Effect of etching with potassium hydrogen difluoride and ammonium hydrogen difluoride on bonding of a tri-n-butylborane initiated resin to zirconia.

The purpose of the current study was to evaluate the effect of etching with potassium hydrogen difluoride (KHF2) and ammonium hydrogen difluoride (NH4HF2) on the bond strength of a self-polymerizing methyl methacrylate resin (MMA-TBB) bonded to zirconia. Zirconia disks were prepared using the following surface treatment: no treatment, alumina blasting, and etching with KHF2 or NH4HF2. The specimens were bonded with the MMA-TBB. The shear bond (Ø=5 mm) strength was measured. The surface free energies of the specimens were determined by measuring contact angles. The KHF2 and NH4HF2 groups exhibited higher shear bond strength and surface free energy than did the alumina blasting and no treatment groups. Compared with alumina blasting, etching with KHF2 and NH4HF2 exhibited superior bonding ability of mechanical retention to zirconia.

Effect of mechanochemical surface preparation on bonding to zirconia of a tri-n-butylborane initiated resin.

This study aimed to evaluate the effect of surface preparation on bond strength of a tri-n-butylborane initiated resin (MMA-TBB) bonded to zirconia. Zirconia disks were either airborne-particle abraded with alumina or silica-coated. The disks were thereafter primed with one of the following materials: phosphate-silane (Clearfil Ceramic Primer), phosphate (Alloy Primer), or silane (ESPE Sil). The specimens were bonded with the MMA-TBB. Shear bond strength was determined both before and after thermocycling. Bond strength of unprimed zirconia (control) was not affected by the surface roughness of each adherend. Priming with phosphate was effective for bonding alumina-blasted zirconia. Priming with silane was effective for bonding silica-coated zirconia. Priming effect of the phosphate-silane was superior to that of silane alone for bonding silica-coated zirconia. Bond strength to zirconia of the MMATBB is significantly influenced by a combination of the specific functional monomer and the surface modification performed rather than the material surface roughness.

Wear characteristics of polished and glazed lithium disilicate ceramics opposed to three ceramic materials.

This study compared the wear characteristics of a heat-pressed lithium disilicate ceramic material opposed to feldspathic porcelain, a lithium disilicate glass ceramic, and zirconia materials. Ceramic plate specimens were prepared from feldspathic porcelain (EX-3 nA1B), lithium disilicate glass ceramics (e.max CAD MO1/C14), and zirconia (Katana KT 10) and then ground or polished. Rounded rod specimens were fabricated from heat-pressed lithium disilicate glass ceramic (e.max press LT A3) and then glazed or polished. A sliding wear testing apparatus was used for wear testing. Wear of glazed rods was greater than that of polished rods when they were abraded with ground zirconia, ground porcelain, polished porcelain, or polished lithium disilicate ceramics. For both glazed and polished rods, wear was greater when the rods were abraded with ground plates. The findings indicate that application of a polished surface rather than a glazed surface is recommended for single restorations made of heat-pressed lithium disilicate material. In addition, care must be taken when polishing opposing materials, especially those used in occlusal contact areas. (J Oral Sci 58, 117-123, 2016).

Effect of sodium sulfite, carboxylic monomer, and phosphoric acid etching on bonding of tri-n-butylborane initiated resin to human enamel.

The purpose of the present study is evaluation of bonding durability of tri-n-butylborane (TBB) initiated resin without 4-methacryloyloxyethyl trimellitate anhydride (4-META) joined to human enamel. Ground human enamel was bonded with TBB resin under six surface conditions: 1) as ground, 2) primed with Teeth Primer, 3) sodium sulfite solution, 4) 4-META solution, 5) acetone-water, and 6) phosphoric acid etching. Pre- and post-thermocycling bond strengths and change in strength after thermocycling were compared. Etching enamel with 35-45% phosphoric acid enhanced bonding durability between enamel and TBB-initiated resin. Priming with Teeth Primer or 4-META solution improved bond strength between enamel and TBB-initiated resin. Sodium sulfite had little effect on enamel bonding in the present bonding systems.

Influence of ceramic surface texture on the wear of gold alloy and heat-pressed ceramics.

The purpose of this study was to evaluate the influence of ceramic surface texture on the wear of rounded rod specimens. Plate specimens were fabricated from zirconia (ZrO2), feldspathic porcelain, and lithium disilicate glass ceramics (LDG ceramics). Plate surfaces were either ground or polished. Rounded rod specimens with a 2.0-mm-diameter were fabricated from type 4 gold alloy and heat-pressed ceramics (HP ceramics). Wear testing was performed by means of a wear testing apparatus under 5,000 reciprocal strokes of the rod specimen with 5.9 N vertical loading. The results were statistically analyzed with a non-parametric procedure. The gold alloy showed the maximal height loss (90.0 µm) when the rod specimen was abraded with ground porcelain, whereas the HP ceramics exhibited maximal height loss (49.8 µm) when the rod specimen was abraded with ground zirconia. There was a strong correlation between height loss of the rod and surface roughness of the underlying plates, for both the gold alloy and HP ceramics.

Effect of silane and phosphate primers on the adhesive performance of a tri-n-butylborane initiated luting agent bonded to zirconia.

The purpose of this study was to evaluate the effects of primers on the bond strength and durability of an acrylic resin luting agent bonded to zirconia. Disk specimens were fabricated from zirconia partially stabilized with yttrium oxide. The disks were primed with one of the following materials: Alloy Primer (AP), Ceramic Primer (CP), Liquid A of the Porcelain Liner M (PLM-A), Liquid B of Porcelain Liner M (PLM-B), Porcelain Liner M (PLM-A+PLM-B), Monobond Plus (MP), and mixture of AP and PLM-B. The specimens were bonded with a tri-n-butylborane (TBB)-initiated luting agent. The shear bond strengths were determined both before and after thermocycling. The results were statistically analyzed with a non-parametric procedure. The highest post-thermocycling bond strength was generated from the groups primed with MP, CP, and AP. It can be concluded that the application of three phosphate primers is recommended for bonding the zirconia with the TBB-initiated luting agent.