Biosensor based on laccase immobilized on plasma polymerized allylamine/carbon electrode.

In this work, a simple and rapid method was used to functionalize carbon electrode in order to efficiently immobilize laccase for biosensor application. A stable allylamine coating was deposited using a low pressure inductively excited RF tubular plasma reactor under mild plasma conditions (low plasma power (10 W), few minutes) to generate high density amine groups (N/C ratio up to 0.18) on rough carbon surface electrodes. The longer was the allylamine plasma deposition time; the better was the surface coverage. Laccase from Trametes versicolor was physisorbed and covalently bound to these allylamine modified carbon surfaces. The laccase activities and current outputs measured in the presence of 2,2'-azinobis-(3-ethylbenzothiazole-6-sulfonic acid) (ABTS) showed that the best efficiency was obtained for electrode plasma coated during 30 min. They showed also that for all the tested electrodes, the activities and current outputs of the covalently immobilized laccases were twice higher than the physically adsorbed ones. The sensitivity of these biocompatible bioelectrodes was evaluated by measuring their catalytic efficiency for oxygen reduction in the presence of ABTS as non-phenolic redox substrate and 2,6-dimethoxyphenol (DMP) as phenolic one. Sensitivities of around 4.8 µA mg(-1)L and 2.7 µA mg(-1)L were attained for ABTS and DMP respectively. An excellent stability of this laccase biosensor was observed for over 6 months.

Plasma functionalized carbon electrode for laccase-catalyzed oxygen reduction by direct electron transfer.

For the first time, a fast and versatile technique, an atmospheric pressure plasma jet (APPJ), has been used to functionalise graphite carbon electrodes for biofuel cell applications. The bioelectrode was functionalized by an atmospheric pressure plasma jet (APPJ) system using air, oxygen (O2) and nitrogen (N2) plasmas applied for only a few seconds. XPS analysis showed that carboxylic groups were created on the carbon substrates using both air and O2 plasmas, while mainly carbonyl and amine/amide functionalities were generated using N2 plasmas. A purified laccase from Trametes versicolor was both adsorbed and covalently bound (NHS/EDC method) to the plasma modified carbon. Higher laccase activity was obtained for the covalently grafted laccase compared to the physically adsorbed one: 13.2 (±2) 10(-3)U of laccase on air treated graphite and two-fold less (5.3 (±1.1) 10(-3)U) were obtained on N2 plasma treated surfaces (1mM ABTS as a substrate, 30°C, pH=3.0), one unit (U) being the quantity of ABTS (µmole) oxidized by laccase per minute. Dioxygen reduction was performed by direct electron transfer (DET). The highest current density, 108µA/cm(2) (at 0.2V (vs. SCE), pH 4.2, room temperature), was recorded for covalently immobilized laccase on N2 plasma treated surfaces (geometric surface=0.38cm(2)). This could be explained by the fact that the highly conductive graphite structure was retained in the case of this surface treatment and could also suggest a preferential orientation of the T1 Cu center of the laccase toward the surface of the N2 plasma treated electrode.

Effect of surface wettability and topography on the adhesion of osteosarcoma cells on plasma-modified polystyrene.

Biomaterials interact with the biological environment at their surface, making accurate biophysical characterization of the surface crucially important for understanding subsequent biological effects. In this study, the surface of polystyrene (PS) was systematically altered in order to determine the effect of plasma treatment and surface roughness on cell adhesion and spreading. Surfaces with water contact angle from hydrophilic (12°) to superhydrophobic (155°) were obtained through a combination of modifying surface roughness (R (a)), the deposition of siloxane coatings and the fluorination of the PS surface. R (a) values in the range of 19-2365 nm were obtained by grinding the PS surface. The nanometer-thick siloxane coatings were deposited using an atmospheric pressure plasma system, while the fluorination of the PS was carried out using a low-pressure radio frequency (RF) plasma. The siloxane coatings were obtained using a liquid poly(dimethylsiloxane) precursor that was nebulized into helium or helium/oxygen plasmas. Water contact angles in the range of 12-122° were obtained with these coatings. Cell adhesion studies were carried out using human MG63 osteosarcoma cells. It was observed that higher polymer surface roughness enhanced cell adhesion, but had a negative effect on cell spreading. Optimum cell adhesion was observed at ∼64° for the siloxane coatings, with a decrease in adhesion observed for the more hydrophilic and hydrophobic coatings. This decrease in cell adhesion with an increase in hydrophobicity was also observed for the fluorinated PS surfaces with water contact angles in the range of 110-155°.