Electrochemical Impedance as an Assessment Tool for the Investigation of the Physical and Mechanical Properties of Graphene-Based Cementitious Nanocomposites.

This investigation explores the potential of electrochemical impedance spectroscopy (EIS) in evaluating graphene-based cementitious nanocomposites, focusing on their physical and structural properties, i.e., electrical resistivity, porosity, and fracture toughness. EIS was employed to study cement mixtures with varying graphene nanoplatelet (xGnP) concentrations (0.05-0.40% per dry cement weight), whereas flexural tests assessed fracture toughness and porosimetry analyses investigated the structural characteristics. The research demonstrated that the electrical resistivity initially decreased with increasing xGnP content, leveling off at higher concentrations. The inclusion of xGnPs correlated with an increase in the total porosity of the cement mixtures, which was indicated by both EIS and porosimetry measurements. Finally, a linear correlation emerged between fracture toughness and electrical resistivity, contributing also to underscore the use of EIS as a potent non-destructive tool for evaluating the physical and mechanical properties of conductive nano-reinforced cementitious nanocomposites.

Piezoresistive Properties of Natural Hydraulic Lime Binary Pastes with Incorporated Carbon-Based Nanomaterials under Cyclic Compressive Loadings.

Natural Hydraulic Limes (NHL) are extensively used for the restoration of Monuments of Cultural Heritage, often combined with pozzolanic materials, such as natural pozzolans and metakaolin etc. In the present study, five (5) different cases of binary lime-based pastes composed of a specific type of NHL (NHL5) and metakaolin as pozzolanic addition were examined, that were reinforced with carbon nanostructures, namely graphene and carbon nanotubes. For the first time in restoration mortars, the incorporation of carbon nanostructures was investigated, aiming to produce materials with adequate piezoresistive response, so that they have the potential to be exploited for in situ structural health monitoring. The compressive strength, flexural strength, electrical resistance and piezoresistive response of the composite pastes was examined. The results showed that all modified carbon nanostructures lead to a significant reduction in electrical resistance. The pastes reinforced with 2D nanostructures (graphene family) displayed up to 30% increase in compressive strength and the pastes reinforced with 1D nanostructures (carbon nanotubes) displayed enhanced flexural strength (up to 100% increase). Piezoresistivity was attained for almost all investigated pastes, nevertheless the graphene oxide (GO) was considered as optimal reinforcement as the sensing ability of such pastes was found to be almost proportional to the applied compressive load level.

Dispersion of Multi-Walled Carbon Nanotubes into White Cement Mortars: The Effect of Concentration and Surfactants.

Multi-wall carbon nanotubes (MWCNTs) exhibit exceptional mechanical and electrical properties and can be used to improve the mechanical and piezoelectric properties of cement-based materials. In the present study, the effect of different MWCNT concentrations as well as different types of surfactants and a superplasticizer were examined to reinforce, at the nanoscale, a white cement mortar typically used for the restoration of monuments of cultural heritage. It was shown that sodium dodecylbenzenesulfonate (SDBS) and Triton X-100 surfactants slightly decreased the white cement mortars' electrical resistivity (by an average of 10%), however, the mechanical properties were essentially decreased by an average of 60%. The most suitable dispersion agent for the MWCNTs proved to be the superplasticizer Ceresit CC198, and its optimal concentration was investigated for different MWCNT concentrations. Carboxylation of the MWCNT surface with nitric acid did not improve the mechanical performance of the white cement nanocomposites. The parametric experimental study showed that the optimum combination of 0.8 wt% of cement superplasticizer and 0.2 wt% of cement MWCNTs resulted in a 60% decrease in the electrical resistivity; additionally, the flexural and compressive strengths were both increased by approximately 25% and 10%, respectively.

In situcontrol of graphene oxide dispersions with a small impedance sensor.

Carbon-based nanomaterials (CBNs), such as graphene and carbon nanotubes, display advanced physical and chemical properties, which has led to their widespread applications. One of these applications includes the incorporation of CBNs into cementitious materials in the form of aqueous dispersions. The main issue that arises in this context is that currently no established protocol exists as far as characterizing the dispersions. In the present article, an innovative method for quick evaluation and quantification of graphene oxide (GO) dispersions is proposed. The proposed method is electrical impedance spectroscopy (EIS) with an impedance sensor. The novelty lies on the exploitation of a small sensor for on-site (field) direct dielectric measurements with the application of alternating current. Five different concentrations of GO dispersions were studied by applying EIS and for various accumulated ultrasonic energies. The low GO concentration leads to high impedance values due to low formed current network. Two opposing mechanisms were revealed during the accumulation of ultrasonic energy, that are taking place simultaneously: breakage of the agglomerates that facilitates the flow of the electric current due to the formation of a better dispersed network, nevertheless the surface hydrophilic structure of the GO is damaged with the high accumulated ultrasonic energy. The dielectric measurements were exploited to express an appropriate quantitative 'quality index' to facilitate with the dispersion control of the nanostructures. An intermediate concentration of GO is suggested (about 0.15 wt% of the binder materials) to be optimal for the specific engineering application, ultrasonicated at approximately 30 to 65 kJ. The investigated methodology is highly novel and displays a high potential to be applied in-field applications where CBNs must be incorporated in building materials.