Enhancing the Performance of Organic Phototransistors Based on Oriented Floating Films of P3HT Assisted by Al-Island Deposition.

The fabrication of high-performance Organic Phototransistors (OPTs) by depositing Al-islands atop Poly(3-hexylthiophene) (P3HT) thin film coated using the unidirectional floating-film transfer method (UFTM) has been realized. Further, the effect of Al-island thickness on the OPTs' performance has been intensively investigated using X-ray photoelectron spectroscopy, X-ray Diffraction, Atomic force microscopy and UV-Vis spectroscopy analysis. Under the optimized conditions, OPTs' mobility and on-off ratio were found to be 2 × 10-2 cm2 V-1 s-1 and 3 × 104, respectively. Further, the device exhibited high photosensitivity of 105, responsivity of 339 A/W, detectivity of 3 × 1014 Jones, and external quantum efficiency of 7.8 × 103% when illuminated with a 525 nm LED laser (0.3 mW/cm2).

Optimization of Cellulose Nanofiber Loading and Processing Conditions during Melt Extrusion of Poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) Bionanocomposites.

This present study optimized the cellulose nanofiber (CNF) loading and melt processing conditions of poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) P(HB-co-11% HHx) bionanocomposite fabrication in twin screw extruder by using the response surface methodology (RSM). A face-centered central composite design (CCD) was applied to statistically specify the important parameters, namely CNF loading (1-9 wt.%), rotational speed (20-60 rpm), and temperature (135-175 °C), on the mechanical properties of the P(HB-co-11% HHx) bionanocomposites. The developed model reveals that CNF loading and temperature were the dominating parameters that enhanced the mechanical properties of the P(HB-co-11% HHx)/CNF bionanocomposites. The optimal CNF loading, rotational speed, and temperature for P(HB-co-11% HHx) bionanocomposite fabrication were 1.5 wt.%, 20 rpm, and 160 °C, respectively. The predicted tensile strength, flexural strength, and flexural modulus for these optimum conditions were 22.96 MPa, 33.91 MPa, and 1.02 GPa, respectively, with maximum desirability of 0.929. P(HB-co-11% HHx)/CNF bionanocomposites exhibited improved tensile strength, flexural strength, and modulus by 17, 6, and 20%, respectively, as compared to the neat P(HB-co-11% HHx). While the crystallinity of P(HB-co-11% HHx)/CNF bionanocomposites increased by 17% under the optimal fabrication conditions, the thermal stability of the P(HB-co-11% HHx)/CNF bionanocomposites was not significantly different from neat P(HB-co-11% HHx).

Investigation on the Redox Properties of a Novel Cu-Based Pr-Modified Oxygen Carrier for Chemical Looping Combustion.

CO2 levels in the atmosphere are growing as a result of the burning of fossil fuels to meet energy demands. The introduction of chemical looping combustion (CLC) as an alternative to traditional combustion by transporting oxygen emphasizes the need to develop greener and more economical energy systems. Metal oxide, also defined as an oxygen carrier (OC), transports oxygen from the air to the fuel. Several attempts are being made to develop an OC with a reasonable material cost for superior fuel conversion and high oxygen transport capacity (OTC). This study aims to synthesize a potential OC using the wet impregnation method for the CLC process. Thermogravimetric analysis (TGA) was used to determine the cyclic redox properties using 5% CH4/N2 and air as reducing and oxidizing gases, respectively. The 10CuPA-based OC retained a high OTC of about 0.0267 mg O2/mg of OC for 10 cycles that was higher than 10CuA-based OC. Furthermore, the oxygen transfer rate for 10CuPA-based OC was relatively higher compared to 10CuA-based OC over 10 cycles. In comparison to 10CuA-based OC, the 10CuPA-based OC presented a steady X-ray diffraction (XRD) pattern after 10 redox cycles, implying that the phase was stably restored due to praseodymium-modified γ alumina support.

Implication of Molecular Weight on Optical and Charge Transport Anisotropy in PQT-C12 Films Fabricated by Dynamic FTM.

Large area (>20 cm × 2 cm)-oriented thin films of PQT-C12 with varying molecular weight and polydispersity index (PDI) were fabricated by the ribbon-shaped floating film transfer method aiming toward their application as an active semiconductor element of organic field effect transistors (OFETs). Investigation on the influence of the molecular weight and PDI upon the extent of molecular alignment and anisotropic charge transport was systematically carried out. It has been demonstrated that high molecular weight in combination with low PDI not only leads to a very high optical anisotropy >10 but also high charge carrier anisotropy with a hole mobility of about 0.07 cm2/V·s for OFETs using parallel-oriented PQT-C12 thin films. Such a structure-property correlation is highly beneficial for the development of high performance organic electronic devices by synergistic and amicable tuning of the optoelectronic anisotropies and polymer synthetic variables.

Recovery and purification of intracellular polyhydroxyalkanoates from recombinant Cupriavidus necator using water and ethanol.

A new halogen-free and environmental-friendly method using water and ethanol is developed as an alternative for the recovery of polyhydroxyalkanoates (PHA) from recombinant Cupriavidus necator in comparison to the established chloroform extraction method. After optimisation, our results showed that the halogen-free method produced a PHA with 81% purity and 96% recovery yield, in comparison to the chloroform extraction system which resulted in a highly pure PHA with 95% yield. Although the purity of the PHA using the new method is lower, the molecular weight of the extracted PHA is not compromised. This new method can be further developed as an alternative and more environmental-friendly method for industrial application.