One-Pot Direct Mechanochemical Silicon Replacement of Sodium Fluorosilicate into Sodium Fluorozirconate and Functionalization of Graphite for Enhanced Sodium-Ion Storage.

Efficient sodium ion storage in graphite is as yet unattainable, because of the thermodynamic instability of sodium ion intercalates-graphite compounds. In this work, sodium fluorozirconate (Na3ZrF7, SFZ) functionalized graphite (SFZ-G) is designed and prepared by the in situ mechanochemical silicon (Si) replacement of sodium fluorosilicate (Na2SiF6, SFS) and functionalization of graphite at the same time. During the mechanochemical process, the atomic Si in SFS is directly replaced by atomic zirconium (Zr) from the zirconium oxide (ZrO2) balls and container in the presence of graphite, forming SFZ-G. The resulting SFZ-G, working as an anode material for sodium ion storage, shows a significantly enhanced capacity of 418.7 mAh g-1 at 0.1 C-rate, compared to pristine graphite (35 mAh g-1) and simply ball-milled graphite (BM-G, 200 mAh g-1). In addition, the SFZ-G exhibits stable sodium-ion storage performance with 86% of its initial capacity retention after 1000 cycles at 2.0 C-rate.

Direct Electroplating Ruthenium Precursor on the Surface Oxidized Nickel Foam for Efficient and Stable Bifunctional Alkaline Water Electrolysis.

Water electrolysis to produce hydrogen (H2) using renewable energy is one of the most promising candidates for realizing carbon neutrality, but its reaction kinetics is hindered by sluggish anodic oxygen evolution reaction (OER). Ruthenium (Ru) in its high-valence state (oxide) provides one of the most active OER sites and is less costly, but thermodynamically unstable. The strong interaction between Ru nanoparticles (NPs) and nickel hydroxide (Ni(OH)2) is leveraged to directly form Ru-Ni(OH)2 on the surface of a porous nickel foam (NF) electrode via spontaneous galvanic replacement reaction. The formation of Ru─O─Ni bonds at the interface of the Ru NPs and Ni(OH)2 (Ru-Ni(OH)2) on the surface oxidized NF significantly enhance stability of the Ru-Ni(OH)2/NF electrode. In addition to OER, the catalyst is active enough for the hydrogen evolution reaction (HER). As a result, it is able to deliver overpotentials of 228 and 15 mV to reach 10 mA cm-2 for OER and HER, respectively. An industry-scale evaluation using Ru-Ni(OH)2/NF as both OER and HER electrodes demonstrates a high current density of 1500 mA cm-2 (OER: 410 mV; HER: 240 mV), surpassing commercial RuO2 (OER: 600 mV) and Pt/C based performance (HER: 265 mV).