Correlation of Fracture Resistance of Dental Implants and Bite Force in Dogs described in the literature: An In Vitro Study.

Dental implants are not routinely used for rehabilitation in veterinary dentistry. For some veterinarians, further studies are necessary to be considered for clinical use in animals. The objective of the present in vitro study was to evaluate static fatigue of dental implants and to correlate that with the bite strength of dogs described in the literature. Sixty implants and abutments were used with the smallest diameter of each brand of implant utilized in the study. Three groups (n = 20) were created on the basis of the implant diameter, all with external hex connector: 3.30 mm (group 1), 4.0 mm (group 2) and 5.0 mm (group 3). All groups were subjected to quasi-static loading at 30° to the implant's long axis in a universal machine (model AME-5 kN). The mean fracture strength for group 1 was 964 ± 187 N, for group 2 was 1618 ± 149 N and for group 3 was 2595 ± 161 N. Significant differences between the groups with respect to resistance after the load applications were observed (P < .05). The diameter of implants affects the resistance to external forces during the application of non-axial strength (off-axis loading) and must be considered during the planning of rehabilitation to avoid problems.

Can changes in implant macrogeometry accelerate the osseointegration process?: An in vivo experimental biomechanical and histological evaluations.

OBJECTIVES: The propose was to compare this new implant macrogeometry with a control implant with a conventional macrogeometry. MATERIALS AND METHODS: Eighty-six conical implants were divided in two groups (n = 43 per group): group control (group CON) that were used conical implants with a conventional macrogeometry and, group test (group TEST) that were used implants with the new macrogeometry. The new implant macrogeometry show several circular healing cambers between the threads, distributed in the implant body. Three implants of each group were used to scanning electronic microscopy (SEM) analysis and, other eighty samples (n = 40 per group) were inserted the tibia of ten rabbit (n = 2 per tibia), determined by randomization. The animals were sacrificed (n = 5 per time) at 3-weeks (Time 1) and at 4-weeks after the implantations (Time 2). The biomechanical evaluation proposed was the measurement of the implant stability quotient (ISQ) and the removal torque values (RTv). The microscopical analysis was a histomorphometric measurement of the bone to implant contact (%BIC) and the SEM evaluation of the bone adhered on the removed implants. RESULTS: The results showed that the implants of the group TEST produced a significant enhancement in the osseointegration in comparison with the group CON. The ISQ and RTv tests showed superior values for the group TEST in the both measured times (3- and 4-weeks), with significant differences (p < 0.05). More residual bone in quantity and quality was observed in the samples of the group TEST on the surface of the removed implants. Moreover, the %BIC demonstrated an important increasing for the group TEST in both times, with statistical differences (in Time 1 p = 0.0103 and in Time 2 p < 0.0003). CONCLUSIONS: Then, we can conclude that the alterations in the implant macrogeometry promote several benefits on the osseointegration process.

Effect of Different Morphology of Titanium Surface on the Bone Healing in Defects Filled Only with Blood Clot: A New Animal Study Design.

Background: The objective of the present histologic animal study was to analyze whether roughness of the titanium surface can influence and/or stimulate the bone growth in defects filled with the blood using a rabbit tibia model. Materials and Methods: Forty sets (implant and abutment), dental implant (3.5 mm in diameter and 7 mm in length) plus healing abutment (2.5 mm in diameter), were inserted in the tibiae of 10 rabbits. Moreover, twenty titanium discs were prepared. The abutment and discs were treated by 4 different methods and divided into 4 groups: (group A) machined abutments (smooth); (group B) double acid etching treatment; (group C) treatment with blasting with particles of aluminum oxide blasted plus acid conditioning; (group D) treatment with thorough blasting with particles of titanium oxide plus acid conditioning. The discs were used to characterize the surfaces by a profilometer and scanning electronic microscopy. Results: After 8 weeks, the new bone formation around the sets of the samples was analyzed qualitatively and quantitatively in relation to bone height from the base of the implant and presence of osteocytes. Group C (1.50±0.20 mm) and group D (1.62±0.18 mm) showed bone growth on the abutment with higher values compared to group A (0.94±0.30 mm) and group B (1.19±0.23 mm), with significant difference between the groups (P < 0.05). In addition, osteocyte presence was higher in groups with surface treatment related to machined (P < 0.05). Conclusions: Within the limitations of the present study, it was possible to observe that there is a direct relationship between the roughness present on the titanium surface and the stimulus for bone formation, since the presence of larger amounts of osteocytes on SLA surfaces evidenced this fact. Furthermore, the increased formation of bone tissue in height demonstrates that there is an important difference between the physical and chemical methods used for surface treatment.