RESUMEN
ZnO/TiO2 anchored on a reduced graphene oxide (rGO) ternary nanocomposite heterojunction was synthesized via the multi-step method including hydrothermal, solvothermal and sol-gel methods. XRD, Raman, FESEM, EDX, Dot Mapping EDS, BET, FTIR, UV-VIS, TGA, and EIS techniques were utilized for characterizing as-synthesized catalysts. The XRD and Raman data proved the formation of anatase phase TiO2 and wurtzite phase ZnO in the prepared samples. Further, the UV-Vis spectrum confirmed that the band gap value of ZnO/TiO2 diminished on introduction of graphene oxide. Photocatalytic performance of the fabricated catalysts was investigated by decontamination of phenol in aqueous solutions. The effect of different operational factors such as pH, catalyst dosage, phenol concentration, and light illumination was investigated to find the optimum decontamination conditions. According to the results, complete degradation of phenol was achieved at pH = 4, catalyst dosage of 0.6 g L-1, light intensity of 150 W, and phenol initial concentration of 60 ppm at 160 min under visible light illumination. With the addition of graphene oxide to the composite, a significant increase was detected in the photocatalytic performance due to the higher available surface area and lower electron/hole recombination rate. In addition, the scavenging experiments revealed that the ·OH is responsible for the degradation of phenol during the reaction. The degradation mechanism, economic performance, mineralization, and recyclability were also investigated. Kinetic studies confirmed that photocatalytic degradation process followed the pseudo-first-order kinetic model. A case of real wastewater treatment was used to examine the performance of the catalyst for real case studies.
RESUMEN
This research is about a novel ultrasound assisted method for synthesis of nano zero valent iron particles (NZVI). The materials were characterized using TEM, FESEM, XRD, BET and acoustic PSA. The effect of ultrasonic power, precursor/reductant concentration (NaBH4, FeSO4·7H2O) and delivery rate of NaBH4 on NZVI characteristics were investigated. Under high ultrasonic power the morphology of nano particles changed from spherical type to plate and needle type. Also, when high precursor/reductant and high ultrasonic power was used the particle size of NZVI decreased. The surface area of NZVI particles synthesized by ultrasonic method was increased when compared by the other method. From the XRD patterns it was found also the crystallinity of particles was poor.
RESUMEN
In this study, chitosan and nano-chitosan were used as flocculants agents for harvesting microalga Nannochloropsis sp. chitosan was modified to nano-chitosan by crosslinking with sodium tripolyphosphate. The effects of type and dosage of flocculants and the pH of the culture were investigated on biomass recovery. Optimum dosages for both bio-flocculants were found. The results showed that the dosage of flocculant consumption decreases by 40% and biomass recovery increases by 9% when nano-chitosan instead of chitosan is used as flocculant agent. Also, the recycled water from the harvesting process was reused which increases the growth of microalgae by about 7%. Finally, the cost analysis of harvesting process showed the feasibility of using nano-chitosan as flocculation agent.