RESUMEN
In order to protect human health and the environment, several regulations have been introduced in recent years to reduce or even eliminate the use of some brominated flame retardants (BFRs) due to their toxicity, persistence and bioaccumulation. Dispersions of these BFRs in polymers are widely used for various applications. In this report, four different brominated molecules, decabromodiphenyl ether (DBDE), hexabromocyclododecane (HBCDD), decabromodiphenyl ethane (DBDPE) and tris(tribromophenoxy)triazine (TTBPT), were dispersed in the solid matrix of an industrial polymer, high impact polystyrene (HIPS). The possibility of degradation of these BFRs within HIPS under UV-visible irradiation in ambient air was investigated. The degradation kinetics of DBDE and HBCDD were followed by Fourier transform infrared spectroscopy (FTIR) and high-resolution two-step laser mass spectrometry (L2MS). The thermal properties of the pristine and irradiated polymer matrix were monitored by thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC), which showed that these properties were globally preserved. Volatile photoproducts from the degradation of DBDE, DBDPE and TTBPT were identified by headspace gas chromatography/mass spectrometry analysis. Under the chosen experimental conditions, BFRs underwent rapid degradation after a few seconds of irradiation, with conversions exceeding 50% for HIPS/DBDE and HIPS/HBCDD systems.
RESUMEN
Recycling of plastic waste from electrical and electronic equipment (EEE), containing brominated flame retardants (BFR) remains difficult due to the increasingly stringent regulations on their handling and recovery. This report deals with photodegradation in a low-pressure reactor applying UV-visible light on Decabromodiphenyl ether (DBDE or BDE-209) randomly dispersed in commercially available Poly(acrylonitrile-butadiene-styrene) (ABS) and Poly(carbonate) (PC). The aim of this study is to investigate the possibility of decomposing a BFR in plastic waste from EEE while maintaining the specifications of the polymeric materials in order to allow for their recycling. The photodegradation of the extracted BFR was monitored using infrared spectroscopy and gas chromatography coupled with mass spectroscopy. DBDE underwent rapid photodegradation during the first minutes of exposure to UV-visible light and reached degradation yields superior to 90% after 15 min of irradiation. The evaluation of polymer properties (ABS and PC) after irradiation revealed superficial crosslinking effects, which were slightly accelerated in the presence of DBDE. However, the use of a low-pressure reactor avoids large photooxidation and allowed to maintain the thermal and structural properties of the virgin polymers.