RESUMEN
Magnetic Fe(2)O(3)/carbon hybrids were prepared in a two-step process. First, acetic acid vapor interacted with iron cations dispersed on the surface of a nanocasted ordered mesoporous carbon (CMK-3). In the second step, the primarily created iron acetate species underwent pyrolysis and transformed to magnetic iron oxide nanoparticles. X-ray diffraction, Fourier-transform infrared, and Raman spectroscopies were used for the chemical and structural characterization of the hybrids, while surface area measurements, thermal analysis, and transmission electron microscopy were employed to determine their physical, surface, and textural properties. These results revealed the preservation of the host carbon structure, which was homogenously and controllably loaded (up to 27 wt %) with nanosized (ca. 20 nm) iron oxides inside the mesoporous system. Mössbauer spectroscopy and magnetic measurements at low temperatures confirmed the formation of γ-Fe(2)O(3) nanoparticles exhibiting superparamagnetic behavior. The kinetic studies showed a rapid removal of Cr(VI) ions from the aqueous solutions in the presence of these magnetic mesoporous hybrids and a considerably increased adsorption capacity per unit mass of sorbent in comparison to that of pristine CMK-3 carbon. The results also indicate highly pH-dependent sorption efficiency of the hybrids, whereas their kinetics was described by a pseudo-second-order kinetic model. Taking into account the simplicity of the synthetic procedure and possibility of magnetic separation of hybrids with immobilized pollutant, the developed mesoporous nanomaterials have quite real potential for applications in water treatment technologies.
RESUMEN
A lightweight, oxygen-rich carbon foam was prepared and doped with Pd/Hg alloy nanoparticles. The composite revealed high H2 sorption capacity (5 wt%) at room temperature and moderate pressure (2 MPa). The results were explained on the basis of the H2 spillover mechanism using Density Functional Theory.