RESUMEN
Background: Impressions that maintain their dimensional stability after autoclaving effectively control cross-infection and contamination resulting from a patient's oral secretions. Purpose: The study aimed to assess the dimensional stability of autoclavable polyvinyl siloxanes after disinfection and sterilization. Methods: A stainless steel metal model containing three full veneer crown preparations was fabricated according to ANSI/ADA specification No. 19. Reference grooves were established on the occlusal and axial surfaces of the abutments for accurate measurements. Forty impressions were created from the master model using single-step impression technique monophase polyvinyl siloxane material (AFFINIS, Coltene/Whaledent, Altstatten, Switzerland). The impressions were categorized into four groups: Group A (control, ten untreated impressions), Group B (ten disinfected impressions with 5.25 % sodium hypochlorite [NaOCl]), Group C (ten disinfected impressions with 2 % glutaraldehyde), and Group D (ten autoclaved impressions at 134 °C for 18 min). Subsequently, stone casts were produced using type IV gypsum products (Gelstone R, BK Giulini Chemie, Ludwigshafen/Rh., Germany). The dimensional accuracy of the obtained casts was assessed by measuring the inter-abutment measurements (between the abutments) and the intra-abutment measurements (diameter and height of the abutments). These measurements were performed using a universal measuring microscope (Olympus stereomicroscope B061 Imaging Corp. Tokyo, Japan) with a precision of 0.001 mm. The dimensions of the stone casts from the study groups were then compared to those of the control group. Data analysis was performed using a one-way ANOVA with a significance level of α = 0.05. Results: AFFINIS impressions subjected to chemical disinfection in 5.25 % NaOCl and 2 % glutaraldehyde with different immersion times showed slight expansion in the intra- and inter-abutment measurements. The impressions autoclaved at 134 °C for 18 min showed slight shrinkage in the intra- and inter-abutment measurements. The dimensional change was statistically non-significant, and the percent of dimensional changes within the experimental groups was within the clinically accepted limit (α < 0.5). Conclusion: AFFINIS polyvinyl siloxanes retain dimensional stability suitable for clinical use when subjected to chemical disinfection and steam autoclaving.
RESUMEN
[This corrects the article DOI: 10.1155/2019/6548519.].
RESUMEN
STATEMENT OF PROBLEM: In some clinical situations, the vertical length of either a prepared tooth or an implant abutment is short, while the occlusal clearance to be restored by a porcelain crown is large. Incisal thickness of the veneering porcelain should be considered to prevent mechanical failure of the crown. PURPOSE: The aim of this study is to evaluate the effect of two different incisal veneering porcelain thickness on the fracture resistance of the anterior all-ceramic CAD/CAM zirconia crown system as compared with the conventionally used metal ceramic crown system. METHOD: CAD/CAM zirconia all-ceramic and metal ceramic crowns were fabricated on the prepared dies with standardized dimensions and designs using standardized methods according to the manufacturer's instructions. All crowns were then adhesively luted with resin-based cement (Multilink cement system), subjected to thermal cycling and cyclic loading, and were loaded until fracture using the universal testing machine to indicate the fracture resistance for each crown material in each veneering thickness. RESULTS: Statistical analysis was carried out, and the results showed that the fracture resistance of the nickel-chromium metal ceramic group was significantly higher than that of the CAD/CAM zirconia all-ceramic group. Also, the fracture resistance of crowns with 1.5 mm incisal veneering thickness was significantly higher than those with 3 mm incisal veneering thickness in both groups. Furthermore, there was no significant difference in the fracture mode of the two groups where 50% of the total specimens demonstrated Mode II (veneer chipping), while 35% demonstrated Mode I (visible crack) and only 15% demonstrated Mode III (bulk fracture). CONCLUSION: High failure load values were demonstrated by the specimens in this study, which suggest sufficient strength of both incisal veneering thickness in both crown systems to withstand clinical applications; however, the fracture patterns still underline the requirement of a core design that support a consistent thickness of the veneering ceramic, and it is recommended to conduct long-term prospective clinical studies to confirm findings reported in the present study.