Influence of different surface treatments on push-out bond strengths of fiber-reinforced posts luted with dual-cure resin cement.

OBJECTIVES: The objective was to evaluate whether fiber postsurface conditioning with air abrasion or erbium:yttrium-aluminum-garnet (Er:YAG) laser would influence the bond strength of dual-cure resin cement to the fiber-reinforced (FRC) posts. MATERIALS AND METHODS: Twenty-one FRC posts were divided into three groups according to surface treatment methods as follows: An untreated control group air abrasion with Al2O3group, and Er:YAG laser treated group with 150 mJ parameter. Fiber posts were then built up to dual-cure resin cement. Eighteen specimens were set and sectioned perpendicularly along the long axis of the post using a saw. Two disks (thickness of 2 mm) were obtained from each specimen (n = 12). Remaining three posts were stored for scanning electron microscopic evaluation. Push out test was performed on the each specimen and the values were recorded as MPa. The data were analyzed using one-way analysis of variance and Tukey post-hoc tests (P < 0.05). RESULTS: The bond strength values for the groups were as follows: Control (15, 28 MPa), air abrasion group (19, 73 MPa), and Er:YAG group (17, 84 MPa). Air abrasion affected the bond strength significantly (P < 0.05). CONCLUSION: Air abrasion attained higher bond strengths when FRC posts were luted to dual-cure resin cement. Additional studies should be designed with different types and parameters of laser devices to understand the effect of these devices on bond strength.

Effectiveness of laser-assisted irrigation and passive ultrasonic irrigation techniques on smear layer removal in middle and apical thirds.

The purpose of this study was to investigate the evaluation of laser-assisted irrigation (LAI) on the removal of the smear layer as compared to passive ultrasonic irrigation (PUI). Forty-eight single-rooted, upper-central incisor teeth were selected and prepared with ProTaper rotary instruments up to size #40 (F4) at the working lengths. Specimens were divided into four groups, as follows: (a) PUI with 5 mL of 2.5% NaOCl for 60 s; (b) PUI with 2.5 mL of 17% EDTA and 2.5 mL of 2.5% NaOCl each for 30 s; (c) LAI with 5 mL of 2.5% NaOCl for 60 s; and (d) LAI with 2.5 mL of 17% EDTA and 2.5 mL of 2.5% NaOCl each for 30 s. In the PUI groups, the ultrasonically activated file was inserted 1 mm short of the working length, but in the LAI groups, the fiber tip was applied into the pulp chamber. LAI in the pulp chamber with the combination of 17% EDTA and 2.5% NaOCl removed more of the smear layer than the other groups (p < 0.018). LAI in the pulp chamber with the combination of 2.5% NaOCl and 17% EDTA better removed the smear layer than LAI applied similarly but without EDTA or PUI with the same NaOCl and EDTA combinations using an ultrasonically activated file inserted 1 mm short of the working length.

Assessment of root surfaces of apicected teeth: a scanning electron microscopy evaluation.

OBJECTIVES: The aim of this study was to determine the apical surface characteristics and presence of dental cracks in single-rooted premolars, resected 3.0 mm from the root apex, using the Er: YAG laser, tungsten carbide bur, and diamond-coated tip, by scanning electron microscopy (SEM). EXPERIMENTAL DESIGN: Thirty single-rooted premolar teeth were collected. The instrumented and obturated teeth were divided into three groups according to the root resection method (2.94 µm, 100 mj, 20-Hz Er: YAG laser, plain tapered fissure tungsten carbide bur at a low speed of 40,000 rpm, or a diamond-coated SG6D tip coupled to the handpiece of a conventional ultrasound device). The specimens were prepared for SEM and analyzed by the Kruskal-Wallis and Mann-Whitney statistical tests. RESULTS: The SEM images showed that tungsten carbide burs produced significantly smoother resected root surfaces than the diamond-coated tip. There was no statistically significant difference between the Er: YAG and tungsten carbide bur groups. The analysis of scores obtained for the cut quality by the Kruskal-Wallis test revealed no significant differences among the groups. In our study, five teeth had no cracks after the apical resection. The mean number of cracks per tooth was 3.5 ± 1.780 (Er: YAG laser group), 2.5 ± 1.716 (tungsten carbide bur group), and 4.5 ± 2.593 (diamond-coated tip group). CONCLUSIONS: Under the tested conditions smoother surfaces were observed in the groups treated with the tungsten carbide bur and Er: YAG laser when compared with the diamond-coated tips.

Weight of apically extruded debris following use of two canal instrumentation techniques and two designs of irrigation needles.

AIM: To compare the weight of apically extruded debris associated with canal shaping using K-files, and the Revo-S system using two different needle tips, open-ended and side-vented. METHODOLOGY: Forty freshly extracted mandibular premolar teeth were divided into four groups as follows; Group 1a: Hand instrumentation of root canal with open-ended needle used to provide irrigation, Group 1b: Hand instrumentation with a two side-port needle, Group 2a: Revo-S preparation with open-ended needle, Group 2b: Revo-S preparation with a two side-port needle. One Eppendorf tube for each tooth was weighed with a 0.0001 electronic weighing machine before instrumentation procedures. During instrumentation, irrigation was performed after every instrument with 1 mL distilled water. On completion of the preparation, teeth were removed from the Eppendorf tubes. All of the tubes were incubated at 37 °C for 15 days, to evaporate the irrigant. After the incubation period, tubes were weighed again. The difference between pre-and post-debris weights was calculated, and statistical evaluation was performed using analysis of variance at 0.05 level of significance. RESULTS: No statistically significant difference was observed between K-files and the RevoS system. A significant difference was observed between needles (P < 0.05). Open-ended needles were associated with significantly more debris than side-vented needles (P < 0.05). CONCLUSIONS: Both hand and rotary canal instrumentation resulted in extrusion of debris beyond the apical foramen. No significant difference was observed between K-files and Revo-S system. Open-ended needles were associated with significantly more extruded debris than two side-port needles.