RESUMEN
Polytetrafluoroethylene (PTFE) is a potential candidate for the fabrication of flexible electronics devices and electronics with applications in various extreme environments, mainly due to its outstanding chemical and physical properties. However, to date, the utilization of PTFE in printing trials has been limited due to the material's low surface tension and wettability, which do not ensure good adhesion of the printing ink at the level of the substrate. Within this paper, successful printing of PTFE is realized after pre-treating the surface of the substrate with the help of dielectric barrier discharge non-thermal plasma. The efficiency of the pre-treatment is demonstrated with respect to both silver- and carbon-based inks that are commercially available, and finally, the long-lasting pre-treatment effect is demonstrated for periods of time spanning from minutes to days. The experimental results are practically paving the way toward large-scale utilization of PTFE as substrate in fabricating printed electronics in harsh working environments. After 3 s of plasma treatment of the foil, the WCA decreased from approximately 103° to approximately 70°. The resolution of the printed lines of carbon ink was not time dependent and was unmodified, even if the printing was realized within 1 min from the time of applying the pre-treatment or 10 days later. The evaluation of the surface tension (σ) measured with Arcotest Ink Pink showed an increase in σ up to 40 < σ < 42 mN/m for treated Teflon foil and from σ < 30 mN/m corresponding to the untreated substrate. The difference in resolution was distinguishable when increasing the width of the printed lines from 500 µm to 750 µm, but when increasing the width from 750 µm to 1000 µm, the difference was minimal.
RESUMEN
The efficiency of photovoltaics (PVs) is related to cover material properties and light management in upper layers of the device. This article investigates new polyimide (PI) covers for PVs that enable light trapping through their induced surface texture. The latter is attained via a novel strategy that involves multi-directional rubbing followed by plasma exposure. Atomic force microscopy (AFM) is utilized to clarify the outcome of the proposed light-trapping approach. Since a deep clarification of either random or periodic surface morphology is responsible for the desired light capturing in solar cells, the elaborated texturing procedure generates a balance among both discussed aspects. Multidirectional surface abrasion with sand paper on pre-defined directions of the PI films reveals some relevant modifications regarding both surface morphology and the resulted degree of anisotropy. The illuminance experiments are performed to examine if the created surface texture is suitable for proper light propagation through the studied PI covers. The adhesion among the upper layers of the PV, namely the PI and transparent electrode, is evaluated. The correlation between the results of these analyses helps to identify not only adequate polymer shielding materials, but also to understand the chemical structure response to new design routes for light-trapping, which might significantly contribute to an enhanced conversion efficiency of the PV devices.
RESUMEN
This study aims to present the properties of the polymeric films after being subjected to DBD plasma treatment in atmospheric conditions. Three different commercial films of polyester (Xerox Inkjet transparencies and Autostat CUS5 Clear film) and polycarbonate (Lexan™ 8010 MC) have been considered for the tests. The surface wettability has been evaluated based on static water contact angle (WCA) for different treatment times varying between 0.2 s and 30 s, the results revealing a maximum WCA decrease compared to a pristine of up to 50% for Xerox films, 75% for Autostat and 70% for Lexan. The persistence of the hydrophilic effect induced by the plasma treatment has also been verified for up to 72 h of storage after treatment, the results indicating a degradation of the treatment effects starting with the first hours after the treatment. The WCA stabilizes to a value inferior to the one corresponding to pristine in the first 24 h after plasma treatment. The adhesion forces, as well as preliminary surface morphology evaluations have been determined for the considered films using atomic force microscopy (AFM). The adhesion forces are increased together with the prolongation of the plasma treatment application time, varying from initial values of 165 nN, 58 nN and 204 nN to around 390 nN, 160 nN and 375 nN for Xerox, Autostat and Lexan films, respectively, after 5 s of DBD treatment. For the considered materials, the results revealed that the plasma treatment determines morphological changes of the surfaces indicating an increase in surface roughness.
RESUMEN
Plasma activated water (PAW) can represent an alternative to chemical fertilizers in agriculture. The effects of PAW treatment applied in two concentrations (1.5 or 3.0 mg L-1 NO3-) on some morphological, physiological, biochemical parameters and yield of Lactuca sativa L. grown in two different pot volumes (400 or 3200 cm3) were investigated in this study. The results showed that both PAW concentrations did not influence the germination, once the process was initiated. Positive effects of the treatments were registered on the length of radicle and hypocotyls of lettuce at a concentration of 1.5 mg L-1 NO3- (PAW I), the chlorophyll content was significantly increased at a concentration of 3.0 mg L-1 NO3- (PAW II) and bigger pot volume, also the foliar weight and area. No significant differences between the treated and untreated plants were recorded for the root weight, leaf length and width. The dry weight was significantly higher for the lettuce treated with PAW I and II grown in big volume pots at 57 days after transplanting (DAT) and small volume pots at 64 DAT. The nitrites content of the lettuce grown in big pots was lower than of the lettuce grown in small pots, regardless of the PAW treatment. Contrary, the nitrates content was higher in the lettuce grown in big pots (up to 36.4 mg KNO3/g DW), compared to small pots (under 0.3 mg KNO3/g DW).