In this work, atomic cobalt (Co) incorporation into the Pd2Ge intermetallic lattice facilitates operando generation of a thin layer of CoO over Co-substituted Pd2Ge, with Co in the CoO surface layer functioning as single metal sites. Hence the catalyst has been titled Co1-CoO-Pd2Ge. High-resolution transmission electron microscopy, X-ray photoelectron spectroscopy, and X-ray absorption spectroscopy confirm the existence of CoO, with some of the Co bonded to Ge by substitution of Pd sites in the Pd2Ge lattice. The role of the CoO layer in the oxygen evolution reaction (OER) has been verified by its selective removal using argon sputtering and conducting the OER on the etched catalyst. In situ X-ray absorption near-edge structure and extended X-ray absorption fine structure spectroscopy demonstrate that CoO gets transformed to CoOOH (Co3+) in operando condition with faster charge transfer through Pd atoms in the core Pd2Ge lattice. In situ Raman spectroscopy depicts the emergence of a CoOOH phase on applying potential and shows that the phase is stable with increasing potential and time without getting converted to CoO2. Density functional theory calculations indicate that the Pd2Ge lattice induces distortion in the CoO phase and generates unpaired spins in a nonmagnetic CoOOH system resulting in an increase in the OER activity and durability. The existence of spin density even after electrocatalysis is verified from electron paramagnetic resonance spectroscopy. We have thus successfully synthesized intermetallic supported CoO during synthesis and rigorously verified the role played by an intermetallic Pd2Ge core in enhancing charge transfer, generating spin density, improving electrochemical durability, and imparting mechanical stability to a thin CoOOH overlayer. Differential electrochemical mass spectrometry has been explored to visualize the instantaneous generation of oxygen gas during the onset of the reaction.
RESUMEN
The development of robust electrocatalysts with low platinum content for acidic hydrogen evolution reaction (HER) is paramount for large scale commercialization of proton exchange membrane electrolyzers. Herein, a simple strategy is reported to synthesize a well anchored, low Pt containing Vulcan carbon catalyst using ZnO as a sacrificial template. Pt containing ZnO (PZ) is prepared by a simultaneous borohydride reduction. PZ is then loaded onto Vulcan carbon to produce a very low Pt content electrocatalyst, PZ@VC. PZ@VC with 2 wt.% Pt shows excellent performance for acidic HER in comparison to the commercial Pt/C (20 wt.%) catalyst. PZ@VC with a very low Pt loading shows significantly low η10 and η100 values (15 and 46 mV, respectively). PZ@VC on coating with Nafion (PZ@VC-N) shows further improvement in its performance (η10 of 7 mV, η100 of 28 mV) with ≈300 h of stability (≈10 mA cm-2 ) with only 4 µgPt cm-2 . PZ@VC-N shows a record high mass activity of 71 A mgPt -1 (32 times larger than Pt/C (20 wt.%) at 50 mV of overpotential. Post reaction characterizations reveal Pt nanoparticles are embedded onto VC with no traces of zinc, suggestive of a strong metal-support interaction leading to this high stability at low Pt loading.
RESUMEN
The scientific community has found immense difficulty to focus on the generation of chiral intermetallics compared to the chiral molecular structure, probably due to the technical difficulty in producing them as no general controlled protocol is available. Herein, using a conventional metal flux technique, we have discovered a new ternary intermetallic Co3Ni3Ga8, substituting Co at the Ni sublattice in a highly symmetric Ni3Ga4 (Ia3Ì d). Co3Ni3Ga8 crystallizes in the I4132 space group, a Sohncke type, and can host the chiral structure. To the best of our knowledge, this is the first report of a ternary intermetallic crystallizing in this space group. The chiral structure of Co3Ni3Ga8 is comprehensively mapped by various techniques such as single-crystal X-ray diffraction (XRD), synchrotron powder XRD, X-ray absorption spectroscopy (XAS), scanning transmission electron microscopy (STEM) and theoretically studied using density functional theory. The discovery of this chiral compound can inspire the researchers to design hidden ternary chiral intermetallics to study the exotic electrical and magnetic properties.
RESUMEN
We present surface reconstruction-induced C-C coupling whereby CO2 is converted into ethylene. The wurtzite phase of CuGaS2. undergoes in situ surface reconstruction, leading to the formation of a thin CuO layer over the pristine catalyst, which facilitates selective conversion of CO2 to ethylene (C2 H4 ). Upon illumination, the catalyst efficiently converts CO2 to C2 H4 with 75.1 % selectivity (92.7 % selectivity in terms of Relectron ) and a 20.6â µmol g-1 h-1 evolution rate. Subsequent spectroscopic and microscopic studies supported by theoretical analysis revealed operando-generated Cu2+ , with the assistance of existing Cu+ , functioning as an anchor for the generated *CO and thereby facilitating C-C coupling. This study demonstrates strain-induced in situ surface reconstruction leading to heterojunction formation, which finetunes the oxidation state of Cu and modulates the CO2 reduction reaction pathway to selective formation of ethylene.
RESUMEN
Obtaining multi-carbon products via CO2 photoreduction is a major catalytic challenge involving multielectron-mediated CC bond formation. Complex design of multicomponent interfaces that are exploited to achieve this chemical transformation, often leads to untraceable deleterious changes in the interfacial chemical environment affecting CO2 conversion efficiency and product selectivity. Alternatively, robust metal centers having asymmetric charge distribution can effectuate CC coupling reaction through the stabilization of intermediates, for desired product selectivity. However, generating inherent charge distribution in a single component catalyst is a difficult material design challenge. Here, a novel photocatalyst, Bi19 S27 Cl3 , is presented which selectively converts CO2 to a C2 product, ethanol, in high yield under visible light irradiation. Structural analysis through transmission electron microscopy, X-ray diffraction, X-ray photoelectron spectroscopy, and X-ray absorption spectroscopy reveals the presence of charge polarized bismuth centers in Bi19 S27 Cl3 . The intrinsic electric field induced by charge polarized bismuth centers renders better separation efficiency of photogenerated electron-hole pair. Furthermore, charge polarized centers yield better adsorption of CO* intermediate and accelerate the rate determining CC coupling step through the formation of OCCOH intermediate. Formation of these intermediates is experimentally mapped by in situ Fourier-transform infrared spectroscopy and further confirmed by theoretical calculation.
RESUMEN
NiFe layered double hydroxide (NiFe LDH) grown in the presence of MoS2 (rich in 1T phase) shows exceptional performance metrics for alkaline oxygen evolution reaction (OER) in this class of composites. The as-prepared NiFe LDH/MoS2 composite (abbreviated as MNF) exhibits a low overpotential (η10) of 190 mV; a low Tafel slope of 31 mV dec-1; and more importantly, a high stability in its performance manifested by the delivery of current output for 45 h. It is important to note that this could be achieved with an exceedingly low loading of 0.14 mg cm-2. The mass activity of this composite (97 A g-1) is about 14 times greater than that of the conventional RuO2 (7 A g-1) at η = 200 mV. When normalized with respect to the total metal content, a mass activity of 1000 A g-1 (η = 300 mV) was achieved. Impedance analysis further reveals that the significant reduction in charge-transfer resistance and hence high current density (5 times greater as compared to NiFe LDH at η = 300 mV) observed for MNF is associated with interfacial adsorption kinetics of intermediates (R1). Significant enhancement in the intrinsic activity of MNF over LDH has been observed through normalization of current with the electrochemically active surface area. Computational studies suggest that the Ni centers in the composite act as the active sites for OER, which is well-corroborated with the observed postreaction appearance of Ni3+ species.
RESUMEN
The well-known limitation of alkaline fuel cells is the slack kinetics of the cathodic half-cell reaction, the oxygen reduction reaction (ORR). Platinum, being the most active ORR catalyst, is still facing challenges due to its corrosive nature and sluggish kinetics. Many novel approaches for substituting Pt have been reported, which suffer from stability issues even after mighty modifications. Designing an extremely stable, but unexplored ordered intermetallic structure, Pd2Ge, and tuning the electronic environment of the active sites by site-selective Pt substitution to overcome the hurdle of alkaline ORR is the main motive of this paper. The substitution of platinum atoms at a specific Pd position leads to Pt0.2Pd1.8Ge demonstrating a half-wave potential (E1/2) of 0.95 V vs RHE, which outperforms the state-of-the-art catalyst 20% Pt/C. The mass activity (MA) of Pt0.2Pd1.8Ge is 320 mA/mgPt, which is almost 3.2 times better than that of Pt/C. E1/2 and MA remained unaltered even after 50,000 accelerated degradation test (ADT) cycles, which makes it a promising stable catalyst with its activity better than that of the state-of-the-art Pt/C. The undesired 2e- transfer ORR forming hydrogen peroxide (H2O2) is diminished in Pt0.2Pd1.8Ge as visible from the rotating ring-disk electrode (RRDE) experiment, spectroscopically visualized by in situ Fourier transform infrared (FTIR) spectroscopy and supported by computational studies. The effect of Pt substitution on Pd has been properly manifested by X-ray absorption spectroscopy (XAS) and X-ray photoelectron spectroscopy (XPS). The swinging of the oxidation state of atomic sites of Pt0.2Pd1.8Ge during the reaction is probed by in situ XAS, which efficiently enhances 4e- transfer, producing an extremely low percentage of H2O2.
Asunto(s)
Peróxido de Hidrógeno , Platino (Metal) , Catálisis , Electrones , Oxígeno/química , Platino (Metal)/químicaRESUMEN
The discovery of novel materials for industrial-standard hydrogen production is the present need considering the global energy infrastructure. A novel electrocatalyst, Pt3 Ge, which is engineered with a desired crystallographic facet (202), accelerates hydrogen production by water electrolysis, and records industrially desired operational stability compared to the commercial catalyst platinum is introduced. Pt3 Ge-(202) exhibits low overpotential of 21.7 mV (24.6 mV for Pt/C) and 92 mV for 10 and 200 mA cm-2 current density, respectively in 0.5 m H2 SO4 . It also exhibits remarkable stability of 15 000 accelerated degradation tests cycles (5000 for Pt/C) and exceptional durability of 500 h (@10 mA cm-2 ) in acidic media. Pt3 Ge-(202) also displays low overpotential of 96 mV for 10 mA cm-2 current density in the alkaline medium, rationalizing its hydrogen production ability over a wide pH range required commercial operations. Long-term durability (>75 h in alkaline media) with the industrial level current density (>500 mA cm-2 ) has been demonstrated by utilizing the electrochemical flow reactor. The driving force behind this stupendous performance of Pt3 Ge-(202) has been envisaged by mapping the reaction mechanism, active sites, and charge-transfer kinetics via controlled electrochemical experiments, ex situ X-ray photoelectron spectroscopy, in situ infrared spectroscopy, and in situ X-ray absorption spectroscopy further corroborated by first principles calculations.
RESUMEN
Electrochemical reduction of CO2 into valuable fuels and chemicals is a promising route of replacing fossil fuels by reducing CO2 emissions and minimizing its adverse effects on the climate. Tremendous efforts have been carried out for designing efficient catalyst materials to selectively produce the desired product in high yield from CO2 by the electrochemical process. In this work, a strategy is reported to enhance the electrochemical CO2 reduction reaction (ECO2RR) by constructing an interface between a metal-based alloy (PdIn) nanoparticle and an oxide (In2O3), which was synthesized by a facile solution method. The oxide-derived PdIn surface has shown excellent eCO2RR activity and enhanced CO selectivity with a Faradaic efficiency (FE) of 92.13% at -0.9 V (vs RHE). On the other hand, surface PdO formation due to charge transfer on the bare PdIn alloy reduces the CO2RR activity. With the support of in situ (EXAFS and IR) and ex situ (XPS, Raman) spectroscopic techniques, the optimum presence of the Pd-In-O interface has been identified as a crucial parameter for enhancing eCO2RR toward CO in a reducing atmosphere. The influence of eCO2RR duration is reported to affect the overall performance by switching the product selectivity from H2 (from water reduction) to CO (from eCO2RR) on the oxide-derived alloy surface. This work also succeeded in the multifold enhancement of the current density by employing the gas diffusion electrode (GDE) and optimizing its process parameters in a flow cell configuration.
RESUMEN
Electrochemical CO2 reduction reaction (eCO2 RR) is performed on two intermetallic compounds formed by copper and gallium metals (CuGa2 and Cu9 Ga4 ). Among them, CuGa2 selectively converts CO2 to methanol with remarkable Faradaic efficiency of 77.26% at an extremely low potential of -0.3 V vs RHE. The high performance of CuGa2 compared to Cu9 Ga4 is driven by its unique 2D structure, which retains surface and subsurface oxide species (Ga2 O3 ) even in the reduction atmosphere. The Ga2 O3 species is mapped by X-ray photoelectron spectroscopy (XPS) and X-ray absorption fine structure (XAFS) techniques and electrochemical measurements. The eCO2 RR selectivity to methanol are decreased at higher potential due to the lattice expansion caused by the reduction of the Ga2 O3 , which is probed by in situ XAFS, quasi in situ powder X-ray diffraction, and ex situ XPS measurements. The mechanism of the formation of methanol is visualized by in situ infrared (IR) spectroscopy and the source of the carbon of methanol at the molecular level is confirmed from the isotope-labeling experiments in presence of 13 CO2 . Finally, to minimize the mass transport limitations and improve the overall eCO2 RR performance, a poly(tetrafluoroethylene)-based gas diffusion electrode is used in the flow cell configuration.
RESUMEN
Understanding the descriptors of electrochemical activity and ways to modulate them are of paramount importance for the efficient structural engineering of electrocatalysts. Although, many studies separately elucidated the significance of thermodynamic and kinetic descriptors, lack of integrative approaches bars the potential utilization of these engineering tools for electrocatalytic activity enhancement. Here, through a facile post-carbonization synthetic technique using templated polyoxometalate based metal organic frameworks (POMOFs), we integrate three major structural engineering tools, viz. phase, size and strain into cost-effective Mo and W carbide electrocatalysts, and demonstrate how these factors qualitatively and quantitatively affect the critical descriptors of electrochemical activity. Deconvolution of these effects through combined experimental-theoretical analyses, shines new light on structure-activity relationships in this class of HER electrocatalysts. Optimum modulation of the structural tools culminated into the design of a superior electrocatalyst, consisting of ultrasmall γ-WC nanocrystals supported on N doped graphitic carbon that exhibited multifold activity enhancement in terms of onset potential, current density and Tafel slope compared to its structural analogues reported in this work and elsewhere. The present comprehensive study showcasing the effects of the structural engineering tools on activity will have considerable influence on future designs of more efficient nano-composite electrocatalysts.