Influence of Cotton Pre-Treatment on Dyeing with Onion and Pomegranate Peel Extracts.

In this paper the possibility of applying natural dyes on cellulose fibres were researched with respect to the impact of cotton material pre-treatment (scouring, chemical bleaching, mercerization and mordanting), using renewable sources of natural dyes (waste as a source). As mordants, metal salts of copper, aluminium and ferrum were used, and the influence on colour change as well as on fastness properties were analysed. The natural dyes were extracted from onion peel (Allium cepa L.) and pomegranate peel (Punica granatum L.). In spectrophotometric analysis performed of the plant extracts, the onion extract has peaks at 400 and 500 nm, resulting in red-orange colourations and the pomegranate extract shows a maximum at 400 nm, i.e., in the yellow region, which is characteristic of punicalin. Results show significant influence of cotton pre-treatments on colour appearance and fastness properties, caused by pre-treatments affecting the properties and structure of the cotton itself. The positive effect of mercerization on dye absorption and bonding is confirmed. For wash and light fastness properties, more satisfactory results have been obtained for yarns dyed with pomegranate peel natural dye, and the key importance of mordants for fastness properties has been confirmed.

Sustainable Alkaline Hydrolysis of Polyester Fabric at Low Temperature.

High crystallinity leads to low hydrophilicity of fabric made of (poly(ethylene terephthalate)) fibers (PET) causing problems in finishing, washing, and dyeing processes. To improve these properties, the surface of PET fibers is usually modified by hydrolysis. Alkaline hydrolysis is a conventional process usually performed at a temperature higher than 100 °C for more than 1 h. However, the use of strong alkali and high processing temperatures (>100 °C) can lead to fabric damage and a negative impact on the environment. Therefore, in this paper, the possibility of hydrolysis of the PET fibers in the fabric in a sustainable, energy-efficient process was researched. The influence of low temperature (60-100 °C) and an accelerator (a cationic surfactant HDTMAC) to PET alkaline hydrolysis was studied through weight loss, the loss in breaking force, and fiber morphology. The kinetics of PET dissolution in 1.5 mol cm-3 NaOH at low temperature with and without the addition of HDTMAC was determined and the activation energy was calculated according to the theoretical model. It has been confirmed that PET hydrolysis can be carried out in 1.5 mol cm-3 NaOH with the addition of HDTMAC as an accelerator at 80 °C for 10 min. This process is more economically and energetically acceptable than the conventional process, and is therefore more sustainable.