Thrombogenicity of biodegradable metals.

Biodegradable metals offer a promising means to ameliorate many of the long-term risks associated with vascular devices made of conventional biostable stent metals. While numerous biodegradable metal alloys have been developed and characterized in animal models, knowledge of their blood reactivity and thrombogenicity remains unknown. Metal hemocompatibility is particularly valuable because current generation drug-eluting stents pose a significant long-term thrombosis risk. In this study, four pure metals, widely used as degradable base materials (Fe, Zn, Mg, and Mo), and three alloys commonly used in cardiovascular devices [NiTi, CoCr, and stainless steel (SS)] were evaluated. This work examined how each of these metals activate platelets, coagulation factors, and inflammation using in vitro hemocompatibility assays and a clinically relevant ex vivo non-human primate arteriovenous shunt model. Testing found that while all metals promoted a downstream activation of platelets and coagulation in flowing whole blood, platelet and fibrin attachment to Mg was markedly reduced. Additionally, Fe and Mo trended toward higher platelet attachment and contact pathway activation. Overall, the results suggest that Mg may delay clot initiation, but not eliminate clot formation, indicating the importance of understanding thrombosis in Mg alloys that are currently being developed for clinical use as biodegradable stents.

A comparison of primary and passaged chondrocytes for use in engineering the temporomandibular joint.

OBJECTIVE: This study examines the tissue engineering potential of passaged (P3) and primary (P0) articular chondrocytes (ACs) and costal chondrocytes (CCs) from skeletally mature goats for use in the temporomandibular joint (TMJ). DESIGN: These four cell types were assembled into scaffoldless tissue engineered constructs and cultured for 4 wks. The constructs were then tested for cell, collagen, and glycosaminoglycan (GAG) content with biochemical assays, and collagen types I and II with enzyme-linked immunosorbent assays. Constructs were also tested under tension and compression to determine biomechanical properties. RESULTS: Both primary and passaged CC constructs had greater GAG/wet weight than AC constructs. Primary AC constructs had significantly less total collagen and contained no collagen type I. AC P3 constructs had the largest collagen I/collagen II ratio, which was also greater in passaged CC constructs relative to primary groups. Primary AC constructs were not mechanically testable, whereas passaged AC and CC constructs had significantly greater tensile properties than primary CC constructs. CONCLUSIONS: Primary CCs are considerably better than primary ACs and have potential use in tissue engineering when larger quantities of collagen type II are desired. The poor performance of the ACs, in this study, which contradicts the results seen with previous studies using immature bovine ACs, may thus be attributed to the animals' maturity. However, CC P3 cells appear particularly well suited for tissue engineering fibrocartilage of the TMJ due to the high quantity of collagen and GAG, and tensile and compressive mechanical properties.