Recent Advances in Magnesium-Magnesium Oxide Nanoparticle Composites for Biomedical Applications.

Magnesium (Mg) is considered an attractive option for orthopedic applications due to its density and elastic modulus close to the natural bone of the body, as well as biodegradability and good tensile strength. However, it faces serious challenges, including a high degradation rate and, as a result, a loss of mechanical properties during long periods of exposure to the biological environment. Also, among its other weaknesses, it can be mentioned that it does not deal with bacterial biofilms. It has been found that making composites by synergizing its various components can be an efficient way to improve its properties. Among metal oxide nanoparticles, magnesium oxide nanoparticles (MgO NPs) have distinct physicochemical and biological properties, including biocompatibility, biodegradability, high bioactivity, significant antibacterial properties, and good mechanical properties, which make it a good choice as a reinforcement in composites. However, the lack of comprehensive understanding of the effectiveness of Mg NPs as Mg matrix reinforcements in mechanical, corrosion, and biological fields is considered a challenge in their application. While introducing the role of MgO NPs in medical fields, this article summarizes the most important results of recent research on the mechanical, corrosion, and biological performance of Mg/MgO composites.

The Effectiveness Mechanisms of Carbon Nanotubes (CNTs) as Reinforcements for Magnesium-Based Composites for Biomedical Applications: A Review.

As a smart implant, magnesium (Mg) is highly biocompatible and non-toxic. In addition, the elastic modulus of Mg relative to other biodegradable metals (iron and zinc) is close to the elastic modulus of natural bone, making Mg an attractive alternative to hard tissues. However, high corrosion rates and low strength under load relative to bone are some challenges for the widespread use of Mg in orthopedics. Composite fabrication has proven to be an excellent way to improve the mechanical performance and corrosion control of Mg. As a result, their composites emerge as an innovative biodegradable material. Carbon nanotubes (CNTs) have superb properties like low density, high tensile strength, high strength-to-volume ratio, high thermal conductivity, and relatively good antibacterial properties. Therefore, using CNTs as reinforcements for the Mg matrix has been proposed as an essential option. However, the lack of understanding of the mechanisms of effectiveness in mechanical, corrosion, antibacterial, and cellular fields through the presence of CNTs as Mg matrix reinforcements is a challenge for their application. This review focuses on recent findings on Mg/CNT composites fabricated for biological applications. The literature mentions effective mechanisms for mechanical, corrosion, antimicrobial, and cellular domains with the presence of CNTs as reinforcements for Mg-based nanobiocomposites.

Heat Treatment's Vital Role: Elevating Orthodontic Mini-Implants for Superior Performance and Longevity-Pilot Study.

Orthodontic mini-implants are devices used for anchorage in various orthodontic treatments. We conducted a pilot study which aimed to observe preliminary trends regarding the impact of heat treatment on the elastic modulus of Ti6Al4V alloy and stainless steel 316L mini-implants. The initial phase involved testing the impact of heat treatment on the mechanical properties of Ti6Al4V alloy and stainless steel 316L mini-implants. MATERIAL AND METHODS: Ten self-drilling mini-implants sourced from two distinct manufacturers (Jeil Medical Corporation® and Leone®) with dimensions of 2.0 mm diameter and 10 mm length were tested. They were separated into two material groups: Ti6Al4V and 316L. Using the CETRUMT-2 microtribometer equipment, indentation testing was conducted employing a diamond-tipped Rockwell penetrator at a constant force of 4.5 N. RESULTS: Slight differences were observed in the elastic modulus of the Ti6Al4V alloy (103.99 GPa) and stainless steel 316L (203.20 GPa) compared to natural bone. The higher elastic moduli of these materials indicate that they are stiffer, which could potentially lead to stress-shielding phenomena and bone resorption. Heat treatment resulted in significant changes in mechanical properties, including elastic modulus reductions of approximately 26.14% for Ti6Al4V and 24.82% for 316L, impacting their performance in orthodontic applications. CONCLUSION: Understanding the effects of heat treatment on these alloys is crucial for optimizing their biomechanical compatibility and longevity in orthodontic treatment. To fully evaluate the effects of heat treatment on mini-implants and to refine their design and efficacy in clinical practice, further research is needed.

Research Progress of Titanium-Based Alloys for Medical Devices.

Biomaterials are currently a unique class of materials that are essential to improving the standard of human life and extending it. In the assent of the appearance of biomaterials that contain non-toxic elements, in this study, we examine a system of Ti25Mo7Zr15TaxSi (x = 0, 0.5, 0.75, 1 wt.%) for future medical applications. The alloys were developed in a vacuum electric arc furnace and then studied from a structural, mechanical and in vivo assessment (on rabbits) perspective. The effect of the silicon addition was clearly seen in both the structural and the mechanical characteristics, standing out as beta alloys with a dendritic structure and lowering the mechanical properties as a result of the silicon addition. In experimental rabbits, the proliferation of mesenchymal stem cells was observed in the periosteum and peri-implant area, differentiating into osteoblasts and then into osteocytes. Osteoclasts were discovered within the cartilaginous islands that provide structural support to newly formed bone, playing a primary role in bone remodeling. The newly formed spongy tissue adhered to the fibrous capsule that surrounds the alloy, ensuring good osseointegration of metallic implants. The overexpression of Osteopontin, Metalloproteinase-2 (also known as gelatinase A), and Metallopeptidase-9 (also known as gelatinase B) underscores the processes of osteogenesis, bone mineralization, and normal bone remodeling.

A Comprehensive Review of the Current Research Status of Biodegradable Zinc Alloys and Composites for Biomedical Applications.

Zinc (Zn)-based biodegradable materials show moderate degradation rates in comparison with other biodegradable materials (Fe and Mg). Biocompatibility and non-toxicity also make them a viable option for implant applications. Furthermore, Pure Zn has poor mechanical behavior, with a tensile strength of around 100-150 MPa and an elongation of 0.3-2%, which is far from reaching the strength required as an orthopedic implant material (tensile strength is more than 300 MPa, elongation more than 15%). Alloy and composite fabrication have proven to be excellent ways to improve the mechanical performance of Zn. Therefore, their alloys and composites have emerged as an innovative category of biodegradable materials. This paper summarizes the most important recent research results on the mechanical and biological characteristics of biodegradable Zn-based implants for orthopedic applications and the most commonly added components in Zn alloys and composites.

Effect of Si Contents on the Properties of Ti15Mo7ZrxSi Alloys.

The main purpose of this research is to evaluate the mechanical characteristics and biocompatibility of two novel titanium alloys, Ti15Mo7ZrxSi (x = 0, 0.5, 0.75, 1). These samples had already undergone grinding, polishing, cutting, and chipping. Electrochemical, metallographic, three-point bending, and microhardness studies were conducted on the studied materials to determine their corrosion behavior, microstructure, Young's modulus, and hardness. The first investigations revealed that both samples had biphasic and dendritic structures, elastic moduli that were between the highest and minimum values achieved by around 20 GPa, and favorable behavior when in contact with physiological fluids at ambient temperature. Ti15Mo7Zr0.5Si and Ti15Mo7Zr0.75Si, the research samples, had greater corrosion potentials, reduced corrosion rates, and therefore higher corrosion resistance, as well as modulus of elasticity values that were comparable to and closer to those of human bone. The results of this investigation indicate that both alloys exhibit favorable corrosion behavior, great biocompatibility, Young's modulus results lower than those of conventional alloys used in biomedical implants, and hardness values higher than commercially pure titanium.

Bredigite-CNTs Reinforced Mg-Zn Bio-Composites to Enhance the Mechanical and Biological Properties for Biomedical Applications.

Magnesium (Mg) and its compounds have been investigated as biodegradable metals for bone implants. However, high corrosion rates and low bioactivity that cause loss of mechanical properties are factors that have limited their biomedical applications. The purpose of this work is to remedy the weaknesses of the Mg-Zn (MZ) alloy matrix. For this purpose, we have synthesized Mg-based composites with different concentrations of bredigite (Br; Ca7MgSi4O16)-carbon nanotubes (CNTs) using mechanical alloying and semi-powder metallurgy processes with spark plasma sintering. Then, we studied the effect of the simultaneous addition of Br-CNTs on in vitro degradation, as well as its effect on the composites' mechanical and antibacterial properties. Increases of 57% and 72% respectively were observed in the microhardness and compressive strength of the MZ/Br-CNTs composite in comparison to the MZ alloy. In addition, the rate of degradation of Mg-based composites in simulated body fluids (SBF) was almost 2 times lower. An assessment of antibacterial behavior disclosed that the simultaneous adding of Br-CNTs to Mg can meaningfully prevent the growth and invasion of E. coli and S. aureus. These research findings demonstrate the potential application of MZ/Br-CNTs composites to implants and the treatment of bone infections.

Near-Infrared (NIR) Silver Sulfide (Ag2S) Semiconductor Photocatalyst Film for Degradation of Methylene Blue Solution.

A silver sulfide (Ag2S) semiconductor photocatalyst film has been successfully synthesized using a solution casting method. To produce the photocatalyst films, two types of Ag2S powder were used: a commercialized and synthesized powder. For the commercialized powder (CF/comAg2S), the Ag2S underwent a rarefaction process to reduce its crystallite size from 52 nm to 10 nm, followed by incorporation into microcrystalline cellulose using a solution casting method under the presence of an alkaline/urea solution. A similar process was applied to the synthesized Ag2S powder (CF/syntAg2S), resulting from the co-precipitation process of silver nitrate (AgNO3) and thiourea. The prepared photocatalyst films and their photocatalytic efficiency were characterized by Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), and UV-visible spectroscopy (UV-Vis). The results showed that the incorporation of the Ag2S powder into the cellulose films could reduce the peak intensity of the oxygen-containing functional group, which indicated the formation of a composite film. The study of the crystal structure confirmed that all of the as-prepared samples featured a monoclinic acanthite Ag2S structure with space group P21/C. It was found that the degradation rate of the methylene blue dye reached 100% within 2 h under sunlight exposure when using CF/comAg2S and 98.6% for the CF/syntAg2S photocatalyst film, and only 48.1% for the bare Ag2S powder. For the non-exposure sunlight samples, the degradation rate of only 33-35% indicated the importance of the semiconductor near-infrared (NIR) Ag2S photocatalyst used.

Influence of Polyformaldehyde Monofilament Fiber on the Engineering Properties of Foamed Concrete.

Foamed concrete is considered a green building material, which is porous in nature. As a result, it poses benefits such as being light in self-weight, and also has excellent thermal insulation properties, environmental safeguards, good fire resistance performance, and low cost. Nevertheless, foamed concrete has several disadvantages such as low strength, a large amount of entrained air, poor toughness, and being a brittle material, all of which has restricted its usage in engineering and building construction. Hence, this study intends to assess the potential utilization of polypropylene fibrillated fiber (PFF) in foamed concrete to enhance its engineering properties. A total of 10 mixes of 600 and 1200 kg/m3 densities were produced by the insertion of four varying percentages of PFF (1%, 2%, 3%, and 4%). The properties assessed were splitting tensile, compressive and flexural strengths, workability, porosity, water absorption, and density. Furthermore, the correlations between the properties considered were also evaluated. The outcomes reveal that the foamed concrete mix with 4% PFF attained the highest porosity, with approximately 13.9% and 15.9% for 600 and 1200 kg/m3 densities in comparison to the control specimen. Besides, the mechanical properties (splitting tensile, compressive and flexural strengths) increased steadily with the increase in the PFF percentages up to the optimum level of 3%. Beyond 3%, the strengths reduced significantly due to poor PFF dispersal in the matrix, leading to a balling effect which causes a degraded impact of scattering the stress from the foamed concrete vicinity to another area of the PFF surface. This exploratory investigation will result in a greater comprehension of the possible applications of PFF in LFC. It is crucial to promote the sustainable development and implementation of LFC materials and infrastructures.

Experimental Research on New Developed Titanium Alloys for Biomedical Applications.

The mechanical properties and electrochemical behavior of two new titanium alloys, Ti20Mo7Zr and Ti20Mo7Zr0.5Si, are investigated in this paper. The alloys have been manufactured by vacuum arc remelting (VAR) technique and studied to determine their microstructure, corrosion behavior, and mechanical properties. Metallographic observations and quantitative microanalysis by optical microscopy, scanning electron microscopy SEM, and energy dispersive X-rays spectroscopy EDX were performed. Data about the three-point bending test and microhardness are presented. For electrochemical properties, three different environments were used: Ringer solution at 25 °C, Ringer solution at 40 °C simulating fever condition, and 3.5% NaCl solution. Metallographic investigation revealed the biphasic and dendritic structure of both samples when the procedures were performed. Electrochemical testing in body simulation fluid, fever conditions, and saline medium showed that the lower the proportion of silicon in the samples, the higher the corrosion resistance. The formation of a titanium oxide layer on the surface of both samples was noticed using quantitative EDX analysis. The three-point bending test for the two samples revealed that the presence of silicon decreases the modulus of elasticity; the surface of the samples displayed soft and hard phases in the microhardness test. Electrochemical impedance spectroscopy (EIS) measurements were carried out at different potentials, and the obtained spectra exhibit a two-time constant system, attesting double-layer passive film on the samples.

Mechanical Characterization and In Vitro Assay of Biocompatible Titanium Alloys.

Metals that come into contact with the body can cause reactions in the body, so biomaterials must be tested to avoid side effects. Mo, Zr, and Ta are non-toxic elements; alloyed with titanium, they have very good biocompatibility properties and mechanical properties. The paper aims to study an original Ti20Mo7ZrxTa system (5, 10, 15 wt %) from a mechanical and in vitro biocompatibility point of view. Alloys were examined by optical microstructure, tensile strength, fractographic analysis, and in vitro assay. The obtained results indicate very good mechanical and biological properties, recommending them for future orthopedic medical applications.

Effectiveness of Dimple Microtextured Copper Substrate on Performance of Sn-0.7Cu Solder Alloy.

This paper elucidates the influence of dimple-microtextured copper substrate on the performance of Sn-0.7Cu solder alloy. A dimple with a diameter of 50 µm was produced by varying the dimple depth using different laser scanning repetitions, while the dimple spacing was fixed for each sample at 100 µm. The dimple-microtextured copper substrate was joined with Sn-0.7Cu solder alloy using the reflow soldering process. The solder joints' wettability, microstructure, and growth of its intermetallic compound (IMC) layer were analysed to determine the influence of the dimple-microtextured copper substrate on the performance of the Sn-0.7Cu solder alloy. It was observed that increasing laser scan repetitions increased the dimples' depth, resulting in higher surface roughness. In terms of soldering performance, it was seen that the solder joints' average contact angle decreased with increasing dimple depth, while the average IMC thickness increased as the dimple depth increased. The copper element was more evenly distributed for the dimple-micro-textured copper substrate than its non-textured counterpart.

Assessment of the Effects of Si Addition to a New TiMoZrTa System.

Ti-based alloys are widely used in medical applications. When implant devices are used to reconstruct disordered bone, prevent bone resorption and enhance good bone remodeling, the Young's modulus of implants should be close to that of the bone. To satisfy this requirement, many titanium alloys with different biocompatible elements (Zr, Ta, Mo, Si etc.) interact well with adjacent bone tissues, promoting an adequate osseointegration. Four new different alloys were obtained and investigated regarding their microstructure, mechanical, chemical and biological behavior (in vitro and in vivo evaluation), as follows: Ti20Mo7Zr15Ta, Ti20Mo7Zr15Ta0.5Si, Ti20Mo7Zr15Ta0.75Si and Ti20Mo7Zr15TaSi. 60 days after implantation, both in control and experimental rabbits, at the level of implantation gap and into the periimplant area were found the mesenchymal stem cells which differentiate into osteoblasts, then osteocytes and osteoclasts which are involved in the new bone synthesis and remodeling, the periimplant fibrous capsule being continued by newly spongy bone tissue, showing a good osseointegration of alloys. A 3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide (MTT) assay confirmed the in vitro cytocompatibility of the prepared alloys.

Biomimetic Deposition of Hydroxyapatite Layer on Titanium Alloys.

Over the last decade, researchers have been concerned with improving metallic biomaterials with proper and suitable properties for the human body. Ti-based alloys are widely used in the medical field for their good mechanical properties, corrosion resistance and biocompatibility. The TiMoZrTa system (TMZT) evidenced adequate mechanical properties, was closer to the human bone, and had a good biocompatibility. In order to highlight the osseointegration of the implants, a layer of hydroxyapatite (HA) was deposited using a biomimetic method, which simulates the natural growth of the bone. The coatings were examined by scanning electron microscopy (SEM), X-ray diffraction (XRD), micro indentation tests and contact angle. The data obtained show that the layer deposited on TiMoZrTa (TMZT) support is hydroxyapatite. Modifying the surface of titanium alloys represents a viable solution for increasing the osseointegration of materials used as implants. The studied coatings demonstrate a positive potential for use as dental and orthopedic implants.

Design, Synthesis, and Preliminary Evaluation for Ti-Mo-Zr-Ta-Si Alloys for Potential Implant Applications.

Considering the future trends of biomaterials, current studies are focused on the corrosion resistance and the mechanical properties of new materials that need to be considered in the process of strengthening alloys with additive non-toxic elements. Many kinds of titanium alloys with different biocompatible elements (Mo, Si, Zr, etc.,) have been recently developed for their similar properties with human bone. Four new different alloys were obtained and investigated regarding their microstructure, mechanical, chemical, and biological behavior (in vitro and in vivo evaluation), the alloys are as follows: Ti15Mo7Zr15Ta, Ti15Mo7Zr15Ta0.5Si, Ti15Mo7Zr15Ta0.75Si, and Ti15Mo7Zr15Ta1Si. There were changes with the addition of the silicon element such as the hardness and the modulus of elasticity increased. An MTT assay confirmed the in vitro cytocompatibility of the prepared alloys.

New Titanium Alloys, Promising Materials for Medical Devices.

Titanium alloys are used in medical devices due to their mechanical properties, but also for their corrosion resistance. The natural passivation of titanium-based biomaterials, on the surface of which a dense and coherent film of nanometric thickness is formed, composed mainly of TiO2, determines an apparent bioactivity of them. In this paper, the method of obtaining new Ti20MoxSi alloys (x = 0.0, 0.5, 0.75, and 1.0) is presented, their microstructure is analyzed, and their electrochemical responses in Ringer´s solution were systematically investigated by linear polarization, cyclic potential dynamic polarization, and electrochemical impedance spectroscopy (EIS). The alloys corrosion resistance is high, and no evidence of localized breakdown of the passive layer was observed. There is no regularity determined by the composition of the alloys, in terms of corrosion resistance, but it seems that the most resistant is Ti20Mo1.0Si.

New Ti-Mo-Si materials for bone prosthesis applications.

Several newly obtained titanium alloys were characterized in order to evaluate the biocompatibility and their possible application as implants. For improvement of the performances of the TiMo alloys compared to other alloys, silicon was added, targeting good mechanical and technological properties, avoiding the toxic effects for human body. Titanium is very used in medical applications, due to their extremely low toxicity and good chemical stability in different body fluids. Four Ti15MoxSi (where x = 0, 0.5, 0.75, 1.0 wt %), alloys were developed and investigated regarding microstructure, mechanical, chemical and biological behavior (in vitro and in vivo evaluation). By increasing the Si content from 0 to 1% wt., the mechanical properties of the Ti15Mo alloys were significantly improved. By increasing the Si content from 0 to 1% wt., the mechanical properties of the Ti15Mo alloys were significantly improved (about 50%) from 44.50 GPa to 19.81 GPa modulus of elasticity and the hardness values 361.28 to 188.52 HV. The cytocompatibility assessment on human line osteoblasts indicated good cell-material interactions and in vivo tests indicated a successful osseointegration, the surrounding newly bone being formed without any significant inflammatory reaction. Expression of osteopontin in the peri-implant area highlights the presence of osteogenesis and bone mineralization. Metalloproteinase-2 (gelatinase A) and metallopeptidase-9 (gelatinase B) overexpression in osteoblasts, osteoclasts and osteocytes represent the markers of normal bone remodeling. All these results suggest that the TiMoSi alloys are promising materials for orthopedics devices, since mechanical properties and biocompatibility offer conditions for applying them as biomaterial.

Characterization and Mechanical Proprieties of New TiMo Alloys Used for Medical Applications.

Ti-based alloys are accessible for use in the human body due to their good mechanical properties, corrosion resistance, and biocompatibilities. These main properties of alloys are important criteria for choosing biomedical implants for human bones or for other kinds of applications in general medicine. This paper presents a comparison of four new Ti-based alloys desired to satisfy various requirements for biomedical implants. The materials were prepared with recipes for two new system alloys, TiMoZrTa (TMZT) and TiMoSi (TMS), alloys with nontoxic elements. The presented research contains microstructure images, indentation tests, Vickers hardness, XRD, and corrosion resistance, showing better characteristics than most commercial products used as implants (Young's modulus closer to the human bone).