RESUMEN
The discharge of synthetic dyes from different industrial sources has become a global issue of concern. Enormous amounts are released into wastewater each year, causing concerns due to the high toxic consequences. Photocatalytic semiconductors appear as a green and sustainable form of remediation. Among them, graphitic carbon nitride (g-C3N4) has been widely studied due to its low cost and ease of fabrication. In this work, the synthesis, characterization, and photocatalytic study over methylene blue of undoped, B/S-doped, and exfoliated heterojunctions of g-C3N4 are presented. The evaluation of the photocatalytic performance showed that exfoliated undoped/S-doped heterojunctions with 25, 50, and 75 mass % of S-doped (g-C3N4) present enhanced activity with an apparent reaction rate constant (kapp) of 1.92 × 10-2 min-1 for the 75% sample. These results are supported by photoluminescence (PL) experiments showing that this heterojunction presents the less probable electron-hole recombination. UV-vis diffuse reflectance and valence band-X-ray photoelectron spectroscopy (VB-XPS) allowed the calculation of the band-gap and the valence band positions, suggesting a band structure diagram describing a type I heterojunction. The photocatalytic activities calculated demonstrate that this property is related to the surface area and porosity of the samples, the semiconductor nature of the g-C3N4 structure, and, in this case, the heterojunction that modifies the band structure. These results are of great importance considering that scarce reports are found concerning exfoliated B/S-doped heterojunctions.
RESUMEN
In situ time-resolved X-ray absorption spectroscopy (XAS) measurements collected at the Pt L3-edge during the synthesis of Pt nanoparticles (NPs) in aqueous solution are reported. A specially designed dispenser-reactor apparatus allowed for monitoring changes in the XAS spectra from the earliest moments of Pt ions in solution until the formation of metallic nanoparticles with a mean diameter of 4.9 ± 1.1â nm. By monitoring the changes in the local chemical environment of the Pt atoms in real time, it was possible to observe that the NPs formation kinetics involved two stages: a reduction-nucleation burst followed by a slow growth and stabilization of NPs. Subsequently, the synthesized Pt NPs were supported on activated carbon and characterized by synchrotron-radiation-excited X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD) and extended X-ray absorption fine structure (EXAFS). The supported Pt NPs remained in the metallic chemical state and with a reduced size, presenting slight lattice parameter contraction in comparison with the bulk Pt values.
RESUMEN
The use of in situ time-resolved dispersive X-ray absorption spectroscopy (DXAS) to monitor the formation of Cu2(OH)3Cl particles in an aqueous solution is reported. The measurements were performed using a dedicated reaction cell, which enabled the evolution of the Cu K-edge X-ray absorption near-edge spectroscopy to be followed during mild chemical synthesis. The formed Cu2(OH)3Cl particles were also characterized by synchrotron-radiation-excited X-ray photoelectron spectroscopy, X-ray diffraction and scanning electron microscopy. The influence of polyvinylpyrrolidone (PVP) on the electronic and structural properties of the formed particles was investigated. The results indicate clearly the formation of Cu2(OH)3Cl, with or without the use of PVP, which presents very similar crystalline structures in the long-range order. However, depending on the reaction, dramatic differences were observed by in situ DXAS in the vicinities of the Cu atoms.