RESUMEN
The aim of this study was to investigate the effect of repressing leftover heat-pressed lithium disilicate material on its mechanical and optical properties. A lithium disilicate ingot (IPS e.max® Press, IvoclarVivadent, Schaan, Liechtenstein) shade (A1) low translucency was first heat-pressed to yield ceramic bars and disks. Then, the second and third presses were fabricated from the leftovers of the previous pressing cycles. A total of 36 bars and 15 disk specimens were fabricated and divided into three groups according to the number of pressing cycles (n = 12 bars and n = 5 disks): P1: first press (control), P2: second press, and P3: third press. The specimens were tested for flexural strength, color change, Vickers hardness, and surface topography under scanning electron microscopy. One-way ANOVA testing was used to evaluate flexural strength and hardness, while an independent t-test was performed to evaluate color change. There was no significant difference in flexural strength as the number of heat-pressed cycles increased (p = 0.283). Similarly, there was no significant difference in the microhardness values between all groups (p = 0.220). The overall color change ∆E between P1-P2 and P1-P3 were 2.01 and 2.14, respectively. The SEM images showed evenly distributed and densely packed lithium disilicate crystals in the P1 group. However, larger and less densely packed crystals were noticeable in P2 and P3. The IPS e.max Press could be repressed up to two times without an adverse effect on mechanical properties or color stability. These results may support the reuse of pressed lithium disilicate for economical purposes, but further clinical evaluation should be conducted to confirm these findings.
RESUMEN
PURPOSE: Despite the good sealing ability and biocompatibility of mineral trioxide aggregate (MTA), its slow setting, high degradation, and weakness limit its use in surgical endodontics and high stress-bearing areas. This study aimed to develop two new liquids to control these drawbacks. They were prepared from calcium chloride, fumed silica, and hydroxyapatite or calcium phosphate and coded "H" and "P," respectively. METHODS: Portland cement, Grey ProRoot® MTA, and white ProRoot MTA were mixed with distilled water (control) or liquid "H" or "P." The pH, setting time, degradation rate, leachant/precipitate' composition, compressive strength, and morphology were assessed. RESULTS: Both liquids maintained MTA's high alkalinity and reduced the setting time by 1-2 orders of magnitude. Both liquids, H in particular, significantly reduced the degradation rate of Grey ProRoot and White ProRoot MTA®. Calcite has been identified as the main phase of the leachant or precipitate formed during the cement's degradation. Calcium hydroxide or hydroxyapatite was also identified with Grey ProRoot MTA mixed with H liquid. These liquids also significantly increased the compressive strength with no statistical differences between them; this was associated with the production of dense, consolidated structures. CONCLUSIONS: The modified MTA could be used in surgical endodontics and high stress-bearing areas.
RESUMEN
Effective shaping and cleaning of root canals are essential for the success of endodontic treatment. Due to the complex anatomy of root canal spaces, the use of various instrumentation techniques alone is not effective in producing bacteria-free root canal spaces. Irrigation, disinfectants, rinses, and intervisit medications are used in conjunction with the mechanical instrumentation to ensure the success of endodontic treatment. Sodium hypochlorite (NaOCl), a halogenated compound, is routinely used to irrigate the root canal during endodontic treatments. NaOCl has been known for its antibacterial action, proteolytic and dissolution capacity, and debridement properties. NaOCl, however, can alter the composition of dentin and hence its interaction with the adhesive resins used to bond the restorative materials to treated dentin. This review therefore covers in depth the action of NaOCl on dentin-adhesive resin bond strength including both enhancement and reduction, then mechanisms proposed for such action, and finally how the adverse action of NaOCl on dentin can be reversed.