RESUMEN
We present a design strategy for fabricating ultrastable phase-pure films of formamidinium lead iodide (FAPbI3) by lattice templating using specific two-dimensional (2D) perovskites with FA as the cage cation. When a pure FAPbI3 precursor solution is brought in contact with the 2D perovskite, the black phase forms preferentially at 100°C, much lower than the standard FAPbI3 annealing temperature of 150°C. X-ray diffraction and optical spectroscopy suggest that the resulting FAPbI3 film compresses slightly to acquire the (011) interplanar distances of the 2D perovskite seed. The 2D-templated bulk FAPbI3 films exhibited an efficiency of 24.1% in a p-i-n architecture with 0.5-square centimeter active area and an exceptional durability, retaining 97% of their initial efficiency after 1000 hours under 85°C and maximum power point tracking.
RESUMEN
One of the primary methods for band gap tuning in metal halide perovskites has been halide (I/Br) mixing. Despite widespread usage of this type of chemical substitution in perovskite photovoltaics, there is still little understanding of the structural impacts of halide alloying, with the assumption being the formation of ideal solid solutions. The FASnI3-xBrx (x = 0-3) family of compounds provides the first example where the assumption breaks down, as the composition space is broken into two unique regimes (x = 0-2.9; x = 2.9-3) based on their average structure with the former having a 3D and the latter having an extended 3D (pseudo 0D) structure. Pair distribution function (PDF) analyses further suggest a dynamic 5s2 lone pair expression resulting in increasing levels of off-centering of the central Sn as the Br concentration is increased. These antiferroelectric distortions indicate that even the x = 0-2.9 phase space behaves as a nonideal solid-solution on a more local scale. Solid-state NMR confirms the difference in local structure yielding greater insight into the chemical nature and local distributions of the FA+ cation. In contrast to the FAPbI3-xBrx series, a drastic photoluminescence (PL) quenching is observed with x ≥ 1.9 compounds having no observable PL. Our detailed studies attribute this quenching to structural transitions induced by the distortions of the [SnBr6] octahedra in response to stereochemically expressed lone pairs of electrons. This is confirmed through density functional theory, having a direct impact on the electronic structure.
RESUMEN
The tunable bandgaps and facile fabrication of perovskites make them attractive for multi-junction photovoltaics1,2. However, light-induced phase segregation limits their efficiency and stability3-5: this occurs in wide-bandgap (>1.65 electron volts) iodide/bromide mixed perovskite absorbers, and becomes even more acute in the top cells of triple-junction solar photovoltaics that require a fully 2.0-electron-volt bandgap absorber2,6. Here we report that lattice distortion in iodide/bromide mixed perovskites is correlated with the suppression of phase segregation, generating an increased ion-migration energy barrier arising from the decreased average interatomic distance between the A-site cation and iodide. Using an approximately 2.0-electron-volt rubidium/caesium mixed-cation inorganic perovskite with large lattice distortion in the top subcell, we fabricated all-perovskite triple-junction solar cells and achieved an efficiency of 24.3 per cent (23.3 per cent certified quasi-steady-state efficiency) with an open-circuit voltage of 3.21 volts. This is, to our knowledge, the first reported certified efficiency for perovskite-based triple-junction solar cells. The triple-junction devices retain 80 per cent of their initial efficiency following 420 hours of operation at the maximum power point.
RESUMEN
Alloying is a common technique to optimize the functional properties of materials for thermoelectrics, photovoltaics, energy storage etc. Designing thermoelectric (TE) alloys is especially challenging because it is a multi-property optimization problem, where the properties that contribute to high TE performance are interdependent. In this work, we develop a computational framework that combines first-principles calculations with alloy and point defect modeling to identify alloy compositions that optimize the electronic, thermal, and defect properties. We apply this framework to design n-type Ba2(1-x)Sr2xCdP2 Zintl thermoelectric alloys. Our predictions of the crystallographic properties such as lattice parameters and site disorder are validated with experiments. To optimize the conduction band electronic structure, we perform band unfolding to sketch the effective band structures of alloys and find a range of compositions that facilitate band convergence and minimize alloy scattering of electrons. We assess the n-type dopability of the alloys by extending the standard approach for computing point defect energetics in ordered structures. Through the application of this framework, we identify an optimal alloy composition range with the desired electronic and thermal transport properties, and n-type dopability. Such a computational framework can also be used to design alloys for other functional applications beyond TE.
RESUMEN
The novel α-BaZn2P2 structural polymorph has been synthesized and structurally characterized for the first time. Its structure, elucidated from single crystal X-ray diffraction, indicates that the compound crystallizes in the orthorhombic α-BaCu2S2 structure type, with unit cell parameters a = 9.7567(14) Å, b = 4.1266(6) Å, and c = 10.6000(15) Å. With ß-BaZn2P2 being previously identified as belonging to the ThCr2Si2 family and with the precedent of structural phase transitions between the α-BaCu2S2 type and the ThCr2Si2 type, the potential for the pattern to be extended to the two different structural forms of BaZn2P2 was explored. Thermal analysis suggests that a first-order phase transition occurs at â¼1123 K, whereby the low-temperature orthorhombic α-phase transforms to a high-temperature tetragonal ß-BaZn2P2, the structure of which was also studied and confirmed by single-crystal X-ray diffraction. Preliminary transport properties and band structure calculations indicate that α-BaZn2P2 is a p-type, narrow-gap semiconductor with a direct bandgap of 0.5 eV, which is an order of magnitude lower than the calculated indirect bandgap for the ß-BaZn2P2 phase. The Seebeck coefficient, S(T), for the material increases steadily from the room temperature value of 119 µV/K to 184 µV/K at 600 K. The electrical resistivity (ρ) of α-BaZn2P2 is relatively high, on the order of 40 mΩ·cm, and the ρ(T) dependence shows gradual decrease upon heating. Such behavior is comparable to those of the typical semimetals or degenerate semiconductors.
RESUMEN
The novel Zintl phase dibarium zinc diphosphide (Ba2ZnP2) was synthesized for the first time. This was accomplished using the Pb flux technique, which allowed for the growth of crystals of adequate size for structural determination via single-crystal X-ray diffraction methods. The Ba2ZnP2 compound was determined to crystallize in a body-centered orthorhombic space group, Ibam (No. 72). Formally, this crystallographic arrangement belongs to the K2SiP2 structure type. Therefore, the structure can be best described as infinite [ZnP2]4- polyanionic chains with divalent Ba2+ cations located between the chains. All valence electrons are partitioned, which conforms to the Zintl-Klemm concept and suggests that Ba2ZnP2 is a valence-precise composition. The electronic band structure of this new compound, computed with the aid of the TB-LMTO-ASA code, shows that Ba2ZnP2 is an intrinsic semiconductor with a band gap of ca 0.6â eV.