Longevity of bond strength of resin cements to root dentine after radiation therapy.

AIM: To evaluate the bond strength and adhesive interface between several resin cements and root dentine immediately and 6 months after radiotherapy. METHODOLOGY: Sixty maxillary canines were selected and randomly assigned to two groups (n = 30): one group was not irradiated and the other one was subjected to a cumulative radiation dose of 60 Gy. The teeth were sectioned to obtain roots 16 mm long and the canals were prepared with the Reciproc system (R50) and filled using a lateral condensation technique with an epoxy resin sealer. Each group was divided into three subgroups (n = 10) according to the resin cement used for fibreglass fibre post cementation: RelyX-U200, Panavia-F2.0 and RelyX ARC. The posts were cemented in accordance with the manufacturer's recommendations. Three 1-mm-thick dentine slices were then obtained from each root third. The first two slices in the crown-apex direction of each third were selected for the push-out test. The failure mode after debonding was determined with a stereo microscope. The third slice from each root third was selected for scanning electron microscopy (SEM) analyses to examine the resin cement-dentine interface with 100, 1000, 2000 and 4000× magnification. Bond strength data were analysed by anova and Tukey's test (α = 0.05). RESULTS: Significantly lower bond strength (P < 0.0001) was obtained after irradiation compared to nonirradiated teeth. RelyX-U200 cemented fibre posts had the higher bond strength (15.17 ± 5.89) compared with RelyX ARC (P < 0.001) and Panavia-F2.0 (P < 0.001). The evaluation after 6 months revealed lower bond strength values compared to the immediate values (P < 0.001) for irradiated and nonirradiated teeth. Cohesive failures occurred in the irradiated dentine. SEM revealed fractures, microfractures and fewer collagen fibres in irradiated root dentine. RelyX-U200 and Panavia-F2.0 were associated with a juxtaposed interface of the cement with the radicular dentine in irradiated and nonirradiated teeth, and for RelyX ARC, hybrid layer formation and tags were observed in both irradiated and nonirradiated teeth. CONCLUSION: Radiation was associated with a decrease in the push-out bond strength and with lower resin cement/root dentine interface adaptation. Self-adhesive resin cement was a better alternative for fibre post cementation in teeth subjected to radiation therapy. The bond strength decreased after 6 months.

Delayed photo-activation and addition of thio-urethane: Impact on polymerization kinetics and stress of dual-cured resin cements.

OBJECTIVE: 1) to determine the moment during the redox polymerization reaction of dual cure cements at which to photo-activate the material in order to reduce the polymerization stress, and 2) to evaluate possible synergistic effects between adding chain transfer agents and delayed photo-activation. METHODS: The two pastes of an experimental dual-cure material were mixed, and the polymerization kinetics of the redox phase was followed. The moment when the material reached its maximum rate of redox polymerization (MRRP) of cement was determined. The degree of conversion (DC) and maximum rates of polymerization (Rpmax) were assessed for materials where: the photoactivation immediately followed material mixing, at MRRP, 1min before and 1min after MRRP. Thio-urethane (TU) additives were synthesized and added to the cement (20% wt), which was then cured under the same conditions. The polymerization kinetics was evaluated for both cements photo-activated immediately or at MRRP, followed by measurements of polymerization stress, flexural strength (FS) and elastic modulus (EM). Knoop hardness was measured before and after ethanol storage. RESULTS: Photo-activating the cement at or after MRRP reduced the Rpmax and the polymerization stress. Addition of TU promoted additional and more significant reduction, while not affecting the Rpmax. Greater hardness loss was observed for cements with TU, but the final hardness was similar for all experimental conditions. Addition of TU slightly reduced the EM and did not affect the FS. CONCLUSION: Delayed photo-activation and addition of TU significantly reduce the polymerization stress of dual-cured cements.

The effect of time between handling and photoactivation on self-adhesive resin cement properties.

PURPOSE: To evaluate the degree of conversion, absorption, and solubility in water of self-adhesive resin cements subjected to different time intervals between material preparation and the photoactivation procedure. MATERIALS AND METHODS: Two dual self-adhesive resin cements were tested: RelyX Unicem and SmartCem2. The degree of conversion as a function of time was evaluated by Fourier-transformed infrared spectroscopy using the attenuated total reflectance technique. Three time intervals between handling and photoactivation were applied: Group 1 = immediately; Group 2 = a 1-minute interval; Group 3 = a 4-minute interval. All specimens were irradiated with a light-emitting diode source for 40 seconds. Thirty discs of each cement (1 mm thick × 6 mm diameter, n = 10) were prepared for the absorption and solubility tests. These specimens were stored in distilled water at 37°C for 90 days. The results were subjected to ANOVA with two factors (material and activation time intervals) and Tukey's test (95% significance). RESULTS: The 4-minute interval significantly reduced the degree of conversion of SmartCem2 (30.6% ± 8.3%). No other significant changes were observed for the degree of conversion; however, the time intervals before photoactivation interfered significantly in the water absorption of the RelyX Unicem specimens but not the SmartCem2 specimens. The time intervals did not affect the solubility of either cement. In all cases, SmartCem2 had higher solubility than RelyX Unicem. CONCLUSION: The time interval between handling and photoactivation significantly influenced the degree of conversion and water sorption of the resin-based cements. In general, one can say that the self-adhesive resin cements should be photoactivated as soon as possible after the material handling process.

Effect of curing unit and adhesive system on marginal adaptation of composite restorations.

This study sought to evaluate how a curing unit and adhesive system affected the marginal adaptation of resin composite restorations. Class V cavities were prepared in bovine teeth with a gingival margin in dentin and an incisal margin in enamel. The cavities were restored with a micro-hybrid resin composite using one of four adhesives: Single Bond 2, Prime & Bond NT, Clearfil SE Bond, Xeno IV. The light-activations were performed using a quartz-tungsten-halogen (QTH) lamp or a second-generation light-emitting diode (LED). Restorations were finished and polished and epoxy replicas were prepared. Marginal adaptation was analyzed by using scanning electronic microscopy (magnification 500X). The widest gaps in each margin were recorded, and data were submitted to Kruskal-Wallis, Mann-Whitney, and Wilcoxon tests (α = 0.05). Differences between the adhesives were observed only when the dentin margins were evaluated: Clearfil SE Bond demonstrated better marginal adaptation than Prime & Bond NT or Single Bond 2 (which demonstrated the widest gaps in the dentin margin). The type of curing unit only affected the results for Xeno IV when the enamel margin was analyzed; the LED lamp promoted smaller gaps than the QTH lamp.

Effect of immediate and delayed light activation on the mechanical properties and degree of conversion in dual-cured resin cements.

We evaluated the effect of activation mode (immediate or delayed light activation vs. no light activation) on diametral tensile strength (DTS), elastic modulus, ultimate tensile strength (UTS), and degree of conversion (DC) in dual-cured resin cements. Three resin cements were evaluated: Enforce, RelyX ARC, and Panavia F. The mixed cements were inserted into circular molds for the DTS test and into dumbbell-shaped molds for the UTS test. Inside the molds, the cements were light-activated either immediately or after 5 min (delayed light activation). If no light activation was performed, the materials were protected from light exposure (control). The DTS and UTS tests were performed until fracture. The elastic modulus was calculated using data from the DTS test, and DC was evaluated 24 h after manipulation using near-infrared spectroscopy. Data for each variable were individually analyzed by two-way ANOVA and the post-hoc Tukey test (α = 0.05). Regarding DTS, activation mode influenced only Panavia Fspecimens, which had the lowest DTS values in the absence of light activation. Activation mode did not influence the elastic modulus or UTS of any resin cement evaluated. Immediate light activation yielded higher DC values as compared with the absence of light activation.

Polymerization kinetics and reactivity of alternative initiators systems for use in light-activated dental resins.

OBJECTIVES: The purpose of this study was to evaluate the reactivity and polymerization kinetics behavior of a model dental adhesive resin with water-soluble initiator systems. METHODS: A monomer blend based on Bis-GMA, TEGDMA and HEMA was used as a model dental adhesive resin, which was polymerized using a thioxanthone type (QTX) as a photoinitiator. Binary and ternary photoinitiator systems were formulated using 1mol% of each initiator. The co-initiators used in this study were ethyl 4-dimethylaminobenzoate (EDAB), diphenyliodonium hexafluorophosphate (DPIHFP), 1,3-diethyl-2-thiobarbituric acid (BARB), p-toluenesulfinic acid and sodium salt hydrate (SULF). Absorption spectra of the initiators were measured using a UV-Vis spectrophotometer, and the photon absorption energy (PAE) was calculated. The binary system camphorquinone (CQ)/amine was used as a reference group (control). Twelve groups were tested in triplicate. Fourier-transform infrared spectroscopy (FTIR) was used to investigate the polymerization reaction during the photoactivation period to obtain the degree of conversion (DC) and maximum polymerization rate (R(p)(max)) profile of the model resin. RESULTS: In the analyzed absorption profiles, the absorption spectrum of QTX is almost entirely localized in the UV region, whereas that of CQ is in the visible range. With respect to binary systems, CQ+EDAB exhibited higher DC and R(p)(max) values. In formulations that contained ternary initiator systems, the group CQ+QTX+EDAB was the only one of the investigated experimental groups that exhibited an R(p)(max) value greater than that of CQ+EDAB. The groups QTX+EDAB+DPIHFP and QTX+DPIHFP+SULF exhibited values similar to those of CQ+EDAB with respect to the final DC; however, they also exhibited lower reactivity. SIGNIFICANCE: Water-soluble initiator systems should be considered as alternatives to the widely used CQ/amine system in dentin adhesive formulations.

Effect of immediate or delayed light activation on curing kinetics and shrinkage stress of dual-cure resin cements.

OBJECTIVES: This study evaluated the effect of light activation (absence, immediate, or delayed) on conversion kinetics and polymerization stress of three commercial dual-cured resin cements (Enforce, RelyX ARC, and Panavia F). METHODS: Degree of conversion (DC) was monitored for 30 minutes using real-time near­Fourier transform infrared spectroscopy. The cement was mixed, placed on the spectrometer sample holder, and light activated either immediately or after five minutes (delayed light activation). When no light activation was performed, the materials were protected from light exposure (control). DC was evaluated at five and 30 minutes postmixture. Maximum rates of polymerization (Rp(max)) were obtained from the first derivative of the DC vs time curve. Polymerization stress was monitored for 30 minutes in 1-mm-thick specimens inserted between two cylinders attached to a universal testing machine. Data were submitted to analysis of variance/Tukey tests (α=0.05). RESULTS: Immediate light activation promoted the highest DC at five minutes. At 30 minutes, only RelyX ARC did not present a significant difference in DC between activation modes. Enforce and Panavia F presented higher Rp(max) for immediate and delayed light-activation, respectively. RelyX ARC showed similar Rp(max) for all activation modes. The absence of light activation resulted in the lowest stress followed by delayed light activation, while immediate light activation led to the highest values. RelyX ARC showed higher stress than Enforce, while the stress of Panavia F was similar to that of the others. CONCLUSION: Delayed light activation reduced the polymerization stress of the resin cements tested without jeopardizing DC.

Effect of reduced exposure times on the cytotoxicity of resin luting cements cured by high-power led.

OBJECTIVE: Applications of resin luting agents and high-power light-emitting diodes (LED) light-curing units (LCUs) have increased considerably over the last few years. However, it is not clear whether the effect of reduced exposure time on cytotoxicity of such products have adequate biocompatibility to meet clinical success. This study aimed at assessing the effect of reduced curing time of five resin luting cements (RLCs) polymerized by high-power LED curing unit on the viability of a cell of L-929 fibroblast cells. MATERIAL AND METHODS: Disc-shaped samples were prepared in polytetrafluoroethylene moulds with cylindrical cavities. The samples were irradiated from the top through the ceramic discs and acetate strips using LED LCU for 20 s (50% of the manufacturer's recommended exposure time) and 40 s (100% exposure time). After curing, the samples were transferred into a culture medium for 24 h. The eluates were obtained and pipetted onto L-929 fibroblast cultures (3x10(4) per well) and incubated for evaluating after 24 h. Measurements were performed by dimethylthiazol diphenyltetrazolium assay. Statistical significance was determined by two-way ANOVA and two independent samples were compared by t-test. RESULTS: Results showed that eluates of most of the materials polymerized for 20 s (except Rely X Unicem and Illusion) reduced to a higher extent cell viability compared to samples of the same materials polymerized for 40 s. Illusion exhibited the least cytotoxicity for 20 s exposure time compared to the control (culture without samples) followed by Rely X Unicem and Rely X ARC (90.81%, 88.90%, and 83.11%, respectively). For Rely X ARC, Duolink and Lute-It 40 s exposure time was better (t=-1.262 p=0,276; t=-9.399 p=0.001; and t=-20.418 p<0.001, respectively). CONCLUSION: The results of this study suggest that reduction of curing time significantly enhances the cytotoxicity of the studied resin cement materials, therefore compromising their clinical performance.

Effect of reduced exposure times on the cytotoxicity of resin luting cements cured by high-power led

OBJECTIVE: Applications of resin luting agents and high-power light-emitting diodes (LED) light-curing units (LCUs) have increased considerably over the last few years. However, it is not clear whether the effect of reduced exposure time on cytotoxicity of such products have adequate biocompatibility to meet clinical success. This study aimed at assessing the effect of reduced curing time of five resin luting cements (RLCs) polymerized by high-power LED curing unit on the viability of a cell of L-929 fibroblast cells. MATERIAL AND METHODS: Disc-shaped samples were prepared in polytetrafluoroethylene moulds with cylindrical cavities. The samples were irradiated from the top through the ceramic discs and acetate strips using LED LCU for 20 s (50 percent of the manufacturer's recommended exposure time) and 40 s (100 percent exposure time). After curing, the samples were transferred into a culture medium for 24 h. The eluates were obtained and pipetted onto L-929 fibroblast cultures (3x10(4) per well) and incubated for evaluating after 24 h. Measurements were performed by dimethylthiazol diphenyltetrazolium assay. Statistical significance was determined by two-way ANOVA and two independent samples were compared by t-test. RESULTS: Results showed that eluates of most of the materials polymerized for 20 s (except Rely X Unicem and Illusion) reduced to a higher extent cell viability compared to samples of the same materials polymerized for 40 s. Illusion exhibited the least cytotoxicity for 20 s exposure time compared to the control (culture without samples) followed by Rely X Unicem and Rely X ARC (90.81 percent, 88.90 percent, and 83.11 percent, respectively). For Rely X ARC, Duolink and Lute-It 40 s exposure time was better (t=-1.262 p=0,276; t=-9.399 p=0.001; and t=-20.418 p<0.001, respectively). CONCLUSION: The results of this study suggest that reduction of curing time significantly enhances the cytotoxicity of the studied resin cement materials, therefore compromising their clinical performance.

Light-activation through indirect ceramic restorations: does the overexposure compensate for the attenuation in light intensity during resin cement polymerization?

OBJECTIVES: This study evaluated the effects of light exposure through simulated indirect ceramic restorations (SICR) on hardness (KHN) of dual-cured resin cements (RCs), immediately after light-activation and 24 h later. MATERIAL AND METHODS: Three dual-cured RCs were evaluated: Eco-Link (Ivoclar Vivadent), Rely X ARC (3M ESPE), and Panavia F (Kuraray Medical Inc.). The RCs were manipulated in accordance to the manufacturers' instructions and were placed into cylindrical acrylic matrixes (1-mm-thick and 4-mm diameter). The RC light-activation (Optilux 501; Demetron Kerr) was performed through a glass slide for 120 s (control group), or through 2-mm or 4-mm thick SICRs (IPS Empress II; Ivoclar Vivadent). The specimens were submitted to KHN analysis immediately and 24 h after light-activation. The data obtained at the 2 evaluation intervals were submitted to 2-way ANOVA repeated measures and post-hoc Tukey's test (pre-set alpha of 5%). RESULTS: Lower KHN was observed when light-activation was performed through SICRs for Eco-Link at all evaluation intervals and for Rely X ARC 24 h later. For Panavia F, no significant difference in KHN was observed between control and experimental groups, regardless of evaluation interval. Most groups exhibited higher KHN after 24 h than immediately after light-activation, with the exception of Rely X ARC light-activated through SICR, as no significant difference in KHN was found between evaluation intervals. CONCLUSIONS: Light overexposure did not compensate for light intensity attenuation due to the presence of SICR when Rely X and Eco-Link were used. Although hardness of such RCs increased over a 24-h interval, the RCs subjected to light overexposure did not reach the hardness values exhibited after direct light exposure.

Light-activation through indirect ceramic restorations: does the overexposure compensate for the attenuation in light intensity during resin cement polymerization?

OBJECTIVES: This study evaluated the effects of light exposure through simulated indirect ceramic restorations (SICR) on hardness (KHN) of dual-cured resin cements (RCs), immediately after light-activation and 24 h later. MATERIAL AND METHODS: Three dual-cured RCs were evaluated: Eco-Link (Ivoclar Vivadent), Rely X ARC (3M ESPE), and Panavia F (Kuraray Medical Inc.). The RCs were manipulated in accordance to the manufacturers' instructions and were placed into cylindrical acrylic matrixes (1-mm-thick and 4-mm diameter). The RC light-activation (Optilux 501; Demetron Kerr) was performed through a glass slide for 120 s (control group), or through 2-mm or 4-mm thick SICRs (IPS Empress II; Ivoclar Vivadent). The specimens were submitted to KHN analysis immediately and 24 h after light-activation. The data obtained at the 2 evaluation intervals were submitted to 2-way ANOVA repeated measures and post-hoc Tukey's test (pre-set alpha of 5 percent). RESULTS: Lower KHN was observed when light-activation was performed through SICRs for Eco-Link at all evaluation intervals and for Rely X ARC 24 h later. For Panavia F, no significant difference in KHN was observed between control and experimental groups, regardless of evaluation interval. Most groups exhibited higher KHN after 24 h than immediately after light-activation, with the exception of Rely X ARC light-activated through SICR, as no significant difference in KHN was found between evaluation intervals. CONCLUSIONS: Light overexposure did not compensate for light intensity attenuation due to the presence of SICR when Rely X and Eco-Link were used. Although hardness of such RCs increased over a 24-h interval, the RCs subjected to light overexposure did not reach the hardness values exhibited after direct light exposure.

Evaluation of the light energy transmission and bottom/top rate in silorane and methacrylate-based composites with different photoactivation protocols.

AIM: This study investigated the influence of different composite resin organic matrix (methacrylate - Filtek Z350 XT and silorane - Filtek P90) on light energy transmission through the composite and bottom/top rate. MATERIALS AND METHODS: A light-emitting diode (New Blue Phase), light-curing unit was used with different photoactivation protocols (high-continuous mode - HCM, 1400 mW/cm2 for 20 seconds; low-continuous mode - LCM , 700 mW/cm2 for 40 seconds; and soft-start mode - SSM, 140 mW/cm2 for 5s followed by 39 seconds for 700 mW/cm2). Twenty specimens were prepared for each composite. The light energy transmission through the composite was calculated (n=10). The bottom/top rate of the same specimen was calculated (n=10). The data were compared by Tukey's test in different tests (light energy transmission through the composite and bottom/top rate). RESULTS: The light energy transmission through the Filtek Z350 XT composite (HCM - 576 mW/cm2, LCM - 238 mW/cm2, SSM - 232 mW/cm2) did not show statistical difference when compared with Filtek P90 composite (HCM - 572 mW/cm2, LCM - 233 mW/cm2, SSM - 230 mW/cm2). The bottom/top rate of the Filtek Z350 XT composite (HCM - 88.98%, LCM - 90.94%, SSM - 89.92%) was statistically higher than that of the Filtek P90 composite (HCM-77.29%, LCM-77.51%, SSM- 77.79%). CONCLUSION: Light energy transmission through the composite was not influenced by the use of different dental composite restoratives. However, the bottom/top rate of the composites was influenced by the use of different dental composite restoratives. CLINICAL SIGNIFICANCE: Insufficiently polymerized composite resin may present a large number of problems. For this reason, dental composite resins should have the similar deep surface polymerization as the top surface in dental restorations.

Efficiency of light-emitting diode and halogen units in reducing residual monomers.

INTRODUCTION: In this in-vitro study, we aimed to compare the residual monomers in composites beneath brackets bonded to enamel, using a light-emitting diode (LED) or a halogen unit, and to compare the residual monomers in the central to the peripheral areas of the composite. METHODS: Twenty bovine teeth preserved in 0.1% thymol were used in this study. Ten teeth were used to standardize the thickness of the composite film, since different thicknesses would cause different absorbance of light. Brackets were bonded to 10 bovine incisors, with the halogen light (n = 5) and the LED (n = 5). The brackets were debonded, and the remaining composite on the enamel surface was sectioned in 2 regions: peripheral (0.8 mm) and central, resulting in 2 subgroups per group: central halogen (n = 5), peripheral halogen (n = 5), central LED (n = 5), and peripheral LED (n = 5). The spectrometric analysis in the infrared region was used to measure the free monomers with the attenuated total reflectance method. RESULTS: Normal distribution was tested by using the Kolmogorov-Smirnov test. Data were compared by 2-way analysis of variance (ANOVA) at P <0.05. The LED group showed fewer residual monomers than did the halogen group (P = 0.014). No differences were found among the regions (P = 0.354), and there were no interactions between light type and region (P = 0.368). CONCLUSIONS: LED leaves less residual monomer than does the halogen light, even with half of the irradiation time; there were no differences between the central and peripheral regions, and no interaction between light type and region.

A critical analysis of the degree of conversion of resin-based luting cements.

OBJECTIVE: This study analyzed the degree of conversion (DC%) of four resin-based cements (All Ceram, Enforce, Rely X ARC and Variolink II) activated by two modes (chemical and dual), and evaluated the decrease of DC% in the dual mode promoted by the interposition of a 2.0-mm-thick IPS Empress 2 disc. MATERIAL AND METHODS: In the chemical activation, the resin-based cements were prepared by mixing equal amounts of base and catalyst pastes. In the dual activation, after mixing, the cements were light-activated at 650 mW/cm² for 40 s. In a third group, the cements were light-activated through a 2.0-mm-thick IPS Empress 2 disc. The DC% was evaluated in a FT-IR spectrometer equipped with an attenuated total reflectance crystal (ATR). The data were analyzed by two-way ANOVA and Tukey's HSD test. RESULTS: For all resin-based cements, the DC% was significantly higher with dual activation, followed by dual activation through IPS Empress 2, and chemical activation (p<0.05). Irrespective of the activation mode, Rely X presented the highest DC% (p<0.05). Chemically activated Variolink and All Ceram showed the worst results (p<0.05). The DC% decreased significantly when activation was performed through a 2.0-mm-thick IPS Empress 2 disc (p<0.05). CONCLUSION: The results of the present study suggest that resin-based cements could present low DC% when the materials are dually activated through 2.0 mm of reinforced ceramic materials with translucency equal to or less than that of IPS-Empress 2.

Activation mode effects on the shear bond strength of dual-cured resin cements.

OBJECTIVES: This study evaluated the immediate (10-minute) and delayed (24-hour) bond strength of dual-cured resin cements that are light-activated either immediately or delayed (after five minutes) or chemically-activated only. MATERIALS AND METHODS: Three dual-cured resin cements were evaluated: RelyX ARC, Panavia F and Enforce. Cylinders of resin cement were built up over resin composite blocks following the manufacturers' instructions for each luting agent. The cements were mixed, inserted into the molds and light-activated either immediately or after five minutes (delayed light activation). When no light activation was performed, the materials were protected from light exposure until testing. Half of the samples were tested at 10 minutes; the remaining samples were stored at 100% relative humidity for 24 hours when they were then tested (n = 10). Data were submitted to three-way ANOVA and post-hoc Tukey's tests (alpha = 0.05). The failure mode was evaluated under SEM. RESULTS: RelyX ARC presented the highest values of shear bond strength, followed by Enforce. Panavia F showed the lowest values. Both immediate and delayed light activation caused the cements to present the highest means of shear bond strength. There was an improvement in bond strength after 24 hours of storage. CONCLUSIONS: RelyX ARC produced the highest bond strength, which was improved by light activation and storage for 24 hours.

A critical analysis of the degree of conversion of resin-based luting cements

OBJECTIVE: This study analyzed the degree of conversion (DC percent) of four resin-based cements (All Ceram, Enforce, Rely X ARC and Variolink II) activated by two modes (chemical and dual), and evaluated the decrease of DC percent in the dual mode promoted by the interposition of a 2.0-mm-thick IPS Empress 2 disc. MATERIAL AND METHODS: In the chemical activation, the resin-based cements were prepared by mixing equal amounts of base and catalyst pastes. In the dual activation, after mixing, the cements were light-activated at 650 mW/cm² for 40 s. In a third group, the cements were light-activated through a 2.0-mm-thick IPS Empress 2 disc. The DC percent was evaluated in a FT-IR spectrometer equipped with an attenuated total reflectance crystal (ATR). The data were analyzed by two-way ANOVA and Tukey's HSD test. RESULTS: For all resin-based cements, the DC percent was significantly higher with dual activation, followed by dual activation through IPS Empress 2, and chemical activation (p<0.05). Irrespective of the activation mode, Rely X presented the highest DC percent (p<0.05). Chemically activated Variolink and All Ceram showed the worst results (p<0.05). The DC percent decreased significantly when activation was performed through a 2.0-mm-thick IPS Empress 2 disc (p<0.05). CONCLUSION: The results of the present study suggest that resin-based cements could present low DC percent when the materials are dually activated through 2.0 mm of reinforced ceramic materials with translucency equal to or less than that of IPS-Empress 2.

Effect of different photo-initiators and light curing units on degree of conversion of composites.

The aim of this study was to evaluate: (i) the absorption of photo-initiators and emission spectra of light curing units (LCUs); and (ii) the degree of conversion (DC) of experimental composites formulated with different photo-initiators when activated by different LCUs. Blends of BisGMA, UDMA, BisEMA and TEGDMA with camphorquinone (CQ) and/ or 1-phenyl-1,2-propanedione (PPD) were prepared. Dimethylaminoethyl methacrylate (DMAEMA) was used as co-initiator. Each mixture was loaded with 65 wt% of silanated filler particles. One quartz-tungsten-halogen - QTH (XL 2500, 3M/ESPE) and two lightemitting diode (LED) LCUs (UltraBlue IS, DMC and UltraLume LED 5, Ultradent) were used for activation procedures. Irradiance (mW/cm²) was calculated by the ratio of the output power by the area of the tip, and spectral distribution with a spectrometer (USB 2000). The absorption curve of each photo-initiator was determined using a spectrophotometer (Varian Cary 5G). DC was assessed by Fourier transformed infrared spectroscopy. Data were submitted to two-way ANOVA and Tukey's test (5%). No significant difference was found for DC values when using LED LCUs regardless of the photo-initiator type. However, PPD showed significantly lower DC values than composites with CQ when irradiated with QTH. PPD produced DC values similar to those of CQ, but it was dependent on the LCU type.

Effect of different photo-initiators and light curing units on degree of conversion of composites

The aim of this study was to evaluate: (i) the absorption of photo-initiators and emission spectra of light curing units (LCUs); and (ii) the degree of conversion (DC) of experimental composites formulated with different photo-initiators when activated by different LCUs. Blends of BisGMA, UDMA, BisEMA and TEGDMA with camphorquinone (CQ) and/ or 1-phenyl-1,2-propanedione (PPD) were prepared. Dimethylaminoethyl methacrylate (DMAEMA) was used as co-initiator. Each mixture was loaded with 65 wt percent of silanated filler particles. One quartz-tungsten-halogen - QTH (XL 2500, 3M/ESPE) and two lightemitting diode (LED) LCUs (UltraBlue IS, DMC and UltraLume LED 5, Ultradent) were used for activation procedures. Irradiance (mW/cm²) was calculated by the ratio of the output power by the area of the tip, and spectral distribution with a spectrometer (USB 2000). The absorption curve of each photo-initiator was determined using a spectrophotometer (Varian Cary 5G). DC was assessed by Fourier transformed infrared spectroscopy. Data were submitted to two-way ANOVA and Tukey's test (5 percent). No significant difference was found for DC values when using LED LCUs regardless of the photo-initiator type. However, PPD showed significantly lower DC values than composites with CQ when irradiated with QTH. PPD produced DC values similar to those of CQ, but it was dependent on the LCU type.

Hardening of a dual-cure resin cement using QTH and LED curing units.

OBJECTIVE: This study evaluated the surface hardness of a resin cement (RelyX ARC) photoactivated through indirect composite resin (Cristobal) disks of different thicknesses using either a light-emitting diode (LED) or quartz tungsten halogen (QTH) light source. MATERIAL AND METHODS: Eighteen resin cement specimens were prepared and divided into 6 groups according to the type of curing unit and the thickness of resin disks interposed between the cement surface and light source. Three indentations (50 g for 15 s) were performed on the top and bottom surface of each specimen and a mean Vickers hardness number (VHN) was calculated for each specimen. The data were analyzed using two-way ANOVA and Tukey-Kramer test was used for post-hoc pairwise comparisons. RESULTS: Increased indirect resin disk thickness resulted in decreased mean VHN values. Mean VHN values for the top surfaces of the resin cement specimens ranged from 23.2 to 46.1 (QTH) and 32.3 to 41.7 (LED). The LED curing light source produced higher hardness values compared to the QTH light source for 2- and 3-mm-thick indirect resin disks. The differences were clinically, but not statistically significant. Increased indirect resin disk thickness also resulted in decreased mean VHN values for the bottom surfaces of the resin cement: 5.8 to 19.1 (QTH) and 7.5 to 32.0 (LED). For the bottom surfaces, a statistically significant interaction was also found between the type of curing light source and the indirect resin disk thickness. CONCLUSION: Mean surface hardness values of resin cement specimens decreased with the increase of indirect resin disk thickness. The LED curing light source generally produced higher surface hardness values.

Hardening of a dual-cure resin cement using QTH and LED curing units

OBJECTIVE: This study evaluated the surface hardness of a resin cement (RelyX ARC) photoactivated through indirect composite resin (Cristobal) disks of different thicknesses using either a light-emitting diode (LED) or quartz tungsten halogen (QTH) light source. MATERIAL AND METHODS: Eighteen resin cement specimens were prepared and divided into 6 groups according to the type of curing unit and the thickness of resin disks interposed between the cement surface and light source. Three indentations (50 g for 15 s) were performed on the top and bottom surface of each specimen and a mean Vickers hardness number (VHN) was calculated for each specimen. The data were analyzed using two-way ANOVA and Tukey-Kramer test was used for post-hoc pairwise comparisons. RESULTS: Increased indirect resin disk thickness resulted in decreased mean VHN values. Mean VHN values for the top surfaces of the resin cement specimens ranged from 23.2 to 46.1 (QTH) and 32.3 to 41.7 (LED). The LED curing light source produced higher hardness values compared to the QTH light source for 2- and 3-mm-thick indirect resin disks. The differences were clinically, but not statistically significant. Increased indirect resin disk thickness also resulted in decreased mean VHN values for the bottom surfaces of the resin cement: 5.8 to 19.1 (QTH) and 7.5 to 32.0 (LED). For the bottom surfaces, a statistically significant interaction was also found between the type of curing light source and the indirect resin disk thickness. CONCLUSION: Mean surface hardness values of resin cement specimens decreased with the increase of indirect resin disk thickness. The LED curing light source generally produced higher surface hardness values.