One-Pot Synthesis of Pd Nanoparticles Supported on Carbide-Derived Carbon for Oxygen Reduction Reaction.

We explored two methods for synthesizing Pd nanoparticles using three different carbide-derived carbon (CDC) support materials, one of which was nitrogen-doped. These materials were studied for oxygen reduction reaction (ORR) in 0.1 M KOH solution, and the resulting CDC/Pd catalysts were characterized using TEM, XRD, and XPS. The citrate method and the polyol method using polyvinylpyrrolidone (PVP) as a capping agent were employed to elucidate the impact of the support material on the final catalyst. The N-doping of the CDC material resulted in smaller Pd nanoparticles, but only in the case of the citrate method. This suggests that the influence of support is weaker when using the polyol method. The citrate method with CDC1, which is predominantly microporous, led to a higher degree of agglomeration and formation of larger particles in comparison to supports, which possessed a higher degree of mesoporosity. We achieved smaller Pd particle sizes using citrate and NaBH4 compared to the ethylene glycol PVP method. Pd deposited on CDC2 and CDC3 supports showed similar specific activity (SA), suggesting that the N-doping did not significantly influence the ORR process. The highest SA value was observed for CDC1/Pd_Cit, which could be attributed to the formation of larger Pd particles and agglomerates.

Iron Triad-Based Bimetallic M-N-C Nanomaterials as Highly Active Bifunctional Oxygen Electrocatalysts.

The use of precious metal electrocatalysts in clean electrochemical energy conversion and storage applications is widespread, but the sustainability of these materials, in terms of their availability and cost, is constrained. In this research, iron triad-based bimetallic nitrogen-doped carbon (M-N-C) materials were investigated as potential bifunctional electrocatalysts for the oxygen reduction reaction (ORR) and oxygen evolution reaction (OER). The synthesis of bimetallic FeCo-N-C, CoNi-N-C, and FeNi-N-C catalysts involved a precisely optimized carbonization process of their respective metal-organic precursors. Comprehensive structural analysis was undertaken to elucidate the morphology of the prepared M-N-C materials, while their electrocatalytic performance was assessed through cyclic voltammetry and rotating disk electrode measurements in a 0.1 M KOH solution. All bimetallic catalyst materials demonstrated impressive bifunctional electrocatalytic performance in both the ORR and the OER. However, the FeNi-N-C catalyst proved notably more stable, particularly in the OER conditions. Employed as a bifunctional catalyst for ORR/OER within a customized zinc-air battery, FeNi-N-C exhibited a remarkable discharge-charge voltage gap of only 0.86 V, alongside a peak power density of 60 mW cm-2. The outstanding stability of FeNi-N-C, operational for about 55 h at 2 mA cm-2, highlights its robustness for prolonged application.