-over design. The apparent cumulative absorption amount of ketoprofen was estimated by plasma profile deconvolution. CR-tablets were able to delay ketoprofen's release. Compared to IR-tablets used as reference, for the CR-tablets the maximum plasma concentration (Cmax) was lower (4920.33±1626.71 ng/mL vs. 9549.50±2156.12 ng/mL for IR-tablets) and the time needed to reach Cmax (tmax) was 5.33±1.63 h for CR-tablets vs. 1.33±0.88 h for IR-tablets. In vitro-in vivo comparison of the apparent cumulative absorption amount of ketoprofen showed similar values for the two formulations. Therefore, the obtained pharmacokinetic parameters and the in vitro-in vivo comparison demonstrated the reliability of the developed pharmaceutical system and the fact that it is able to avoid the release of ketoprofen in the first part of the digestive tract.

Polymeric prodrug-functionalized polypropylene films for sustained release of salicylic acid.

Medical devices decorated with salicylic acid-based polymer chains (polymeric prodrug) that slowly release this anti-inflammatory and anti-biofilm drug at the implantation site were designed. A "grafting from" method was implemented to directly grow chains of a polymerizable derivative of salicylic acid (2-methacryloyloxy-benzoic acid, 2MBA) onto polypropylene (PP). PP was modified both at bulk and on the surface with poly(2MBA) by means of an oxidative pre-irradiation method ((60)Co source), in order to obtain a grafted polymer in which salicylic acid units were linked by means of labile ester bonds. The grafting percent depended on absorbed dose, reaction time, temperature and monomer concentration. The functionalized films were analyzed regarding structure (FTIR-ATR, SEM-EDX, fluorescence microscopy), temperature stability (TGA), interaction with aqueous medium (water contact angle and swelling), pH-responsive release and cytocompatibility (fibroblasts). In the obtained poly(2MBA)-grafted biomaterial, poly(2MBA) behaved as a polymeric prodrug that regulates salicylic acid release once in contact with aqueous medium, showing pH-dependent release rate.