Correlation between mechanical properties and stabilization time of chemical bonds in glass-ionomer cements.

The objective was to evaluate the compressive strength (CS), diametral tensile strength (DTS), flexural strength (FS), and Knoop microhardness (KH) of different conventional restorative glass-ionomer cements (GICs) and to correlate these mechanical properties (MP) with the stabilization time (ST) of their chemical bonds. Eighteen GICs were tested: Bioglass [B], Chemfil Rock [CR], Equia Forte [EF], Gold Label 2 [GL2], Gold Label 9 [GL9], Glass Ionomer Cement II [GI], Ionglass [IG], Ion Z[ IZ], Ionomaster [IM], Ionofil Plus [IP], Ionostar Plus [IS], Ketac Molar Easymix [KM], Magic Glass [MG], Maxxion R [Ma], Riva Self Cure [R], Vidrion R [V], Vitro Fil [VF] and Vitro Molar [VM]. The mechanical strength tests were performed in a universal testing machine. KH readings were done with a diamond indenter. STs were examined by Fourier Transform Infrared spectroscopy (FTIR). Data were analyzed with ANOVA and Tukey test (p<0.05). The Spearman rank test was used to evaluate the dependence between the MPs and ST results. The highest MP values were EF, GL2, GL9, GI and KM and the lowest for MG, MA, B, VF and IM. The longest ST was for GL2 and the shortest was for B. ST correlated positively with MP. GICs with longer chemical bonds ST are generally stronger and the ST value obtained from FTIR was useful in predicting the strength of GICs tested.

Correlation between mechanical properties and stabilization time of chemical bonds in glass-ionomer cements

Abstract The objective was to evaluate the compressive strength (CS), diametral tensile strength (DTS), flexural strength (FS), and Knoop microhardness (KH) of different conventional restorative glass-ionomer cements (GICs) and to correlate these mechanical properties (MP) with the stabilization time (ST) of their chemical bonds. Eighteen GICs were tested: Bioglass [B], Chemfil Rock [CR], Equia Forte [EF], Gold Label 2 [GL2], Gold Label 9 [GL9], Glass Ionomer Cement II [GI], Ionglass [IG], Ion Z[ IZ], Ionomaster [IM], Ionofil Plus [IP], Ionostar Plus [IS], Ketac Molar Easymix [KM], Magic Glass [MG], Maxxion R [Ma], Riva Self Cure [R], Vidrion R [V], Vitro Fil [VF] and Vitro Molar [VM]. The mechanical strength tests were performed in a universal testing machine. KH readings were done with a diamond indenter. STs were examined by Fourier Transform Infrared spectroscopy (FTIR). Data were analyzed with ANOVA and Tukey test (p<0.05). The Spearman rank test was used to evaluate the dependence between the MPs and ST results. The highest MP values were EF, GL2, GL9, GI and KM and the lowest for MG, MA, B, VF and IM. The longest ST was for GL2 and the shortest was for B. ST correlated positively with MP. GICs with longer chemical bonds ST are generally stronger and the ST value obtained from FTIR was useful in predicting the strength of GICs tested.

Influence of activation mode, fatigue, and ceramic interposition on resin cements' diametral tensile strength.

This study evaluated the influence of activation modes, on Diametral Tensile Strength (DTS) of dual cured resin cements subjected to a Mechanical Fatigue test (MF). Four dual-cured resin cements (RelyX UNICEM [U], RelyX ARC [A], ENFORCE [E] and Nexus 2 [N]) were activated by three different curing modes as follows: Self-Curing (SC), Dual Cure activation with photoactivation executed directly (DC) and Dual Cure activation with Photoactivation Through Porcelain (DCTP). After 24 hours, half of the sample was subjected to 30.000 fatigue cycles at 1 Hz frequency and 12 N load. Then, all specimens were subjected to DTS test in Instron Universal Testing Machine and data were analyzed by three-way ANOVA and Tukey's Test (5%). The results of DTS test means (MPa) and standard deviation, for each cement factor activated by SC, DC and DCTP was respectively: U (28.12 ± 5.29; 37.44 ± 6.49 and 40.10 ± 4.39), A (49.68 ± 8.42; 55.12 ± 5.16 and 63.43 ± 6.92), E (49.12 ± 3.89; 56.42 ± 8.88 and 56.96 ± 6.45) and N (61.89 ± 11.21; 59.26 ± 9.47 and 62.56 ± 10.93). Turkey's test indicated that DC is related to the highest DTS values; Nexus 2 DTS remained the same independently of activation mode and that the Porcelain disk interposition enhanced DTS only for RelyX ARC the ANOVA statistical test indicated that MF didn't alter the DTS values for all experimental groups. MF results clinical implication is that all cements tested exhibited, in an immediate loading, good cross linked bonds quality.

Effect of ultrasonic and Nd: Yag laser activation on irrigants on the push-out bond strength of fiber post to the root canal.

OBJECTIVE: This in vitro study aimed to compare the efficacy of irrigants using various irrigation activation methods to the push-out bond strengths of fiber post to root canal luted with self-adhesive resin cement (SARC). METHODOLOGY: Forty-eight decoronated human canines were used. The specimens were divided into four groups corresponding with the post-space irrigation process and were treated as follows: distilled water (DW) (Control) group received 15 mL of DW; sodium hypochlorite (NaOCl)+ethylenediaminetetraacetic acid (EDTA) group was treated with 5 mL of 5.25% NaOCl, 5 mL of 17% EDTA, and 5 mL of DW; passive ultrasonic irrigation (PUI) group was treated with 5 mL of 5.25% NaOCl, 5 mL of 17% EDTA, and 5 mL of DW, and each irrigant was agitated with an ultrasonic file; and laser activated irrigation (LAI) group was treated with 5 mL of 5.25% NaOCl, 5 mL of 17% EDTA, and 5 mL of DW, and each irrigant was irradiated with Nd: YAG laser. Fiber posts were luted with SARC, and a push-out test was performed. Data was analyzed using one-way analysis of variance and Tukey HSD test. RESULTS: The bond strength values for the groups obtained were as follows: Control (10.04 MPa), NaOCl+EDTA (11.07 MPa), PUI (11.85 MPa), and LAI (11.63 MPa). No statistically significant differences were found among all experimental groups (p>0.05). The coronal (12.66 MPa) and middle (11.63 MPa) root regions indicated a significantly higher bond strength compared with the apical (9.16 MPa) region (p<0.05). CONCLUSIONS: Irrigant activation methods did not increase the bond strength of fiber post to canal.

Effect of Different Laser Treatments on the Bond Strength of Intracanal Fiber Posts Cemented with a Self-Adhesive Resin Cement.

PURPOSE: To evaluate the influence of laser-activated irrigation by Er:YAG and Er:YSGG (LAI) protocols and Nd:YAG laser irradiation on the bond strength of self-adhesively cemented fiber posts to root canal dentine. MATERIALS AND METHODS: The study sample consisted of 84 human single-rooted permanent teeth instrumented with ProTaper Next technique. After obturation, post space preparations were created for fiber-reinforced composite posts. The prepared specimens were divided according to the laser treatment of the post space preparations: group 1: LAI (Er:YAG) + saline solution (pulse energy: 20 mJ, repetition rate: 15 Hz); group 2: LAI (Er:YAG) + QMiX solution (pulse energy: 20 mJ, repetition rate: 15 Hz); group 3: LAI (Er,Cr:YSGG) + saline solution (pulse energy: 62.5 mJ, 20 Hz); group 4: LAI (Er,Cr:YSGG) + QMiX (pulse energy: 62.5 mJ, 20 Hz); Nd:YAG laser (pulse energy: 100 mJ, 10 Hz). Fiber-reinforced posts were cemented with a self-adhesive cement. The bond strength was evaluated by the push-out bond strength test, and the mode of failure was determined under a stereomicroscope. Kruskal-Wallis test was used for the intergroup comparative analysis with 5% level of significance. RESULTS: The highest bond strength was recorded in the Er:YAG + QMiX group (mean 3.401 MPa) (p < 0.05), followed by the Er,Cr:YSGG and the Er:YAG + saline solution (mean 1.111 MPa and 1.094 MPa, respectively), which did not differ significantly (p = 0.232). The irradiation with the Nd:YAG laser caused similar bond strength as the Er,Cr:YSGG + QMiX (p = 0.942). CONCLUSION: All laser protocols enhanced the bond strength of the self-adhesive cement in root canals compared to only saline irrigation. The bond strength of the self-adhesive cement depended on the laser parameters and irrigant used for the LAI.

Effect of ultrasonic and Nd: Yag laser activation on irrigants on the push-out bond strength of fiber post to the root canal

Abstract Objective: This in vitro study aimed to compare the efficacy of irrigants using various irrigation activation methods to the push-out bond strengths of fiber post to root canal luted with self-adhesive resin cement (SARC). Methodology: Forty-eight decoronated human canines were used. The specimens were divided into four groups corresponding with the post-space irrigation process and were treated as follows: distilled water (DW) (Control) group received 15 mL of DW; sodium hypochlorite (NaOCl)+ethylenediaminetetraacetic acid (EDTA) group was treated with 5 mL of 5.25% NaOCl, 5 mL of 17% EDTA, and 5 mL of DW; passive ultrasonic irrigation (PUI) group was treated with 5 mL of 5.25% NaOCl, 5 mL of 17% EDTA, and 5 mL of DW, and each irrigant was agitated with an ultrasonic file; and laser activated irrigation (LAI) group was treated with 5 mL of 5.25% NaOCl, 5 mL of 17% EDTA, and 5 mL of DW, and each irrigant was irradiated with Nd: YAG laser. Fiber posts were luted with SARC, and a push-out test was performed. Data was analyzed using one-way analysis of variance and Tukey HSD test. Results: The bond strength values for the groups obtained were as follows: Control (10.04 MPa), NaOCl+EDTA (11.07 MPa), PUI (11.85 MPa), and LAI (11.63 MPa). No statistically significant differences were found among all experimental groups (p>0.05). The coronal (12.66 MPa) and middle (11.63 MPa) root regions indicated a significantly higher bond strength compared with the apical (9.16 MPa) region (p<0.05). Conclusions: Irrigant activation methods did not increase the bond strength of fiber post to canal.

Influence of activation mode, fatigue, and ceramic interposition on resin cements' diametral tensile strength

Abstract This study evaluated the influence of activation modes, on Diametral Tensile Strength (DTS) of dual cured resin cements subjected to a Mechanical Fatigue test (MF). Four dual-cured resin cements (RelyX UNICEM [U], RelyX ARC [A], ENFORCE [E] and Nexus 2 [N]) were activated by three different curing modes as follows: Self-Curing (SC), Dual Cure activation with photoactivation executed directly (DC) and Dual Cure activation with Photoactivation Through Porcelain (DCTP). After 24 hours, half of the sample was subjected to 30.000 fatigue cycles at 1 Hz frequency and 12 N load. Then, all specimens were subjected to DTS test in Instron Universal Testing Machine and data were analyzed by three-way ANOVA and Tukey's Test (5%). The results of DTS test means (MPa) and standard deviation, for each cement factor activated by SC, DC and DCTP was respectively: U (28.12 ± 5.29; 37.44 ± 6.49 and 40.10 ± 4.39), A (49.68 ± 8.42; 55.12 ± 5.16 and 63.43 ± 6.92), E (49.12 ± 3.89; 56.42 ± 8.88 and 56.96 ± 6.45) and N (61.89 ± 11.21; 59.26 ± 9.47 and 62.56 ± 10.93). Turkey's test indicated that DC is related to the highest DTS values; Nexus 2 DTS remained the same independently of activation mode and that the Porcelain disk interposition enhanced DTS only for RelyX ARC the ANOVA statistical test indicated that MF didn't alter the DTS values for all experimental groups. MF results clinical implication is that all cements tested exhibited, in an immediate loading, good cross linked bonds quality.

Effect of different bonding protocols on degree of monomer conversion and bond strength between orthodontic brackets and enamel.

The objective of the present study was to evaluate the effect of different surface treatments and polymerization protocols on the bond strength of brackets to enamel, and the degree of conversion of the bonding agents. 120 bovine crowns were embedded in acrylic resin blocks and sanded. Next, the blocks were randomly assigned into 12 groups. Metal brackets were bonded to enamel according to the "surface treatment" factor (A: Phosphoric Acid; ATxt: Phosphoric Acid + Transbond XT Primer®; Tse: Transbond Plus Self Etching Primer®; and SBU: Scotchbond Universal®) and "polymerization" factor (R20: Radii-Cal®/20 seconds; V20: Valo Cordless®/20 seconds; and V3: Valo Cordless®/3 seconds). All samples were stored for 6 months (water, 37ºC) and then subjected to a shear bond strength test (SBS). Bond failures were classified according to the Adhesive Remnant Index (ARI) and analyzed with the Kruskal-Wallis and Mann-Whitney tests (5%). Using the same factors, 120 resin discs were made to assess the degree of conversion (DC) of the monomer. Data from the SBS (MPa) and DC (%) were analyzed by analysis of variance (2 factors) and Tukey's test (5%). For the SBS, the factors "polymerization" (R20 = 8.1B; V20 = 13.2A; V3 = 5.2C, p = 0.0001) and "surface treatment" (A = 3.1C; ATxt = 13.6A; Tse = 12.3A; SBU = 6.3B, p = 0.0001) were statistically significant among groups. The highest adhesion value were found for the ATxt/V20 group (22.2A) and the lowest value for the A/R20 group (1.2E). Regarding ARI, score 2 was the most prevalent in groups A, ATxt, V20 and V3, while score 4 was the most prevalent in the Tse, SBU and R20 groups, with no significant difference between them (p = 1.0). Regarding DC, the factors "polymerization" (R20 = 66.6A; V20 = 58.4B; V3 = 45.1C, p = 0.0001) and "surface treatment" (A = 52B, ATxt = 59.7A, Tse = 51.4B, SBU = 63.8A, p = 0.0001) were statistically significant. Tse was more sensitive to the variations in polymerization protocols than the other surface treatments. Treatment A did not present suitable bond strength or degree of conversion.

Alternativas de tratamientos de superficie para adhesión de cerámica de disilicado de litio / Alternatives of surface treatments for adhesion of lithium disilicate ceramics

Introduction: the clinical success of a restoration is strongly associated with the quality and durability of the ceramic-cement resin interface. In order to obtain an adequate union between these materials of different nature surface treatments are used and achieve mechanical retention or chemical interaction. Objectives: to check if any method promotes a true chemical bond between lithium disilicate ceramics and resin cement. As well as determineif there is any treatment that reports bonding values comparable to hydrofluoric acid and silane (gold standard). Methods: a systematic literature review was developed based on the PRISMA strategy, where the databases were searched: Science Direct, Pubmed (MEDLINE), EMBASE, Springer Journal, SciELO with MeSH and free terms from 2005 to November 2016 for articles in English and Spanish on surface treatments for lithium disilicate. Results: from 58 publications selected a sample of 21 articles. Two articles reported high risk of bias. Conclusions: hydrofluoric acid and silane continue to be the method with the highest and most reliable adhesion values in the literature. Universal adhesives are an alternative to promote chemical adhesion additional to the silane. Diamond burs, Nd: YAG and Er: YAG laser are not recommended as surface treatments(AU)

Introducción: el éxito clínico de una restauración se asocia fuertemente a la calidad y duración de la interface cerámica-cemento resinoso. Para que exista una adecuada unión entre estos materiales de distinta naturaleza se emplean tratamientos de superficie para lograr una buena retención mecánica o interacción química. Objetivos: revisar si algún método promueve una verdadera adhesión química entre la cerámica de disilicato de litio y el cemento resinoso, así como determinar si existe algún tratamiento que reporte valores de unión comparables al ácido fluorhídrico y silano (patrón de oro). Métodos: se desarrolló una revisión sistemática de literatura basada en la estrategia PRISMA, donde se buscó en las bases de datos: Science Direct, Pubmed (MEDLINE), EMBASE, Springer Journal, SciELO con términos MeSH y libres desde el 2005 a noviembre de 2016 para artículos en inglés y español sobre tratamientos de superficie para disilicato de litio. Resultados: de 58 publicaciones, se seleccionó una muestra de 21 artículos. Dos artículos reportaron riesgo de sesgo alto. Conclusiones: el ácido fluorhídrico y silano continúan siendo el método con los valores de adhesión más altos y confiables de la literatura. Los adhesivos universales son una alternativa para promover adhesión química adicional al silano. Fresas diamantadas, laser Nd: YAG y Er:YAG no se recomienda como tratamientos de superficie(AU)

Alternativas de tratamientos de superficie para adhesión de cerámica de disilicado de litio / Alternatives of surface treatments for adhesion of lithium disilicate ceramics

Introduction: the clinical success of a restoration is strongly associated with the quality and durability of the ceramic-cement resin interface. In order to obtain an adequate union between these materials of different nature surface treatments are used and achieve mechanical retention or chemical interaction. Objectives: to check if any method promotes a true chemical bond between lithium disilicate ceramics and resin cement. As well as determineif there is any treatment that reports bonding values comparable to hydrofluoric acid and silane (gold standard). Methods: a systematic literature review was developed based on the PRISMA strategy, where the databases were searched: Science Direct, Pubmed (MEDLINE), EMBASE, Springer Journal, SciELO with MeSH and free terms from 2005 to November 2016 for articles in English and Spanish on surface treatments for lithium disilicate. Results: from 58 publications selected a sample of 21 articles. Two articles reported high risk of bias. Conclusions: hydrofluoric acid and silane continue to be the method with the highest and most reliable adhesion values in the literature. Universal adhesives are an alternative to promote chemical adhesion additional to the silane. Diamond burs, Nd: YAG and Er: YAG laser are not recommended as surface treatments(AU)

Introducción: el éxito clínico de una restauración se asocia fuertemente a la calidad y duración de la interface cerámica-cemento resinoso. Para que exista una adecuada unión entre estos materiales de distinta naturaleza se emplean tratamientos de superficie para lograr una buena retención mecánica o interacción química. Objetivos: revisar si algún método promueve una verdadera adhesión química entre la cerámica de disilicato de litio y el cemento resinoso, así como determinar si existe algún tratamiento que reporte valores de unión comparables al ácido fluorhídrico y silano (patrón de oro). Métodos: se desarrolló una revisión sistemática de literatura basada en la estrategia PRISMA, donde se buscó en las bases de datos: Science Direct, Pubmed (MEDLINE), EMBASE, Springer Journal, SciELO con términos MeSH y libres desde el 2005 a noviembre de 2016 para artículos en inglés y español sobre tratamientos de superficie para disilicato de litio. Resultados: de 58 publicaciones, se seleccionó una muestra de 21 artículos. Dos artículos reportaron riesgo de sesgo alto. Conclusiones: el ácido fluorhídrico y silano continúan siendo el método con los valores de adhesión más altos y confiables de la literatura. Los adhesivos universales son una alternativa para promover adhesión química adicional al silano. Fresas diamantadas, laser Nd: YAG y Er:YAG no se recomienda como tratamientos de superficie(AU)

Effect of different bonding protocols on degree of monomer conversion and bond strength between orthodontic brackets and enamel

Abstract The objective of the present study was to evaluate the effect of different surface treatments and polymerization protocols on the bond strength of brackets to enamel, and the degree of conversion of the bonding agents. 120 bovine crowns were embedded in acrylic resin blocks and sanded. Next, the blocks were randomly assigned into 12 groups. Metal brackets were bonded to enamel according to the "surface treatment" factor (A: Phosphoric Acid; ATxt: Phosphoric Acid + Transbond XT Primer®; Tse: Transbond Plus Self Etching Primer®; and SBU: Scotchbond Universal®) and "polymerization" factor (R20: Radii-Cal®/20 seconds; V20: Valo Cordless®/20 seconds; and V3: Valo Cordless®/3 seconds). All samples were stored for 6 months (water, 37ºC) and then subjected to a shear bond strength test (SBS). Bond failures were classified according to the Adhesive Remnant Index (ARI) and analyzed with the Kruskal-Wallis and Mann-Whitney tests (5%). Using the same factors, 120 resin discs were made to assess the degree of conversion (DC) of the monomer. Data from the SBS (MPa) and DC (%) were analyzed by analysis of variance (2 factors) and Tukey's test (5%). For the SBS, the factors "polymerization" (R20 = 8.1B; V20 = 13.2A; V3 = 5.2C, p = 0.0001) and "surface treatment" (A = 3.1C; ATxt = 13.6A; Tse = 12.3A; SBU = 6.3B, p = 0.0001) were statistically significant among groups. The highest adhesion value were found for the ATxt/V20 group (22.2A) and the lowest value for the A/R20 group (1.2E). Regarding ARI, score 2 was the most prevalent in groups A, ATxt, V20 and V3, while score 4 was the most prevalent in the Tse, SBU and R20 groups, with no significant difference between them (p = 1.0). Regarding DC, the factors "polymerization" (R20 = 66.6A; V20 = 58.4B; V3 = 45.1C, p = 0.0001) and "surface treatment" (A = 52B, ATxt = 59.7A, Tse = 51.4B, SBU = 63.8A, p = 0.0001) were statistically significant. Tse was more sensitive to the variations in polymerization protocols than the other surface treatments. Treatment A did not present suitable bond strength or degree of conversion.

Adhesive Durability Inside the Root Canal Using Self-adhesive Resin Cements for Luting Fiber Posts.

OBJECTIVES: The aim of the study was to investigate the effects of various self-adhesive resin cements on the push-out bond strengths and nanoleakage expression at the luting interfaces of fiber posts immediately and after one year of aging. METHODS AND MATERIALS: One hundred forty-four extracted human anterior teeth were endodontically treated. After post space preparation, fiber posts were luted using five commercially available self-adhesive resin (SAR) cements and a core build-up material applied with a self-etch adhesive (BF: Bifix SE/Rebilda Post, VOCO; CSA: Clearfil SA Cement/Rely X Fiber Post, 3M ESPE; RX: RelyX Unicem 2/Rely X Fiber Post, 3M ESPE; SPC: Speed Cem/FRC Postec, Ivoclar Vivadent; SMC: Smart Cem/X Post, Dentsply; RB: Rebilda DC-Futurabond/Rebilda Post; n=22). For each group, half of the specimens were subjected to thermocycling (TC) (5°C-55°C, 10,000 cycles) and stored humid for one year at 37°C. Push-out bond strength data of six slices (thickness 1 mm) per root and nanoleakage expression of representative specimens were evaluated after 24 hours (baseline) and after TC and storage for one year (aging), respectively. RESULTS: Bond strength differed significantly among resin cements (p<0.0005) and the location inside the root canal (p<0.0005), but not by aging (p=0.390; repeated-measures analysis of variance). SMC (14.6±5.8 MPa) and RX (14.1±6.8 MPa) revealed significantly higher bond strength compared to BF (10.6±5.4 MPa) and RB (10.0±4.6 MPa) but differed not significantly from SPC (12.8±4.8) MPa; CSA (6.1±4.6 MPa) revealed significantly lower bond strength compared to all other investigated materials (p<0.05; Tukey Honestly Significantly Different). Qualitative nanoleakage analysis revealed more silver deposits at the interface in all groups after aging. For CSA, a large amount of silver deposits inside the cement was also observed at baseline and after aging. CONCLUSIONS: Fiber post luting using SAR cements demonstrated reliable bond strengths. Product-specific differences and initial degradation effects could be demonstrated.

Dental Cements for Luting and Bonding Restorations: Self-Adhesive Resin Cements.

Self-adhesive resin cements combine easy application of conventional luting materials with improved mechanical properties and bonding capability of resin cements. The presence of functional acidic monomers, dual cure setting mechanism, and fillers capable of neutralizing the initial low pH of the cement are essential elements of the material and should be understood when selecting the ideal luting material for each clinical situation. This article addresses the most relevant aspects of self-adhesive resin cements and their potential impact on clinical performance. Although few clinical studies are available to establish solid clinical evidence, the information presented provides clinical guidance in the dynamic environment of material development.

Influence of Different Curing Modes on Polymerization Behavior and Mechanical Properties of Dual-Cured Provisional Resins.

This study determined the influence of curing mode on polymerization behavior and mechanical properties of dual-cured provisional resins. Three dual-cured bisacryl-based provisional resins were used: Tempsmart (TS; GC Corp), Luxatemp Automix Solar (LX; DMG Chemisch Pharmazeutishe Fabrik GmbH), and Integrity Multi·Cure (IG; Dentsply Caulk). A self-cured bisacryl-based provisional resin, Protemp Plus (PP; 3M ESPE) and a conventional poly(methyl methacrylate) (PMMA) provisional resin, Unifast III (UF; GC Corp) were used as controls. The inorganic filler content and coefficients of linear thermal expansion of the test materials were measured. Six specimens of each material were used to determine the flexural strength, elastic modulus, and resilience. The changes in ultrasound velocity during polymerization were measured. The average inorganic filler contents of the provisional resins, apart from UF, ranged from 24.4 to 39.3 wt%. The highest inorganic filler content was determined for LX, whereas TS showed the lowest value among the tested materials. The average coefficients of thermal expansion of the tested provisional resins ranged from 77.3 to 107.7 (×10-6/°C). TS and IG showed significantly lower thermal expansions than the other tested provisional resins. The mean flexural strengths of the provisional resins ranged from 70.4 to 122.6 MPa, the mean elastic moduli ranged from 1.8 to 3.7 GPa, and the mean resilience of the provisional resins ranged from 1.1 to 2.3 MJ/mm3, respectively. Dual-cured provisional resins showed significantly higher flexural strengths than the PMMA resin. However, in all cases, the light-curing mode showed significantly higher flexural strengths than the self-curing mode. In the initial polymerization phase, dual-cured resins in the light-curing mode showed a rapid increase in the speed of sound (V) during light irradiation, followed by a slower increase. Conversely, the dual-cured resins in the self-curing mode showed a slower initial increase, followed by a rapid increase. Although no significant difference in V was observed between 10 and 15 minutes in the light-curing mode of all tested dual-cured resins, a significantly higher V value was obtained at 15 minutes than at 10 minutes in the self-curing modes for LX and IG. Regardless of the curing mode, tested dual-cured provisional resins showed superior mechanical properties than the conventional PMMA provisional resin. However, dual-cured provisional resin flexural properties and polymerization behavior were affected by the curing mode. This study indicated that the light-curing mode might be recommended for all dual-cured provisional resins because of the enhancement of their mechanical properties and reduction of chair time.

Longevity of metal-ceramic crowns cemented with self-adhesive resin cement: a prospective clinical study

Resin cements are often used for single crown cementation due to their physical properties. Self-adhesive resin cements gained widespread due to their simplified technique compared to regular resin cement. However, there is lacking clinical evidence about the long-term behavior of this material. The aim of this prospective clinical trial was to assess the survival rates of metal-ceramic crowns cemented with self-adhesive resin cement up to six years. One hundred and twenty-nine subjects received 152 metal-ceramic crowns. The cementation procedures were standardized and performed by previously trained operators. The crowns were assessed as to primary outcome (debonding) and FDI criteria. Statistical analysis was performed using Kaplan-Meier statistics and descriptive analysis. Three failures occurred (debonding), resulting in a 97.6% survival rate. FDI criteria assessment resulted in scores 1 and 2 (acceptable clinical evaluation) for all surviving crowns. The use of self-adhesive resin cement is a feasible alternative for metal-ceramic crowns cementation, achieving high and adequate survival rates.

Is the bonding of self-adhesive cement sensitive to root region and curing mode?

OBJECTIVES: To evaluate the influence of two curing techniques on the degree of conversion (DC) of resin cements and on bond strength (BS) of fiber posts in different regions of root dentin. MATERIAL AND METHODS: Twenty single-rooted premolars were endodontically treated, and the post spaces were prepared. The roots were randomly divided into two groups (n=10), according to the activation mode of the resin cement RelyX™ U200 (3M ESPE Saint Paul, MN, USA): conventional (continuous activation mode) and soft-start activation mode (Ramp). The posts (WhitePost DC/FGM) were cemented according to the manufacturer's recommendations and, after one week, the roots were cross-sectioned into six discs each of 1-mm thickness, and the cervical, medium, and apical thirds of the root canals were identified. The DC was evaluated under micro-Raman spectroscopy and the BS was evaluated by the push-out test. The data were analyzed by two-way ANOVA and Tukey's test (α=0.05). RESULTS: Neither the activation mode nor the root regions affected the DC of the resin cement. Higher BS was achieved in the soft-start group (p=0.036); lower BS was observed in the apical third compared to the other root regions (p<0.001). Irrespective of the activation mode and root region, the mixed failure mode was the most prevalent. CONCLUSION: The BS of fiber posts to root canals can be improved by soft-started polymerization. The DC was not affected by the curing mode.

[Curing mode of universal adhesives affects the bond strength of resin cements to dentin].

OBJECTIVE: To determine the effects of curing mode of one-step and two-step universal adhesives on the micro-tensile bond strength (µTBS) of different dual-cure resin cements to dentin. METHODS: One-step universal adhesive Single Bond Universal (SBU), and two-step universal adhesive OptiBond Versa (VSA) were chosen as the subjects, one-step self-etching adhesive OptiBond All in One (AIO) and two-step self-etching adhesive Clearfil SE Bond (SEB) were control groups, and two dual-cure resin cements RelyX Ultimate (RLX) and Nexus 3 Universal (NX3) were used in this study. In this study, 80 extracted human molars were selected and the dentin surface was exposed using diamond saw. The teeth were divided into 16 groups according to the adhesives (AIO, SBU, SEB, VSA), cure modes of adhesives (light cure, non-light cure) and resin cements (RLX, NX3). The adhesives were applied on the dentin surface following the instruction and whether light cured or not, then the resin cements were applied on the adhesives with 1 mm thickness and light cured (650 mW/cm(2) for 20 s. A resin was built up (5 mm) on the cements and light cured layer by layer. After water storage for 24 h, the specimens were cut into resin-cement-dentin strips with a cross sectional area of 1 mm×1 mm and the µTBS was measured. RESULTS: Regarding one-step universal adhesive (SBU) light cured, the µTBS with RLX [(35.45±7.04) MPa] or NX3 [(26.84±10.39) MPa] were higher than SBU non-light cured with RLX [(17.93±8.93) MPa)] or NX3 [(10.07±5.89) MPa, P<0.001]. Compared with AIO, light-cured SBU combined with RLX presented higher µTBS than AIO group [(35.45±7.04) MPa vs. (24.86±8.42) MPa, P<0.05]. When SBU was not lighted, the µTBS was lower than AIO [(17.93±8.93) MPa vs. (22.28±7.57) MPa, P<0.05]. For two-step universal adhesive (VSA) and control adhesive (SEB), curing mode did not affect the µTBS when used with either RLX or NX3 (25.98-32.24 MPa, P>0.05). CONCLUSION: Curing mode of one-step universal adhesive may affect the µTBS between dual-cure resin cements and dentin, while for two-step universal adhesive, the curing mode and the type of resin cements did not influence the µTBS.

Is the bonding of self-adhesive cement sensitive to root region and curing mode?

Abstract Objectives To evaluate the influence of two curing techniques on the degree of conversion (DC) of resin cements and on bond strength (BS) of fiber posts in different regions of root dentin. Material and Methods Twenty single-rooted premolars were endodontically treated, and the post spaces were prepared. The roots were randomly divided into two groups (n=10), according to the activation mode of the resin cement RelyX™ U200 (3M ESPE Saint Paul, MN, USA): conventional (continuous activation mode) and soft-start activation mode (Ramp). The posts (WhitePost DC/FGM) were cemented according to the manufacturer’s recommendations and, after one week, the roots were cross-sectioned into six discs each of 1-mm thickness, and the cervical, medium, and apical thirds of the root canals were identified. The DC was evaluated under micro-Raman spectroscopy and the BS was evaluated by the push-out test. The data were analyzed by two-way ANOVA and Tukey’s test (α=0.05). Results Neither the activation mode nor the root regions affected the DC of the resin cement. Higher BS was achieved in the soft-start group (p=0.036); lower BS was observed in the apical third compared to the other root regions (p<0.001). Irrespective of the activation mode and root region, the mixed failure mode was the most prevalent. Conclusion The BS of fiber posts to root canals can be improved by soft-started polymerization. The DC was not affected by the curing mode.

Longevity of metal-ceramic crowns cemented with self-adhesive resin cement: a prospective clinical study

Abstract Resin cements are often used for single crown cementation due to their physical properties. Self-adhesive resin cements gained widespread due to their simplified technique compared to regular resin cement. However, there is lacking clinical evidence about the long-term behavior of this material. The aim of this prospective clinical trial was to assess the survival rates of metal-ceramic crowns cemented with self-adhesive resin cement up to six years. One hundred and twenty-nine subjects received 152 metal-ceramic crowns. The cementation procedures were standardized and performed by previously trained operators. The crowns were assessed as to primary outcome (debonding) and FDI criteria. Statistical analysis was performed using Kaplan-Meier statistics and descriptive analysis. Three failures occurred (debonding), resulting in a 97.6% survival rate. FDI criteria assessment resulted in scores 1 and 2 (acceptable clinical evaluation) for all surviving crowns. The use of self-adhesive resin cement is a feasible alternative for metal-ceramic crowns cementation, achieving high and adequate survival rates.

Efeito de adição de rodamina B e fluoresceína sódica a sistemas adesivos não simplificados: aspectos fotofísicos e físico-químicos / Effect of addition of rhodamine B and fluorescein to conventional etch-and-rinse and self-etching adhesive systems: photophysical and physical-chemical aspects

A adição de corantes fluorescentes a adesivos odontológicos possibilita a investigação da distribuição espacial desses materiais na interface dente-restauração, utilizando-se a microscopia confocal de varredura a laser (MCVL). A literatura indica falta de padronização na aplicação de agentes fluorescentes com tal finalidade. Esse estudo sistematizou estratégias para a adição de rodamina B (RB) e fluoresceína sódica (FS) a um sistema adesivo convencional de três passos, Adper Scotchbond Multi-Purpose (MP), e um autocondicionante de dois passos, Clearfil SE Bond (SE), considerados "padrão-ouro" na Odontologia. Os objetivos principais foram (a) determinar a menor faixa de concentrações de RB e FS necessária para produzir imagens satisfatórias da interface dentina-adesivo e (b) avaliar o efeito da adição desses corantes sobre algumas propriedades das resinas. Os adesivos foram marcados com RB ou FS em concentrações decrescentes (0,5, 0,1, 0,02 e 0,004 mg/mL) por meio de um método de dispersão semidireto. O comportamento fotofísico/ fluorescente dos adesivos marcados foi investigado por espectroscopia de fotoluminescência e MCVL. Paralelamente, avaliaram-se os adesivos quanto ao grau de conversão (GC) e ao ângulo de contato (AC). Tanto os resultados de GC como os de AC foram submetidos à análise de variância com dois fatores (adesivo e tratamento) com α = 0,05, seguida de teste post-hoc de Tukey. Os máximos comprimentos de onda de emissão e de excitação da RB e da FS foram influenciados pelo meio polimérico e pela concentração de corante de modo geral. A MCVL preliminar de amostras de adesivo polimerizado, realizada sob condições experimentais padronizadas, mostrou que o comportamento fluorescente da RB em MP e SE foi muito semelhante na mesma concentração de corante, mas o mesmo não pôde ser dito do comportamento da FS, que foi notavelmente inferior no adesivo autocondicionante, SE, na concentração mais alta. Em dentina, os adesivos preparados com RB nas concentrações-alvo de 0,1 e 0,02 mg/mL apresentaram fluorescência ótima; já aqueles preparados com 0,004 mg/mL produziram fraco sinal. Adesivos preparados com FS a 0,5 mg/mL apresentaram ótima fluorescência na interface de adesão, enquanto que concentração menor desse corante não produziu sinal suficiente. Padrões morfológicos aparentemente atípicos foram observados na interface de adesão, quando da associação do adesivo SE com o corante FS. A adição de RB e FS nas quatro concentrações indicadas aos adesivos MP e SE não afetou o GC nem o AC em comparação com os grupos de controle correspondentes. Em suma, a RB mostra-se um corante mais versátil que a FS na avaliação morfológica das interfaces dentina-MP e dentina-SE via MCVL. A menor faixa de concentrações de RB nos adesivos MP e SE, na qual é possível produzir imagens satisfatórias das interfaces, situa-se entre 0,1­0,02 mg/mL. Já o corante FS deve ser adicionado a esses adesivos a pelo menos 0,5 mg/mL para produzir níveis de fluorescência satisfatórios na interface de adesão. A não ocorrência de efeitos deletérios sobre a polimerização e a molhabilidade das resinas estabelece uma margem de segurança para a incorporação desses agentes fluorescentes (em concentração ≤ 0,5 mg/mL) nesses sistemas monoméricos.(AU)

The addition of fluorescent dyes to dental adhesives makes it possible to investigate the spatial distribution of such resin-based materials in the tooth-restoration interface, using confocal laser scanning microscopy (CLSM). Literature indicates a lack of standardization on the application of fluorescent agents for this purpose. This work presents strategies for adding rhodamine B (RB) and fluorescein sodium salt (FS) to a three-step etch-and-rinse adhesive system, Adper Scotchbond Multi-Purpose (MP), and a two-step self-etching one, Clearfil SE Bond (SE), both regarded as "gold standard" in restorative dentistry. The main objectives were (a) to determine the lowest range of RB and FS concentrations required to produce suitable images of the dentin-adhesive interface via CLSM and (b) to investigate potential effects of addition of these dyes on some resin properties. The adhesives were labeled with RB or FS at decreasing concentrations (0.5, 0.1, 0.02 and 0.004 mg/mL) by means of a semi-direct dispersion method. The photophysical/fluorescent behavior of the labeled resins was investigated by photoluminescence spectroscopy and by CLSM. The adhesives were also investigated with regards to the degree of conversion (DC) and contact angle (CA). A two-way ANOVA of "adhesive" and "treatment" was conducted on DC and CA separately, followed by Tukey's test. The maximum emission and excitation wavelengths of RB and FS were influenced by the host polymer and the dye concentration in general. The preliminary CLSM of cured adhesive samples, performed with standardized settings, showed that the fluorescent behavior of RB in MP and SE was very similar in the same dye concentration, unlike the behavior of FS, which was lower in the self-etching adhesive for the highest dye concentration. In dentin, the adhesives prepared with RB at the target concentrations of 0.1 and 0.02 mg/mL presented optimal fluorescence; those with 0.004 mg/mL produced poor signal. Adhesives prepared with FS at 0.5 mg/mL presented optimal fluorescence at the bonding interface, whereas lower concentrations of FS did not produce sufficient signal. Atypical morphological features were observed at the bonding interface, when adhesive SE was used with FS. The addition of RB and FS at the four decreasing concentrations to adhesives MP and SE did not affect DC or CA compared to the corresponding controls. In short, RB is more versatile than FS for the morphological characterization of dentin-MP and dentin-SE interfaces via MCVL. The lowest range of RB concentrations in adhesives MP and SE that can produce suitable images of the bonding interface lies between 0.1­0.02 mg/mL. The dye FS should be added to these adhesives at 0.5 mg/mL at least to produce satisfactory fluorescence levels at the bonding interface. Since negative effects on polymerization and wettability of the resins were not observed, the use of RB and FS (in concentration ≤ 0.5 mg/mL) together with MP and SE should be reliable in terms of resin properties.(AU)