RESUMEN
NiV2O6 thin films were grown on glass slides with varying thicknesses using nebulizer spray pyrolysis. The impact of thickness on the thin films' optical, structural, morphological, and electrical characteristics was systematically investigated. X-ray diffraction and micro-Raman analysis confirmed the formation of the triclinic NiV2O6 system. Surface morphology and roughness variations in the as-deposited NiV2O6 films were studied using scanning electron microscopy (SEM) and a profilometer. Optical properties, including optical band gap (Eg), extinction coefficient (k), absorption coefficient (α), and refractive index (n), were determined through optical reflectance and transmittance measurements. The optical energy gap of the as-deposited NiV2O6 films decreased from 2.02 eV to 1.58 eV with increased layer thickness. Furthermore, the photo-detectivity of the films demonstrated an enhancement corresponding to the prolonged spray time. The sensitivity values obtained for visible irradiation were 328, 511, and 433 for samples S1, S2, and S3, respectively. The obtained results can be imputed to the specific porous microstructure.
RESUMEN
The beneficial effects of lanthanide incorporation into 0.94Na0.5Bi0.5TiO3-0.06BaTiO3 (BNT-BT) matrix on its functional properties were investigated. The conventional solid-state method was used for synthesizing samples. The structural refinement revealed that all samples crystallized in R3c rhombohedral symmetry. Raman spectroscopy study was carried out using green laser excitation and revealed that no clear perceptible variation in frequency is observed. Dielectric measurements unveiled that the introduction of rare earth obstructed the depolarization temperature promoted in BNT-BT, the diffusive phase transition decreasing with increasing lanthanide size. Only dysprosium addition showed comparable diffusion constant and dielectric behavior as the unmodified composition. Further, the comparison of the obtained ferroelectric hysteresis and strain-electric field loops revealed that only Dy-phase exhibited interesting properties comparing parent composition. In addition, the incorporation of lanthanides Ln3+ into the BNT-BT matrix led to the development of luminescence characteristics in the visible and near infrared regions, depending on the excitation wavelengths. The simultaneous occurrence of photoluminescence and ferroelectric/piezoelectric properties opens up possibilities for BNT-BT-Ln to exhibit multifunctionality in a wide range of applications.
RESUMEN
The effect of ferromagnetic CaMnO3 (CMO) addition to structural, magnetic, dielectric, and ferroelectric properties of BiFeO3 is presented. X-ray diffraction and Raman investigation allowed the identification of a single pseudocubic perovskite structure. The magnetic measurement showed that the prepared films exhibit a ferromagnetic behavior at a low temperature with both coercive field and remnant magnetization increased with increasing CMO content. However, a deterioration of magnetization was observed at room temperature. Ferroelectric study revealed an antiferroelectric-like behavior with a pinched P-E hysteresis loop for 5% CMO doping BFO, resulting in low remnant polarization and double hysteresis loops. Whereas, high remnant polarization and coercive field with a likely square hysteresis loop are obtained for 10% CMO addition. Furthermore, a bipolar resistive switching behavior with a threshold voltage of about 1.8 V is observed for high doped film that can be linked to the ferroelectric polarization switching.
RESUMEN
Rare earth element-doped Bi0.5Na0.5TiO3-BaTiO3 (BNT-BT-RE) polycrystalline thin films were processed on a platinized substrate by chemical solution deposition. The microstructure, dielectric, and ferroelectric properties were investigated for all prepared films. It was found that the incorporation of rare earth elements into the BNT-BT matrix increases both the dielectric constant and the breakdown strength while maintaining low dielectric losses, leading to an enhancement of the energy storage density to Wrec = 12 and 16 J/cm3 under an effective field of E = 2500 kV/cm, for Nd- and Dy-based films, respectively. The optical properties of films containing the lanthanide element were investigated and the obtained results bear interest for luminescence applications. The simultaneous appearance of ferroelectric and optical properties in the system under investigation is very promising for advanced optoelectronic devices.