The application of FRPs in civil infrastructure has increased, particularly in the last 20 years. FRPs have gained importance because of their resistance to harsh environments, high strength-to-weight ratio, and good corrosion resistance, and they are faster and easier to apply than other traditional methods. The rehabilitation of structures is the main area in which FRPs have been developed, because they have allowed for compliance with architectural restraints in historic structures. This review is a compilation of the research conducted on the laboratory and field applications of FRPs, highlighting the different applied methods, installation difficulties, and failure modes of FRPs. Moreover, this review compares studies on the types of fibers such as CFRPs, GFRPs, and AFRPs, and their effects would affect the mechanical properties of civil infrastructure and the durability characteristics of civil infrastructure in challenging environmental conditions. In addition, this review focuses on the modification of the mechanical properties of structural elements using different methods of installing FRPs, including externally bonded reinforcement (EBR), and their main problem: debonding failure before the ultimate load.
RESUMEN
This study proposes a novel test method and corresponding procedure to evaluate how coconut fibres affect crack propagation rates resulting from plastic shrinkage during the accelerated drying of concrete slabs. The experiment employed concrete plate specimens, which were used to simulate slab structural elements with a surface dimension notably greater than their thickness. These slabs were reinforced with coconut fibre with 0.5%, 0.75%, and 1% fibre content. A wind tunnel was designed to simulate two significant climate parameters (wind speed and air temperature), which could impact the cracking behaviour of surface elements. The proposed wind tunnel allowed air temperature to be controlled alongside wind speed while monitoring moisture loss and the cracking propagation process. During testing, a photographic recording method was used to evaluate cracking behaviour, with the total crack length serving as a parameter to assess the impact of fibre content on the crack propagation of slab surfaces. Additionally, crack depth was measured using ultrasound equipment. The results indicate that the proposed test method was appropriate for future research, allowing for the evaluation of the effect of natural fibres on the plastic shrinkage behaviour of surface elements under controlled environmental conditions. Based on initial studies and the results obtained through the proposed test method, concrete containing 0.75% fibre content exhibited significantly reduced crack propagation on slab surfaces, as well as a reduction in the crack depth caused by plastic shrinkage during the early age of the concrete.