Effect of different solutions in reversing the damage caused by radiotherapy in dentin structure.

BACKGROUND: Previous studies have shown that radiotherapy of the head and neck region can cause direct changes in dental structure. This study evaluated the effect of different solutions on the dentin chemical composition and collagen structure of irradiated dentin. MATERIAL AND METHODS: Sixty maxillary canines were distributed in 2 groups (n=30): non-irradiated and irradiated (radiotherapy: X-rays of 6 MV in 30 cycles of 2 Gy to 60 Gy). The teeth were sectioned, sanded, and polished to obtain 3x3x2 mm fragments, which were redistributed in 3 subgroups (n=10) according to the treatment employed: chlorhexidine 2% (CL), chitosan 0.2% (QT), and 0.5 M carbodiimide (EDC). The samples were analyzed in FTIR at time zero (T0-control) and after 1 (T1), 3 (T3), and 5 (T5) minutes of immersion in the tested solutions. The data for the areas of the carbonate (C), amide I (AI) bands, and the ratio between the areas of the amide III/proline and hydroxyproline (AIII/PH) bands were analyzed using ANOVA and Tukey test (α=5%). RESULTS: QT showed lower C values at T1, T3, and T5 (P<0.0001), presenting lower values when compared to CL and EDC subgroups (P<0.05). AI values at T3 and T5 were higher than T0-control and T1, independently of the radiotherapy and dentin treatment factors (P<0.05). At T0-control, the AIII/PH ratio was lower in the irradiated group (P<0.05), whereas the EDC treatment at T1, T3, and T5 and QT at T3 and T5 increased these values (P<0.05), making them similar to non-irradiated subgroups (P>0.05). CONCLUSIONS: Radiotherapy changes the secondary structure of collagen, and EDC was able to restore collagen integrity after 1 minute of immersion, without changing dentin inorganic composition.

Effect of carbodiimide and chlorhexidine on the bond strength longevity of resin cement to root dentine after radiation therapy.

AIM: To evaluate the effect of carbodiimide (EDC) and chlorhexidine (CHX) on the bond strength (BS) of resin cement to root dentine of teeth submitted to radiotherapy. METHODOLOGY: One hundred and twenty extracted maxillary canines were selected and assigned to 2 groups (n = 60): nonirradiated and irradiated (30 cycles of 2 Gy, total 60 Gy). Roots lengths were standardized, and canals were prepared and filled. Post spaces were then prepared, and the samples were redistributed according to dentine treatment (n = 20): saline solution (SF); CHX 2%; or EDC 0.5M. After drying the post space, fibreglass posts were cemented. Cross-sectioned slices were obtained, and in half of the specimens of each subgroup (n = 10), the analysis was performed immediately; the others (n = 10) were stored for 10 months before analyses. The most cervical slice of each third was subjected to a push-out test and failure pattern analysis (n = 10), and the most apical slice submitted to the analysis of the adhesive interface by SEM (n = 5). The bond strength data were submitted to anova and Tukey tests, the adhesive interface adaptation was submitted to Kruskal-Wallis and Dunn's tests, and the Chi-square test was used to evaluate the type of failure. RESULTS: The irradiated specimens had significantly lower bond strength (13.8 ± 4.3) than the nonirradiated (18.1 ± 3.1; P < 0.001). For the irradiated teeth, the bond strengths were significantly lower in the SF and CHX groups (P < 0.001). Also, the bond strengths reduced significantly after 10 months in the SF and CHX groups (P < 0.001). Cohesive failures occurred in dentine for irradiated specimens. Poorer interface adaptation, dentine fractures and microfractures were observed in irradiated specimens, and better adaptation was observed for specimens after EDC treatment. CONCLUSIONS: Radiotherapy was associated with lower bond strength and worse interface adaptation. Dentine treatment with EDC contributed to adhesive interface longevity during the cementation of glass fibre posts in nonirradiated and irradiated teeth.

Effects of different lasers on organic/inorganic ratio of radicular dentin.

The aim of this study was to evaluate the chemical stability of endodontic-treated root dentin after different laser irradiations through Raman spectroscopy. Fifty maxillary canines were selected and prepared with K3 system. Roots were randomly distributed into five groups (n = 10) according to the surface treatment: GI (water), GII (NaOCl + EDTA), GIII (NaOCl + EDTA + 980 nm Diode laser), GIV (NaOCl + EDTA+ 1064 nm Nd: YAG laser) and GV (NaOCl + EDTA+ 2780 nm Er,Cr: YSGG laser). Lasers were applied for 20 s. Samples were bisected, and the organic and inorganic content of dentin was analyzed by Raman spectroscopy. Data were submitted to ANOVA and Tukey tests (p < 0.05). None of the surface treatments alter the inorganic content (cts) (p = 0.183). Roots irradiated with Er,Cr: YSGG laser had a reduced collagen content (GV-290.7 ± 41.7) compared with the water-treated roots (GI-328.3 ± 63.5) and those treated with NaOCl + EDTA (GII-333.9 ± 55.8). Roots irradiated with Er,Cr: YSGG laser also showed a higher inorganic/organic ratio (GV-9.5 ± 1.1) than roots treated with water (GI-7.7 ± 1.5), NaOCl + EDTA (GII-8.0 ± 1.4) and diode laser (GIII-8.2 ± 1.6). Both organic and inorganic contents increased from cervical to apical thirds in all groups. None of the surface treatments were able to promote changes in the inorganic content of the root dentin; treatment with NaOCl + EDTA combined with Er,Cr: YSGG altered collagen.