RESUMEN
Powder injection molding is an established, cost effective and often near-net-shape mass production process for metal or ceramic parts with complex geometries. This paper deals with the extension of the powder injection molding process chain towards the usage of a commercially available borosilicate glass and the realization of glass compounds with huge densities. The whole process chain consists of the individual steps of compounding, molding, debinding, and sintering. The first part, namely, the search for a suitable feedstock composition with a very high solid load and reliable molding properties, is mandatory for the successful manufacture of a dense glass part. The most prominent feature is the binder composition and the related comprehensive rheological characterization. In this work, a binder system consisting of polyethylene glycol and polymethylmethacrylate with stearic acid as a surfactant was selected and its suitability for glass injection molding was evaluated. The influence of all feedstock components on processing and of the process steps on the final sintered part was investigated for sintered glass parts with densities around 99% of the theoretical value.
RESUMEN
This work presents a comprehensive investigation into the optimization of critical process parameters associated with metal fused filament fabrication (Metal-FFF) for the production of copper-based components. The study focused on three different commercial and one self-manufactured filament, each with unique chemical compositions. These filaments were systematically optimized and the density was characterized for all processing steps, as well as the electrical conductivity on the specimen scale. Remarkably, two of the studied filaments exhibited exceptional properties after sintering with forming gas (up to 94% density and 55.75 MS/m electrical conductivity), approaching the properties measured for established manufacturing methods like metal injection molding. Finally, the research was extended to component-scale applications, demonstrating the successful fabrication of inductors with integrated cooling channels. These components exhibited water tightness and were used in induction hardening experiments, validating the practical utility of the optimized Metal-FFF process. In summary, the results show great promise in advancing the utilization of Metal-FFF in industrial contexts, particularly in the production of high-performance copper components.
RESUMEN
High-performance thermoplastics like polyetheretherketone (PEEK), with their outstanding thermal stability, mechanical properties and chemical stability, have great potential for various structural applications. Combining with additive manufacturing methods extends further PEEK usage, e.g., as a mold insert material in polymer melt processing like injection molding. Mold inserts must possess a certain mechanical stability, a low surface roughness as well as a good thermal conductivity for the temperature control during the molding process. With this in mind, the commercially available high-performance thermoplastic PEEK was doped with small amounts of carbon nanotubes (CNT, 6 wt%) and copper particles (10 wt%) targeting enhanced thermomechanical properties and a higher thermal conductivity. The composites were realized by a commercial combined compounder and filament maker for the usage in a material extrusion (MEX)-based 3D-printer following the fused filament fabrication (FFF) principle. Commercial filaments made from PEEK and carbon fiber reinforced PEEK were used as reference systems. The impact of the filler and the MEX printing conditions like printing temperature, printing speed and infill orientation on the PEEK properties were characterized comprehensively by tensile testing, fracture imaging and surface roughness measurements. In addition, the thermal conductivity was determined by the laser-flash method in combination with differential scanning calorimetry and Archimedes density measurement. The addition of fillers did not alter the measured tensile strength in comparison to pure PEEK significantly. The fracture images showed a good printing quality without the MEX-typical voids between and within the deposited layers. Higher printing temperatures caused a reduction of the surface roughness and, in some cases, an enhanced ductile behavior. The thermal conductivity could be increased by the addition of the CNTs. Following the given results, the most critical process step is the compounding procedure, because for a reliable process-parameter-property relationship, a homogeneous particle distribution in the polymer matrix yielding a reliable filament quality is essential.
RESUMEN
In this work, a process chain for the realization of dense Ti6Al4V parts via different material extrusion methods will be introduced applying eco-friendly partially water-soluble binder systems. In continuation of earlier research, polyethylene glycol (PEG) as a low molecular weight binder component was combined either with poly(vinylbutyral) (PVB) or with poly(methylmethacrylat) (PMMA) as a high molecular weight polymer and investigated with respect to their usability in FFF and FFD. The additional investigation of different surfactants' impact on the rheological behaviour applying shear and oscillation rheology allowed for a final solid Ti6Al4V content of 60 vol%, which is sufficient to achieve after printing, debinding and thermal densification parts with densities better than 99% of the theoretical value. The requirements for usage in medical applications according to ASTM F2885-17 can be fulfilled depending on the processing conditions.
RESUMEN
In this work, a holistic approach for the fabrication of dense Ti6Al4V parts via material extrusion methods (MEX), such as fused filament fabrication (FFF) or fused feedstock deposition (FFD), will be presented. With respect to the requirements of the printing process, a comprehensive investigation of the feedstock development will be described. This covers mainly the amount ratio variation of the main binder components LDPE (low-density polyethylene), HDPE (high-density polyethylene), and wax, characterized by shear and oscillation rheology. Solid content of 60 vol% allowed the 3D printing of even more complex small parts in a reproducible manner. In some cases, the pellet-based FFD seems to be superior to the established FFF. After sintering, a density of 96.6% of theory could be achieved, an additional hot isostatic pressing delivered density values better than 99% of theory. The requirements (mechanical properties, carbon, and oxygen content) for the usage of medical implants (following ASTM F2885-17) were partially fulfilled or shortly missed.