Layered 2D perovskites are making inroads as materials for photovoltaics and light emitting diodes, but their photophysics is still lively debated. Although their large exciton binding energies should hinder charge separation, significant evidence has been uncovered for an abundance of free carriers among optical excitations. Several explanations have been proposed, like exciton dissociation at grain boundaries or polaron formation, without clarifying yet if excitons form and then dissociate, or if the formation is prevented by competing relaxation processes. Here we address exciton stability in layered Ruddlesden-Popper PEA2PbI4 (PEA stands for phenethylammonium) both in form of thin film and single crystal, by resonant injection of cold excitons, whose dissociation is then probed with femtosecond differential transmission. We show the intrinsic nature of exciton dissociation in 2D layered perovskites, demonstrating that both 2D and 3D perovskites are free carrier semiconductors and their photophysics is described by a unique and universal framework.
RESUMEN
Here we demonstrate blue LEDs with a peak wavelength of 481 nm, with outstanding colour purity of up to 88% (CIE coordinates (0.1092, 0.1738)), an external quantum yield of 5.2% and a luminance of 8260 cd m-2. These devices are based on quasi-2D PEA2(Cs0.75MA0.25)Pb2Br7, which is cast from solutions containing isopropylammonium (iPAm). iPAm as additive assist in supressing the formation of bulk-like phases, as pointed out by both photophysical and structural characterization. Additionally, the study of the excitation dynamics demonstrates a hindering of the energy transfer to domains of lower energy that generally undermines the performance and emission characteristics of blue-emitting LEDs based on quasi-2D perovskites. The achieved narrow distribution of quantum well sizes and the hindered energy transfer result in a thin film photoluminescence quantum yield exceeding 60%. Our work demonstrates the great potential to tailor the composition and the structure of thin films based on Ruddlesden-Popper phases to boost performance of optoelectronic devices - specifically blue perovskite LEDs.
RESUMEN
The development of an environmentally friendly fabrication process for non-fullerene acceptor organic solar cells is an essential condition for their commercialization. However, devices fabricated by processing the active layer with green solvents still struggle to reach, in terms of efficiency, the same performance as those fabricated with halogenated solvents. The reason behind this is the non-optimal nanostructure of the active layer obtained with green solvents. Additives in solution have been used to fine-tune the nanostructure and improve the performance of organic solar cells. Therefore, the identification of non-halogenated additives and the study of their effects on the device performance and stability are of primary importance. In this work, we propose the use of diphenyl ether (DPE) as additive, in combination with the non-halogenated solvent o-xylene, to fabricate organic solar cells with a completely halogen-free process. Thanks to the addition of DPE, a best efficiency of 11.7% have been obtained for the system TPD-3F:IT-4F, an increase over 15% with respect to the efficiency of devices fabricated without additive. Remarkably, the stability under illumination of the solar cells is also improved when DPE is used. The addition of DPE has effects on the molecular organization in the active layer, with an enhancement in the donor polymer ordering, showing a higher domain purity. The resulting structure improves the charge carrier collection, leading to a superior short-circuit current and fill factor. Furthermore, a reduction of the non-radiative recombination losses and an improved exciton diffusion, are the results of the superior molecular ordering. With a comprehensive insight of the effects of DPE when used in combination with a non-halogenated solvent, our study provides an approach to make the fabrication of organic solar cell environmentally friendlier and more suitable for large scale production.
RESUMEN
Manipulation by external pressure of the optical response of 2D Metal Halide Perovskites (MHPs) is a fascinating route to tune their properties and promote the emergence of novel features. We investigate here DA2PbI4 and DA2GeI4 (DA = decylammonium) perovskites in the pressure range up to â¼12 GPa by X-ray powder diffraction, absorption, and photoluminescence spectroscopy. Although the two systems share a similar structural evolution with pressure, the optical properties are rather different and influenced by Pb or Ge. DA2PbI4 shows a progressive red shift from 2.28 eV (P = 0 GPa) to 1.64 eV at 11.5 GPa, with a narrow PL emission, whereas DA2GeI4, changes from a non-PL system at ambient pressure to a clear broadband emitter centered around 730 nm with an intensity maximum at about 3.7 GPa. These results unveil the role of the central atom on the nature of emission under pressure in 2D MHPs containing a long alkyl chain.
RESUMEN
Hybrid lead halides CH3NH3PbX3 (X = I, Br, and Cl) have emerged as a new class of semiconductors for low-cost optoelectronic devices with superior performance. Since their perovskite crystal structure may have lattice instabilities against polar distortions, they are also being considered as potential photo-ferroelectrics. However, so far, research on their ferroelectricity has yielded inconclusive results and the subject is far from being settled. Here, we investigate, using a combined experimental and theoretical approach, the possible presence of electric polarization in tetragonal and orthorhombic CH3NH3PbBr3 (T-MAPB and O-MAPB). We found that T-MAPB does not sustain spontaneous polarization but, under an external electric field, it is projected into a metastable, ionic space-charge electret state. The electret can be frozen on cooling, producing a large and long-lasting polarization in O-MAPB. Molecular dynamics simulations show that the ferroelastic domain boundaries are able to trap charges and segregate ionic point defects, thus playing a favorable role in the stabilization of the electret. At lower temperatures, the lack of ferroelectric behavior is explained using first principles calculations as the result of the tight competition among many metastable states with randomly oriented polarization; this large configurational entropy does not allow a single polar state to dominate at any significant temperature range.
RESUMEN
The potential of silicon-based fluorescent platforms for the detection of trace toxic metal ions was investigated in an aqueous environment. To this aim, silicon chips were first functionalized with amino groups, and fluorescein organic dyes, used as sensing molecules, were then covalently linked to the surface via formation of thiourea groups. The obtained hybrid heterostructures exhibited high sensitivity and selectivity towards copper(ii), a limit of detection compatible with the recommended upper limits for copper in drinking water, and good reversibility using a standard metal-chelating agent. The fluorophore-analyte interaction mechanism at the basis of the reported fluorescence quenching, as well as the potential of performance improvement, were also studied. The herein presented sensing architecture allows, in principle, tailoring of the selectivity towards other metal ions by proper fluorophore selection, and provides a favorable outlook for integration of fluorescent chemosensors with silicon photonics technology.
RESUMEN
Compositional engineering has been a strong tool to improve the quality of the perovskite materials and, in turn, the reproducibility of the solar cells. However, the control over the active layer uniformity, one of the most important requirements for the obtainment of efficient devices, is still a weak point of perovskite solar cells (PSCs) manufacturing. Here, we develop an approach to grow a uniform mixed cation perovskite layer, foreseeing its implementation in inverted solar cells endowing organic transporting layers, through the addition of a stoiochiometric amount of tropolone as chelating agent for the lead. Thanks to low melting and boiling temperatures, tropolone is present in the system only during the colloidal liquid phase, leaving the film during its formation; this unique characteristic promotes the obtainment of ideal perovskite surface morphologies and an increased short circuit current of photovoltaic devices. A maximum power conversion efficiency of 20% was obtained, with a 25% increase with respect to the reference.
RESUMEN
We report on the successful application of RF-magnetron sputtering to deposit, by using a single type of target, three different materials in the form of thin films within the Cs-Sn-Br compositional range, namely, CsSnBr3, CsSn2Br5 and Cs2SnBr6. It is shown that, by playing with the deposition parameters and post-deposition treatments, it is possible to stabilize these three perovskites or perovskite related compounds by exploiting the versatility of vapor phase deposition. Full characterization in terms of crystal structure, optical properties and morphology is reported. The power of vapor phase methods in growing all-inorganic materials of interest for photovoltaic and optoelectronic applications is demonstrated here, indicating the advantageous use of sputtering for these complex materials.
RESUMEN
In August 2016, a magnitude 6.0 earthquake struck Central Italy, starting a devastating seismic sequence, aggravated by other two events of magnitude 5.9 and 6.5, respectively. After the first mainshock, four Italian institutions installed a dense temporary network of 50 seismic stations in an area of 260 km2. The network was registered in the International Federation of Digital Seismograph Networks with the code 3A and quoted with a Digital Object Identifier ( https://doi.org/10.13127/SD/ku7Xm12Yy9 ). Raw data were converted into the standard binary miniSEED format, and organized in a structured archive. Then, data quality and completeness were checked, and all the relevant information was used for creating the metadata volumes. Finally, the 99 Gb of continuous seismic data and metadata were uploaded into the INGV node of the European Integrated Data Archive repository. Their use was regulated by a Memorandum of Understanding between the institutions. After an embargo period, the data are now available for many different seismological studies.
RESUMEN
An optical radiometry technique enabling simultaneous transmittance and reflectance measurements from both sides of a device was used to investigate bifacial diffuse absorptance of neutral-colored semitransparent perovskite solar cells based on a thin film of microsized perovskite islands. In such microstructured solar cells, diffuse irradiance was more effectively absorbed than direct irradiance at near-normal incidence, in contrast to reference solar cells comprising a continuous perovskite thin film. Experimental findings were discussed in ray-optic approximation in relation to the surface texture of the active layer, highlighting the role of light trapping. This absorptance spectroscopy technique is envisaged to find wide applicability to bifacial solar cells for building-integrated photovoltaics and other bifacial light-harvesting systems.
RESUMEN
The possible existence of mixed methylammonium (MA)/dimethylammonium (DMA) lead bromide hybrid perovskites of general formula MA1- xDMA xPbBr3 (0 ≤ x ≤ 1) was investigated. A combined X-ray diffraction and solid-state nuclear magnetic resonance approach indicates that DMA can be incorporated up to about x = 0.30 while retaining the cubic lattice of MAPbBr3. By increasing the DMA content ( x), the absorption shows a progressive blue shift and the band gap moves from about 2.17 eV ( x = 0) to about 2.23 ( x = 0.30) with a concomitant slightly faster recombination in the mixed cation powders.
RESUMEN
Solution-based methods represent the most widespread approach used to deposit hybrid organic-inorganic perovskite films for low-cost but efficient solar cells. However, solution-process techniques offer limited control over film morphology and crystallinity, and most importantly do not allow sequential film deposition to produce perovskite-perovskite heterostructures. Here the successful deposition of CH3NH3PbI3 (MAPI) thin films by RF-magnetron sputtering is reported, an industry-tested method to grow large area devices with precisely controlled stoichiometry. MAPI films are grown starting from a single-target made of CH3NH3I (MAI) and PbI2. Films are single-phase, with a barely detectable content of unreacted PbI2, full surface coverage and thickness ranging from less than 200 nm to more than 3 µm. Light absorption and emission properties of the deposited films are comparable to as-grown solution-processed MAPI films. The development of vapor-phase deposition methods is of interest to advance perovskite photovoltaic devices with the possibility of fabricating perovskite multijunction solar cells or multicolor bright light-emitting devices in the whole visible spectrum.
RESUMEN
Herein, an insulating biopolymer is exploited to guide the controlled formation of micro/nano-structure and physical confinement of α-δ mixed phase crystalline grains of formamidinium lead iodide (FAPbI3) perovskite, functioning as charge carrier concentrators and ensuring improved radiative recombination and photoluminescence quantum yield (PLQY). This composite material is used to build highly efficient near-infrared (NIR) FAPbI3 Perovskite light-emitting diodes (PeLEDs) that exhibit a high radiance of 206.7 W/sr*m2, among the highest reported for NIR-PeLEDs, obtained at a very high current density of 1000 mA/cm2, while importantly avoiding the efficiency roll-off effect. In depth photophysical characterization allows to identify the possible role of the biopolymer in i) enhancing the radiative recombination coefficient, improving light extraction by reducing the refractive index, or ii) enhancing the effective optical absorption because of dielectric scattering at the polymer-perovskite interfaces. Our study reveals how the use of insulating matrixes for the growth of perovskites represents a step towards high power applications of PeLEDs.
RESUMEN
Er clustering plays a major role in hindering sufficient optical gain in Er-doped Si materials. For porous Si, the long-standing failure to govern the clustering has been attributed to insufficient knowledge of the several, concomitant and complex processes occurring during the electrochemical Er-doping. We propose here an alternative road to solve the issue: instead of looking for an equilibrium between Er content and light emission using 1-2% Er, we propose to significantly increase the electrochemical doping level to reach the filling the porous silicon pores with luminescent Er-rich material. To better understand the intricate and superposing phenomena of this process, we exploit an original approach based on needle electron tomography, EXAFS and photoluminescence. Needle electron tomography surprisingly shows a heterogeneous distribution of Er content in the silicon thin pores that until now couldn't be revealed by the sole use of scanning electron microscopy compositional mapping. Besides, while showing that pore filling leads to enhanced photoluminescence emission, we demonstrate that the latter is originated from both erbium oxide and silicate. These results give a much deeper understanding of the photoluminescence origin down to nanoscale and could lead to novel approaches focused on noteworthy enhancement of Er-related photoluminescence in porous silicon.
RESUMEN
Metal-halide perovskite solar cells rival the best inorganic solar cells in power conversion efficiency, providing the outlook for efficient, cheap devices. In order for the technology to mature and approach the ideal Shockley-Queissier efficiency, experimental tools are needed to diagnose what processes limit performances, beyond simply measuring electrical characteristics often affected by parasitic effects and difficult to interpret. Here we study the microscopic origin of recombination currents causing photoconversion losses with an all-optical technique, measuring the electron-hole free energy as a function of the exciting light intensity. Our method allows assessing the ideality factor and breaks down the electron-hole recombination current into bulk defect and interface contributions, providing an estimate of the limit photoconversion efficiency, without any real charge current flowing through the device. We identify Shockley-Read-Hall recombination as the main decay process in insulated perovskite layers and quantify the additional performance degradation due to interface recombination in heterojunctions.
RESUMEN
Metal halide perovskites have come to the attention of the scientific community for the progress achieved in solar light conversion. Energy sustainability is one of the priorities of our society, and materials advancements resulting in low-cost but efficient solar cells and large-area lighting devices represent a major goal for applied research. From a basic point of view, perovskites are an exotic class of hybrid materials combining some merits of organic and inorganic semiconductors: large optical absorption, large mobilities, and tunable band gap together with the possibility to be processed in solution. When a novel class of promising semiconductors comes into the limelight, lively discussions ensue on the photophysics of band-edge excitations, because just the states close to the band edge are entailed in energy/charge transport and light emission. This was the case several decades ago for III-V semiconductors, it has been up to 10 years ago for organics, and it is currently the case for perovskites. Our aim in this Account is to rationalize the body of experimental evidence on perovskite photophysics in a coherent theoretical framework, borrowing from the knowledge acquired over the years in materials optoelectronics. A crucial question is whether photon absorption leads to a population of unbound, conductive free charges or instead excitons, neutral and insulating bound states created by Coulomb interaction just below the energy of the band gap. We first focus on the experimental estimates of the exciton binding energy (Eb): at room temperature, Eb is comparable to the thermal energy kBT in MAPbI3 and increases up to values 2-3kBT in wide band gap MAPbBr3 and MAPbCl3. Statistical considerations predict that these values, even though comparable to or larger than thermal energy, let free carriers prevail over bound excitons for all levels of excitation densities relevant for devices. The analysis of photophysics evidence confirms that all hybrid halide perovskites behave as free-charge semiconductors. Thanks to such property, in combination with band gap energies covering the entire solar spectrum, perovskites represent a promising materials platform for highly efficient, single and multijunction solar cells. Concerning the use of perovskites as color-tunable materials in light emitting devices, free-charges are not the preferred species, as they recombine radiatively through a bimolecular process that is inefficient at the charge-injection levels typical of LED operation. Strategies to overcome this limit, and thus extend the use of perovskite materials beyond solar energy conversion, could be borrowed from inorganic semiconductor optoelectronics and include the fabrication of nanostructures with reduced dimensionality to alter the electronic density of states, as well as engineering composite materials.
RESUMEN
Advances of optoelectronic devices based on methylammonium lead halide perovskites depend on understanding the role of excitons, whether it is marginal as in inorganic semiconductors, or crucial, like in organics. However, a consensus on the exciton binding energy and its temperature dependence is still lacking, even for widely studied methylammonium lead iodide and bromide materials (MAPbI3, MAPbBr3). Here we determine the exciton binding energy based on an f-sum rule for integrated UV-vis absorption spectra, circumventing the pitfalls of least-squares fitting procedures. In the temperature range 80-300 K, we find that the exciton binding energy in MAPbBr3 is EB = (60 ± 3) meV, independent of temperature; for MAPbI3, in the orthorhombic phase (below 140 K) EB = (34 ± 3) meV, while in the tetragonal phase the binding energy softens to 29 meV at 170 K and stays constant up to 300 K. Implications of binding energy values on solar cell and LED workings are discussed.
RESUMEN
Multilayered epitaxial nanofibers are exemplary model systems for the study of exciton dynamics and lasing in organic materials because of their well-defined morphology, high luminescence efficiencies, and color tunability. We use temperature-dependent continuous wave and picosecond photoluminescence (PL) spectroscopy to quantify exciton diffusion and resonance-energy transfer (RET) processes in multilayered nanofibers consisting of alternating layers of para-hexaphenyl (p6P) and α-sexithiophene (6T) serving as exciton donor and acceptor material, respectively. The high probability for RET processes is confirmed by quantum chemical calculations. The activation energy for exciton diffusion in p6P is determined to be as low as 19 meV, proving p6P epitaxial layers also as a very suitable donor material system. The small activation energy for exciton diffusion of the p6P donor material, the inferred high p6P-to-6T resonance-energy-transfer efficiency, and the observed weak PL temperature dependence of the 6T acceptor material together result in an exceptionally high optical emission performance of this all-organic material system, thus making it well suited, for example, for organic light-emitting devices.
RESUMEN
Biosensing technologies based on plasmonic nanostructures have recently attracted significant attention due to their small dimensions, low-cost and high sensitivity but are often limited in terms of affinity, selectivity and stability. Consequently, several methods have been employed to functionalize plasmonic surfaces used for detection in order to increase their stability. Herein, a plasmonic surface was modified through a controlled, silica platform, which enables the improvement of the plasmonic-based sensor functionality. The key processing parameters that allow for the fine-tuning of the silica layer thickness on the plasmonic structure were studied. Control of the silica coating thickness was achieved through a combined approach involving sol-gel and dip-coating techniques. The silica films were characterized using spectroscopic ellipsometry, contact angle measurements, atomic force microscopy and dispersive spectroscopy. The effect of the use of silica layers on the optical properties of the plasmonic structures was evaluated. The obtained results show that the silica coating enables surface protection of the plasmonic structures, preserving their stability for an extended time and inducing a suitable reduction of the regeneration time of the chip.
RESUMEN
A unique example of discrete molecular entity Nd(y)Er(x)Yb(3-(x+y))Q9 (1) (Q = quinolinolato) containing three different lanthanides simultaneously emitting in three different spectral regions in the NIR, ranging from 900 to 1600â nm, has been synthesized and fully chararacterized. A simple molecular strategy based on tuning metal composition in the Ln3Q9 framework, which contains inequivalent central and terminal coordination sites, has allowed a satisfactory ion-size-driven control of molecular speciation close to 90%. In 1 the central position of the larger Nd ion is well distinguished from the terminal ones of the smaller Yb(3+) and Er(3+), which are almost "vicariants" as found in the heterobimetallic Er(x)Yb(3-x)Q9 (2). The Ln3Q9 molecular architecture, which allows communication between the ions, has proved to afford multiple NIR emission in 1 and 2, and is promising to develop a variety of multifunctional materials through the variation of the Ln composition.