RESUMEN
A double layer 2-terminal device is employed to show Na-controlled interfacial resistive switching and neuromorphic behavior. The bilayer is based on interfacing biocompatible NaNbO3 and Nb2O5, which allows the reversible uptake of Na+ in the Nb2O5 layer. We demonstrate voltage-controlled interfacial barrier tuning via Na+ transfer, enabling conductivity modulation and spike-amplitude- and spike-timing-dependent plasticity. The neuromorphic behavior controlled by Na+ ion dynamics in biocompatible materials shows potential for future low-power sensing electronics and smart wearables with local processing.
RESUMEN
A design concept of phase-separated amorphous nanocomposite thin films is presented that realizes interfacial resistive switching (RS) in hafnium oxide-based devices. The films are formed by incorporating an average of 7% Ba into hafnium oxide during pulsed laser deposition at temperatures ≤400°C. The added Ba prevents the films from crystallizing and leads to â¼20-nm-thin films consisting of an amorphous HfOx host matrix interspersed with â¼2-nm-wide, â¼5-to-10-nm-pitch Ba-rich amorphous nanocolumns penetrating approximately two-thirds through the films. This restricts the RS to an interfacial Schottky-like energy barrier whose magnitude is tuned by ionic migration under an applied electric field. Resulting devices achieve stable cycle-to-cycle, device-to-device, and sample-to-sample reproducibility with a measured switching endurance of ≥104 cycles for a memory window ≥10 at switching voltages of ±2 V. Each device can be set to multiple intermediate resistance states, which enables synaptic spike-timing-dependent plasticity. The presented concept unlocks additional design variables for RS devices.