Repair Bond Strength to Hybrid CAD/CAM Materials after Silane Heat Treatment with Laser.

PURPOSE: This study investigated the effect of different surface treatments and the effect of silane heat treatment with laser on the shear bond strength (SBS) of a nanoceramic composite to repaired hybrid CAD/CAM blocks. MATERIALS AND METHODS: 60 hybrid CAD/CAM specimens (Cerasmart, GC) were prepared and randomly divided into six groups according to the different surface treatments (n = 10): group ER: Er:YAG laser+silane (Monobond Plus, Ivoclar Vivadent); group ER+SHT: Er:YAG laser+silane heat treatment; group B: bur+silane; group B+SHT: bur+silane heat treatment; group HF: hydrofluoric acid+silane; group HF+SHT: hydrofluoric acid+silane heat treatment. Afterwards, a universal adhesive (Universal Bond Quick, Kuraray) was applied, and nanoceramic resin composite (Zenit, President) cylinders were bonded to the Cerasmart specimens. They were thermocycled for 10,000 cycles (5-55°C) and subjected to SBS testing using a universal testing machine. Failure modes were examined with a stereomicroscope (15X). Scanning electron microscopy (SEM) was used to evaluate the surface topography (n = 2). The data were statistically analyzed using the Mann-Whitney U-test and the Kruskal-Wallis test (p < 0.05). RESULTS: Regarding the surface treatments, group ER showed significantly lower SBS than groups B and HF (p < 0.05). Regarding the presence of silane heat treatment by laser, groups ER+SHT and B+SHT showed significantly lower SBS than group HF+SHT(p < 0.05). In addition, group B+SHT showed significantly lower SBS than did group B (p < 0.05). CONCLUSION: Er:YAG laser treatment for repairing hybrid CAD/CAM blocks was not as effective as bur roughening or hydrofluoric acid etching. Silane heated by Er:YAG laser was incapable of significantly increasing the bond strength to repaired hybrid CAD/CAM blocks.

Effect of Er:YAG Laser Etching on the Shear Bond Strength and Microleakage of Self-Glazed Zirconia Ceramics.

Objective: To investigate the effect of Er:YAG laser irradiation on the shear bond strength (SBS) and microleakage of self-glazed zirconia (SZ) ceramics. Background: SZ is a novel type ceramic; laser irradiation has started to be used in the surface treatment of different ceramics, while SZ has been rarely studied to improve the bond quality. Methods: One hundred twenty blocks (5 mm × 5 mm × 5 mm) of SZ ceramics were produced and split into eight groups following different surface treatments (n = 15): Group A: no treatment; Group B: standard grid processing; and Group C-H: different Er:YAG laser power settings (100, 200, 300, 400, 500, and 600 mJ). Ten blocks of each group received the measurement of SBS and fracture mode analysis, three blocks underwent the evaluation of the microleakage depths, and the other two blocks were observed under the scanning electronic microscopy (SEM). Results: Group F obtained the highest SBS and the lowest microleakage depth without damaging the ceramic surface structure, which was statistically significant compared with the control group and gridding group (p < 0.05), whereas the difference was not statistically significant (p > 0.05) between group E and group F. The results of bonding performance were consistent with failure types and observation of surface characterizations in SEM images. Conclusions: According to the results here, Er:YAG irradiation had effect on surface treatment. In addition, 400 mJ Er:YAG could increase the SBS and decrease the microleakage depth on SZ ceramics without damaging the surface structure.

Radiotherapy impairs adhesive bonding in permanent teeth.

OBJECTIVES: To evaluate the in vitro effects of radiotherapy (RT) on the morphological surface of the enamel and dentin and to determine the best adhesive system and most appropriate time to restore teeth in head and neck cancer patients. METHODS: Sixty third molars were cut into 120 enamel fragments and 120 dentin fragments and divided into four groups (n = 30): G1 (control): nonirradiated, only restorative procedure; G2: restorative procedure immediately before RT; G3: restorative procedure immediately after RT; and G4: restorative procedure 6 months after RT. Each group was divided into two subgroups: Adper™ Single Bond 2 (SB) and Clearfill SE Bond (CL) based on the material used. After RT and restorative procedures, the specimens were subjected to confocal microscopy and shear bond strength test. Data were analyzed using a two-way ANOVA followed by Tukey's test at a significance level of 5%. RESULTS: Morphological changes were observed in both substrates after a cumulative dose of 40 Gy, and after 60 Gy, the changes were more evident in both substrates. CL had the highest strength values in both substrates (p < 0.05), and G2 had the lowest strength values for the enamel and dentin (p < 0.05). CONCLUSIONS: Based on the in vitro study results, we can conclude that RT substantially changes the morphological surface of enamel and dentin and impairs the bond strength. The Clearfill system yielded better results than Adper Single Bond 2, and restoring teeth before RT resulted in the worst results in both substrates.

Effect of Different Laser Treatments on the Bond Strength of Intracanal Fiber Posts Cemented with a Self-Adhesive Resin Cement.

PURPOSE: To evaluate the influence of laser-activated irrigation by Er:YAG and Er:YSGG (LAI) protocols and Nd:YAG laser irradiation on the bond strength of self-adhesively cemented fiber posts to root canal dentine. MATERIALS AND METHODS: The study sample consisted of 84 human single-rooted permanent teeth instrumented with ProTaper Next technique. After obturation, post space preparations were created for fiber-reinforced composite posts. The prepared specimens were divided according to the laser treatment of the post space preparations: group 1: LAI (Er:YAG) + saline solution (pulse energy: 20 mJ, repetition rate: 15 Hz); group 2: LAI (Er:YAG) + QMiX solution (pulse energy: 20 mJ, repetition rate: 15 Hz); group 3: LAI (Er,Cr:YSGG) + saline solution (pulse energy: 62.5 mJ, 20 Hz); group 4: LAI (Er,Cr:YSGG) + QMiX (pulse energy: 62.5 mJ, 20 Hz); Nd:YAG laser (pulse energy: 100 mJ, 10 Hz). Fiber-reinforced posts were cemented with a self-adhesive cement. The bond strength was evaluated by the push-out bond strength test, and the mode of failure was determined under a stereomicroscope. Kruskal-Wallis test was used for the intergroup comparative analysis with 5% level of significance. RESULTS: The highest bond strength was recorded in the Er:YAG + QMiX group (mean 3.401 MPa) (p < 0.05), followed by the Er,Cr:YSGG and the Er:YAG + saline solution (mean 1.111 MPa and 1.094 MPa, respectively), which did not differ significantly (p = 0.232). The irradiation with the Nd:YAG laser caused similar bond strength as the Er,Cr:YSGG + QMiX (p = 0.942). CONCLUSION: All laser protocols enhanced the bond strength of the self-adhesive cement in root canals compared to only saline irrigation. The bond strength of the self-adhesive cement depended on the laser parameters and irrigant used for the LAI.

Evaluation of Intra Root Canal Er,Cr:YSGG Laser Irradiation on Prosthetic Post Adherence.

PURPOSE: In clinical prosthetics procedures, including endodontics and post fixation, the presence of a smear layer can reduce the post bond strength. An Er,Cr:YSGG laser, which emits at 2780 nm, can promote a smear-layer-free surface due to the ablation process. Considering these aspects, the purpose of this work was to evaluate the influence of Er,Cr:YSGG laser irradiation using either a radial or an axial fiber tip on the bond strength of three resin cements to the fiber-reinforced composite posts. MATERIALS AND METHODS: Ninety recently extracted single rooted human teeth had their root canal instrumented and were randomly distributed into nine experimental groups, in which three resin cements (total-etching Variolink II, self-etching Panavia F, and self-adhesive RelyX Unicem Aplicap) and three root canal treatments (no treatment, laser irradiation using the radial fiber tip, laser irradiation using the axial fiber tip) were used. Specimens were then sectioned into three sections (cervical, middle, and apical thirds) with two slices on each section. A push-out test was performed on each slice, and the values were recorded as MPa. The push-out data were analyzed by a Ryan-Joiner normality test followed by a two-way ANOVA test and Tukey pairwise comparison. The statistical analysis was performed on each third section separately, with a 5% significance level. RESULTS: Laser irradiation with axial fiber tip significantly increased the post bond strength of RelyX Unicem Aplicap on middle third of specimens (p < 0.001) when compared to other root canal treatments (unlased or irradiated with radial tip). Considering the Panavia resin cement, laser irradiation with either axial or radial tips promoted a significant increase on the post bond strength of middle third when compared to unlased specimens (p < 0.001); however, laser irradiation did not influence the post bond strength of Variolink resin cement. CONCLUSIONS: The use of the Er,Cr:YSGG laser for clinical prosthetics procedures enhances the post bond strength of Panavia and RelyX Unicem Aplicap resin cements, mainly at middle third of roots, and does not interfere with the bond strength of Variolink resin cement. For the RelyX Unicem Aplicap system, the use of axial tip is most advantageous and can be recommended for future clinical application.

Effect of diode laser irradiation on the bond strength of polymerized non-simplified adhesive systems after 12 months of water storage

Abstract Objectives: The aim of this in vitro study was to evaluate the bonding strength of non-simplified dentin bonding systems (DBS) to dentin irradiated with a diode laser (970 nm) immediately and after 12 months of water storage following either primer or bond application. Material and methods: The experimental design included three different factors: DBS type [AdperTM Scotchbond Multipurpose (MP) and Clearfil™ SE Bond (CSE)], irradiation [without irradiation - control (C), irradiation after primer application (AP), and irradiation after bond application (AB)], and time [initial (I) and after 12 months of water storage (12 m)]. Sixty sound human third molars (n = 10) were obtained, and their flat occlusal dentin areas were prepared and standardized. Laser irradiation was performed in the contact mode perpendicular to the dental surface over an automatically selected scanning area at a pulse energy of 0.8 W, frequency of 10 Hz, and energy density of 66.67 J/cm2. After 7 days of treatment, the specimens were cut, and half of them were subjected to microtensile testing (500 N/0.05 mm/min), whereas the remaining sticks were examined after 12 months of water storage. The obtained data were analyzed by three-way analysis of variance (ANOVA) followed by a Tukey test (p<0.05). The observed fracture modes were investigated using a portable digital microscope with a magnification of 40x. Results: Among the utilized DBS, MP generally exhibited higher bond strengths, but did not always differ from CSE under similar conditions. The irradiation factor was statistically significant only for the MP/AB groups. After 12 months of storage, all groups demonstrated a significant reduction in the bond strength, whereas the results of fracture analysis showed a predominance of the adhesive type. Conclusions: The laser treatment of non-simplified DBS was not able to stabilize their bonding characteristics after 12 months.

Effect of diode laser irradiation on the bond strength of polymerized non-simplified adhesive systems after 12 months of water storage.

OBJECTIVES: The aim of this in vitro study was to evaluate the bonding strength of non-simplified dentin bonding systems (DBS) to dentin irradiated with a diode laser (970 nm) immediately and after 12 months of water storage following either primer or bond application. MATERIAL AND METHODS: The experimental design included three different factors: DBS type [AdperTM Scotchbond Multipurpose (MP) and Clearfil™ SE Bond (CSE)], irradiation [without irradiation - control (C), irradiation after primer application (AP), and irradiation after bond application (AB)], and time [initial (I) and after 12 months of water storage (12 m)]. Sixty sound human third molars (n = 10) were obtained, and their flat occlusal dentin areas were prepared and standardized. Laser irradiation was performed in the contact mode perpendicular to the dental surface over an automatically selected scanning area at a pulse energy of 0.8 W, frequency of 10 Hz, and energy density of 66.67 J/cm2. After 7 days of treatment, the specimens were cut, and half of them were subjected to microtensile testing (500 N/0.05 mm/min), whereas the remaining sticks were examined after 12 months of water storage. The obtained data were analyzed by three-way analysis of variance (ANOVA) followed by a Tukey test (p<0.05). The observed fracture modes were investigated using a portable digital microscope with a magnification of 40x. RESULTS: Among the utilized DBS, MP generally exhibited higher bond strengths, but did not always differ from CSE under similar conditions. The irradiation factor was statistically significant only for the MP/AB groups. After 12 months of storage, all groups demonstrated a significant reduction in the bond strength, whereas the results of fracture analysis showed a predominance of the adhesive type. CONCLUSIONS: The laser treatment of non-simplified DBS was not able to stabilize their bonding characteristics after 12 months.

Light curing resin cements containing iodonium salts promote suitable apical bonding of posts to radicular dentin.

The aim of this study was to analyze the efficiency of experimental light-curing resin cements (ERCs) with a ternary photo-initiator system containing diphenyliodonium hexafluorphosphate (DPI) and different amines on retention of glass-fiber posts to dentin (GFP). ERCs formulations: a 1:1 mass ratio of 2,2-bis[4-(2-hydroxy-3-methacryloxypropoxy)phenylpropane and triethyleneglycol dimethacrylate. Camphorquinone was used as initiator. Six experimental groups were established according to the amine used: [ethyl-4-(dimethylamino)benzoate-EDMAB or 2-(dimethylamino)ethyl methacrylate-DMAEMA] and the concentration of DPI (0, 0.5 mol%, 1 mol%). The resin cements Variolink II (dual- and light-cured versions) were used as commercial reference. Eighty recently extracted bovine incisors (n = 10) were selected for this study. The roots were prepared and the fiber posts were cemented with the resin cement specified for each experimental group. Specimens from coronal, middle, and apical thirds of the root were subjected to push-out bond strength test 24 hours after bonding. Data were subjected to split-plot ANOVA and the Tukey test (p = 0.05). ERCs containing DPI showed statistically significant higher bond strengths compared with ERCs without DPI. ERCs containing DPI were statistically similar to VARIOLINK II - dual-cured and superior to VARIOLINK II - light-cured (except for EDMAB - 1DPI in the medium third and DMAEMA - 1DPI in the coronal third). Different amines did not influence post retention. The apical root region showed the lowest bond strength for the groups EDAB-0DPI, DMAEMA-0DPI and VARIOLINK II light-cured. Light-cured ERCs containing DPI were efficient for GFP retention to radicular dentin, with similar behaviour to that of dual-curing commercial resin cement.

Longevity of bond strength of resin cements to root dentine after radiation therapy.

AIM: To evaluate the bond strength and adhesive interface between several resin cements and root dentine immediately and 6 months after radiotherapy. METHODOLOGY: Sixty maxillary canines were selected and randomly assigned to two groups (n = 30): one group was not irradiated and the other one was subjected to a cumulative radiation dose of 60 Gy. The teeth were sectioned to obtain roots 16 mm long and the canals were prepared with the Reciproc system (R50) and filled using a lateral condensation technique with an epoxy resin sealer. Each group was divided into three subgroups (n = 10) according to the resin cement used for fibreglass fibre post cementation: RelyX-U200, Panavia-F2.0 and RelyX ARC. The posts were cemented in accordance with the manufacturer's recommendations. Three 1-mm-thick dentine slices were then obtained from each root third. The first two slices in the crown-apex direction of each third were selected for the push-out test. The failure mode after debonding was determined with a stereo microscope. The third slice from each root third was selected for scanning electron microscopy (SEM) analyses to examine the resin cement-dentine interface with 100, 1000, 2000 and 4000× magnification. Bond strength data were analysed by anova and Tukey's test (α = 0.05). RESULTS: Significantly lower bond strength (P < 0.0001) was obtained after irradiation compared to nonirradiated teeth. RelyX-U200 cemented fibre posts had the higher bond strength (15.17 ± 5.89) compared with RelyX ARC (P < 0.001) and Panavia-F2.0 (P < 0.001). The evaluation after 6 months revealed lower bond strength values compared to the immediate values (P < 0.001) for irradiated and nonirradiated teeth. Cohesive failures occurred in the irradiated dentine. SEM revealed fractures, microfractures and fewer collagen fibres in irradiated root dentine. RelyX-U200 and Panavia-F2.0 were associated with a juxtaposed interface of the cement with the radicular dentine in irradiated and nonirradiated teeth, and for RelyX ARC, hybrid layer formation and tags were observed in both irradiated and nonirradiated teeth. CONCLUSION: Radiation was associated with a decrease in the push-out bond strength and with lower resin cement/root dentine interface adaptation. Self-adhesive resin cement was a better alternative for fibre post cementation in teeth subjected to radiation therapy. The bond strength decreased after 6 months.

Effect of light irradiation and primer application on polymerization of selfadhesive resin cements monitored by ultrasonic velocity.

In this study, we investigated the effect of light irradiation and primer/adhesive application on the polymerization reaction and elastic modulus (E) of self-adhesive resin cement (SAC) through ultrasonic velocity (V) measurements. The V values of longitudinal and shear waves were determined based on the transit time through the specimens and specimen thicknesses, and were used to calculate the E values. Analysis of variance and Tukey tests revealed that V increased rapidly, reaching a plateau at 2,700-2,900 m/s, when the SACs were light-irradiated. However, the increasing rate of V was retarded for the non-irradiated SACs. In addition, when the primer/adhesive was applied, higher E values were obtained after 24 h. Finally, the polymerization behavior of the SACs was affected by light irradiation and primer application, and the use of prime/adhesive might improve mechanical properties. In clinical situations, use of primer/adhesive is recommended for getting proper adhesion.

Delayed Light Activation Improves Color Stability of Dual-Cured Resin Cements.

PURPOSE: To evaluate the color change caused by post-irradiation conversion (ΔE24h and ΔE8 days ) and artificial aging (ΔEAGING ) of resin cements light activated through ceramics of different opacities immediately and 6 minutes after manipulating the material. MATERIALS AND METHODS: Resin cement disks (Allcem and LuxaCore) were light activated through ceramics (without ceramic, e.max HT, LT, and MO) immediately and 6 minutes after the manipulation (n = 10). Spectrophotometry was used to evaluate ΔE24h and ΔE8 days after 37˚C-dry-dark-storage for 24 hours and 8 days, and ΔEAGING after 60˚C-water-storage for 24 hours. Data were analyzed with three-way ANOVA and Tukey's HSD (α = 0.05). RESULTS: Regarding the post-irradiation color change, significant differences were found between the cements (p < 0.0001), light activation protocols (p = 0.037), and ceramics (p < 0.001). The immediate activation (16.2 ± 0.1) showed lower ΔE values than the delayed activation (16.5 ± 0.1). Ceramics influenced the ΔE values as follows: MO (14.0 ± 1.2) < LT (14.9 ± 1.2) ≈ HT (15.4 ± 1.2) < control (21.2 ± 1.2). Regarding ΔEAGING , significant differences were found between cements (p < 0.001), light activation (p = 0.006), and ceramics (p < 0.001). The delayed activation (8.4 ± 0.1) showed lower values than the immediate activation (8.9 ± 0.1). Ceramic spacers influenced ΔEAGING as follows: control (5.6 ± 0.2) < MO (6.6 ± 0.2) < HT (11.0 ± 0.2) ≈ LT (11.5 ± 0.2). CONCLUSION: The delayed light activation resulted in increased color stability, while the ceramic interposition resulted in lower color stability.

Effect of Laser Etching on Glass Fiber Posts Cemented with Different Adhesive Systems.

BACKGROUND: Glass fiber-reinforced posts have been preferred frequently because of some physical properties similar to the dentin, chemically bonding to dentin, biocompatibility, and esthetics. OBJECTIVE: This study aimed to evaluate the microleakage and bond strength of glass fiber posts cemented with various adhesive systems on laser-etched root canal walls. METHODS: Roots of 120 human mandibular premolars were divided into two groups for push-out bond strength test and the microleakage test (n = 60). Erbium-doped yttrium-aluminum-garnet (Er:YAG) laser etching of the root canal walls was carried out on half of the specimens in both test groups. The laser-treated and laser-nontreated groups were divided again into three subgroups (n = 10). Glass fiber posts (everStick Post) were luted using three different resin cements: total-etch (Variolink N), self-etch (Panavia F 2.0), and self-adhesive (Rely X Unicem). Three dentin discs were obtained from each root, and the bond strength of the glass fiber posts was measured by push-out tests. The dye penetration method was used to investigate coronal microleakage. In addition, surface treatments and the bonding interfaces were observed using scanning electron microscope. RESULTS: The highest bond strengths were observed for the total-etch and self-adhesive resin cement groups with laser etching (p < 0.05), and the lowest bond strength was obtained for the self-etch resin cement group (p < 0.05). There were no statistically significant differences in terms of microleakage (p > 0.05), except for the self-adhesive resin cement group (p < 0.05). CONCLUSIONS: Er:YAG laser etching enhances the bonding strength of glass fiber posts. In addition, laser etching can reduce microleakage of self-adhesive resin cement.

Light curing resin cements containing iodonium salts promote suitable apical bonding of posts to radicular dentin

Abstract The aim of this study was to analyze the efficiency of experimental light-curing resin cements (ERCs) with a ternary photo-initiator system containing diphenyliodonium hexafluorphosphate (DPI) and different amines on retention of glass-fiber posts to dentin (GFP). ERCs formulations: a 1:1 mass ratio of 2,2-bis[4-(2-hydroxy-3-methacryloxypropoxy)phenylpropane and triethyleneglycol dimethacrylate. Camphorquinone was used as initiator. Six experimental groups were established according to the amine used: [ethyl-4-(dimethylamino)benzoate-EDMAB or 2-(dimethylamino)ethyl methacrylate-DMAEMA] and the concentration of DPI (0, 0.5 mol%, 1 mol%). The resin cements Variolink II (dual- and light-cured versions) were used as commercial reference. Eighty recently extracted bovine incisors (n = 10) were selected for this study. The roots were prepared and the fiber posts were cemented with the resin cement specified for each experimental group. Specimens from coronal, middle, and apical thirds of the root were subjected to push-out bond strength test 24 hours after bonding. Data were subjected to split-plot ANOVA and the Tukey test (p = 0.05). ERCs containing DPI showed statistically significant higher bond strengths compared with ERCs without DPI. ERCs containing DPI were statistically similar to VARIOLINK II - dual-cured and superior to VARIOLINK II - light-cured (except for EDMAB - 1DPI in the medium third and DMAEMA - 1DPI in the coronal third). Different amines did not influence post retention. The apical root region showed the lowest bond strength for the groups EDAB-0DPI, DMAEMA-0DPI and VARIOLINK II light-cured. Light-cured ERCs containing DPI were efficient for GFP retention to radicular dentin, with similar behaviour to that of dual-curing commercial resin cement.

Comparing depth-dependent curing radiant exposure and time of curing of regular and flow bulk-fill composites.

The effect of restoration depth on the curing time of a conventional and two bulk-fill composite resins by measuring microhardness and the respective radiosity of the bottom surface of the specimen was investigated. 1-, 3- and 5-mm thick washers were filled with Surefil SDR Flow-U (SDR), Tetric EvoCeram Bulk Fill-IVA (TEC) or Esthet-X HD-B1 (EHD), and cured with Bluephase® G2 for 40s. Additional 1-mm washers were filled with SDR, TEC or EHD, placed above the light sensor of MARC®, stacked with pre-cured 1-, 3- or 5-mm washer of respective material, and cured for 2.5~60s to mimic 2-, 4- and 6-mm thick composite curing. The sensor measured the radiosity (EB) at the bottom of specimen stacks. Vickers hardness (VH) was measured immediately at 5 locations with triplicate specimens. Nonlinear regression of VH vs EB by VH=α[1-exp(-EB/ß)] with all thickness shows that the values of α, maximum hardness, are 21.6±1.0 kg/mm2 for SDR, 38.3±0.6 kg/mm2 for TEC and 45.3±2.6 kg/mm2 for EHD, and the values of ß, rate parameter, are 0.40±0.06 J/cm2 for SDR, 0.77±0.04 J/cm2 for TEC and 0.58±0.09 J/cm2 for EHD. The radiosity of the bottom surface was calculated when the bottom surface of each material attained 80% of α of each material. The curing times for each material are in agreement with manufacturer recommendation for thickness. It is possible to estimate time needed to cure composite resin of known depth adequately by the radiosity and microhardness of the bottom surface.

Delayed photo-activation and addition of thio-urethane: Impact on polymerization kinetics and stress of dual-cured resin cements.

OBJECTIVE: 1) to determine the moment during the redox polymerization reaction of dual cure cements at which to photo-activate the material in order to reduce the polymerization stress, and 2) to evaluate possible synergistic effects between adding chain transfer agents and delayed photo-activation. METHODS: The two pastes of an experimental dual-cure material were mixed, and the polymerization kinetics of the redox phase was followed. The moment when the material reached its maximum rate of redox polymerization (MRRP) of cement was determined. The degree of conversion (DC) and maximum rates of polymerization (Rpmax) were assessed for materials where: the photoactivation immediately followed material mixing, at MRRP, 1min before and 1min after MRRP. Thio-urethane (TU) additives were synthesized and added to the cement (20% wt), which was then cured under the same conditions. The polymerization kinetics was evaluated for both cements photo-activated immediately or at MRRP, followed by measurements of polymerization stress, flexural strength (FS) and elastic modulus (EM). Knoop hardness was measured before and after ethanol storage. RESULTS: Photo-activating the cement at or after MRRP reduced the Rpmax and the polymerization stress. Addition of TU promoted additional and more significant reduction, while not affecting the Rpmax. Greater hardness loss was observed for cements with TU, but the final hardness was similar for all experimental conditions. Addition of TU slightly reduced the EM and did not affect the FS. CONCLUSION: Delayed photo-activation and addition of TU significantly reduce the polymerization stress of dual-cured cements.

Does the CO2 laser reduce bond strength in different types of ceramic brackets?

OBJECTIVE:: The aim of this study was to assess in vitro the influence of the CO2 laser and of the type of ceramic bracket on the shear bond strength (SBS) to enamel. METHODS:: A total of 60 enamel test surfaces were obtained from bovine incisors and randomly assigned to two groups, according to the ceramic bracket used: Allure (A); Transcend (T). Each group was divided into 2 subgroups (n = 15): L, laser (10W, 3s); C, no laser, or control. Twenty-four hours after the bonding protocol using Transbond XT, SBS was tested at a crosshead speed of 0.5 mm/min in a universal testing machine. After debonding, the Adhesive Remnant Index (ARI) was evaluated at 10 x magnification and compared among the groups. Data were analyzed by one-way ANOVA, Tukey's, Mann-Whitney's and Kruskal-Wallis tests (α = 0.05). RESULTS:: Mean SBS in MPa were: AL = 0.88 ± 0.84; AC = 12.22 ± 3.45; TL = 12.10 ± 5.11; TC = 17.71 ± 6.16. ARI analysis showed that 73% of the specimens presented the entire adhesive remaining on the tooth surfaces (score 3). TC group presented significantly higher SBS than the other groups. The lased specimens showed significantly lower bond strength than the non-lased groups for both tested brackets. CONCLUSION:: CO2 laser irradiation decreased SBS values of the polycrystalline ceramic brackets, mainly Allure.

Does the CO2 laser reduce bond strength in different types of ceramic brackets?

ABSTRACT OBJECTIVE: The aim of this study was to assess in vitro the influence of the CO2 laser and of the type of ceramic bracket on the shear bond strength (SBS) to enamel. METHODS: A total of 60 enamel test surfaces were obtained from bovine incisors and randomly assigned to two groups, according to the ceramic bracket used: Allure (A); Transcend (T). Each group was divided into 2 subgroups (n = 15): L, laser (10W, 3s); C, no laser, or control. Twenty-four hours after the bonding protocol using Transbond XT, SBS was tested at a crosshead speed of 0.5 mm/min in a universal testing machine. After debonding, the Adhesive Remnant Index (ARI) was evaluated at 10 x magnification and compared among the groups. Data were analyzed by one-way ANOVA, Tukey’s, Mann-Whitney’s and Kruskal-Wallis tests (α = 0.05). RESULTS: Mean SBS in MPa were: AL = 0.88 ± 0.84; AC = 12.22 ± 3.45; TL = 12.10 ± 5.11; TC = 17.71 ± 6.16. ARI analysis showed that 73% of the specimens presented the entire adhesive remaining on the tooth surfaces (score 3). TC group presented significantly higher SBS than the other groups. The lased specimens showed significantly lower bond strength than the non-lased groups for both tested brackets. CONCLUSION: CO2 laser irradiation decreased SBS values of the polycrystalline ceramic brackets, mainly Allure.

RESUMO OBJETIVO: o objetivo deste estudo foi avaliar in vitro a influência do laser de CO2 sobre a resistência ao cisalhamento da colagem (RCC) no esmalte dentário, usando diferentes tipos de braquetes cerâmicos. MÉTODOS: no total, 60 superfícies de esmalte de incisivos bovinos foram obtidas e aleatoriamente divididas em dois grupos, de acordo com o braquete cerâmico utilizado: Allure (A) e Transcend (T). Cada grupo foi dividido em dois subgrupos (n = 15): L, laser (10W, 3s); C, sem laser, ou controle. Vinte e quatro horas após a colagem dos braquetes com o sistema Transbond XT, foi realizado o teste de resistência ao cisalhamento, com velocidade de 0,5 mm/min, em máquina universal de ensaios mecânicos. Após a descolagem, o Índice de Remanescente de Adesivo (IRA) foi avaliado com aumento de 10X e comparado entre os grupos. Os dados foram analisados pelo ANOVA one-way, testes de Tukey’s, Mann-Whitney’s e Kruskal-Wallis (α = 0,05). RESULTADOS: as médias da RCC em MPa foram: AL = 0,88 ± 0,84; AC = 12,22 ± 3,45; TL = 12,10 ± 5,11; TC = 17,71 ± 6,16. A análise do IRA mostrou que 73% dos corpos de prova apresentaram todo o compósito remanescente aderido à superfície do esmalte (escore 3). O grupo TC apresentou valor significativamente maior de RCC do que os outros grupos. Os corpos de prova dos grupos com laser obtiveram valores adesivos significativamente menores do que os corpos de prova dos grupos sem laser, com ambos os tipos de braquetes. CONCLUSÃO: a irradiação com laser de CO2 diminuiu os valores de RCC dos braquetes policristalinos testados, principalmente do Allure.

Shear bond, wettability and AFM evaluations on CO2 laser-irradiated CAD/CAM ceramic surfaces.

The purpose of this study is to determine the CO2 laser irradiation in comparison with sandblasting (Sb), hydrofluoric acid (Hf) and silane coupling agent (Si) on shear bond strength (SBS), roughness (Rg) and wettability (Wt) of resin cement to CAD/CAM ceramics. Sixty (CAD/CAM) ceramic discs were prepared and distributed into six different groups: group A, control lithium disilicate (Li); group B, control zirconia (Zr); group C, Li: CO2/HF/Si; group D, Li: HF/Si; group E, Zr: CO2/Sb/Si; group F, Zr: Sb/Si. Result showed significant difference between irradiated and non-irradiated in terms of shear bond strength for zirconia ceramics (p value = 0.014). Moreover, partial surface wettability for irradiated and non-irradiated ceramics. Irradiated surface demonstrated more rough surface in lithium disilicate than zirconia ceramics. CO2 irradiation could increase shear bond strength, surface roughness and wettability for both CAD/CAM ceramics.

The effect of Er:YAG laser irradiation on the bond stability of self-etch adhesives at different dentin depths.

The aim of this study was to evaluate the effect of Er:YAG laser irradiation on the micro-shear bond strength of self-etch adhesives to the superficial dentin and the deep dentin before and after thermocycling. Superficial dentin and deep dentin surfaces were prepared by flattening of the occlusal surfaces of extracted human third molars. The deep or superficial dentin specimens were randomized into three groups according to the following surface treatments: group I (control group), group II (Er:YAG laser; 1.2 W), and group III (Er:YAG laser; 0.5 W). Clearfil SE Bond or Clearfil S3 Bond was applied to each group's dentin surfaces. After construction of the composite blocks on the dentin surface, the micro-shear bond testing of each adhesive was performed at 24 h or after 15,000 thermal cycles. The data were analyzed using a univariate analysis of variance and Tukey's test (p < 0.05). Laser irradiation in superficial dentin did not significantly affect bond strength after thermocycling (p > 0.05). However, deep-dentin specimens irradiated with laser showed significantly higher bond strengths than did control specimens after thermocycling (p < 0.05). Thermocycling led to significant deterioration in the bond strengths of all deep-dentin groups. The stable bond strength after thermocycling was measured for all of the superficial-dentin groups. No significant difference was found between the 0.5 and 1.2 W output power settings. In conclusion, the effect of laser irradiation on the bond strength of self-etch adhesives may be altered by the dentin depth. Regardless of the applied surface treatment, deep dentin showed significant bond degradation.

Light Transmission of Novel CAD/CAM Materials and Their Influence on the Degree of Conversion of a Dual-curing Resin Cement.

PURPOSE: To evaluate the light transmission characteristics of different types, shades, and thicknesses of novel CAD/CAM materials and their effect on the degree of conversion (DC) of a dual-curing resin cement. MATERIALS AND METHODS: Square specimens (12 × 12 mm2) of three CAD/CAM materials - GC Cerasmart, Lava Ultimate, Vita Enamic - of different thicknesses (1.00, 1.50, and 2.00 mm, n = 5 per thickness) were irradiated with an LED unit. The amount of transmitted light was quantified. Thereafter, the DC% of the dual-curing resin cement (RelyX Ultimate) was recorded after 15 min using Fourier transform infrared spectroscopy. Statistical analysis was performed using two-way ANOVA followed by the Tukey's HSD post-hoc test at a significance level of p < 0.05. Regression analysis was performed to investigate the correlation between the DC and radiant energy, and the DC and thickness. RESULTS: Although the type and shade of CAD/CAM material significantly affect transmitted light irradiation (p < 0.0001), degrees of conversion are similar when the CAD/CAM material or material shade were taken into consideration (p > 0.05). Conversely, material thickness significantly affected light transmission (p < 0.0001) and DC (p < 0.0001). Multiple effects of material, shade, and thickness did not significantly affect the evaluated parameters (p = 0.638 for light irradiation; p = 0.637 for DC). Linear regression analysis showed a correlation between delivered energy and DC% results of the Vita Enamic (R²â€¯= 0.4169, p < 0.0001). CONCLUSION: Reduced light transmission in 2-mm-thick specimens of all CAD/CAM materials indicates that proper curing of the cement beneath CAD/CAM materials should be ensured.