Selective determination of ellagic acid in aqueous solution using blue-green emissive copper nanoclusters.

Development of beneficial sensors to analyze ellagic acid concentrations is of great importance for food safety and human health. Herein, a facile and fast fluorescent probe was carried out for the excellently selective and sensitive measurement of ellagic acid in real samples through histidine protected copper nanoclusters (histidine@Cu NCs) as a nanosensor. This as-developed histidine@Cu NCs were performed through UV-vis absorption spectroscopy, fluorescence spectroscopy, transmission electron microscopy, Fourier-transform infrared spectroscopy, X-ray photoelectron spectroscopy and fluorescence lifetime analysis. The TEM image revealed that this nanomaterial had spherical features with the average diameter of 2.5 ± 0.05 nm. The blue-green fluorescence of this Cu NCs was found under the UV light. Meanwhile, the maximum excitation and emission wavelength were located at 387 nm and 488 nm. After addition of ellagic acid, the fluorescence of histidine@Cu NCs was slowly weakened with excellent linear range of 0.5-300 µM and detection limit of 0.077 µM. The fluorescence weakening mechanism of this nanosensor were attributed to the inner filter effect (IFE) and static quenching. Finally, this as-established analysis platform was successfully employed to measure ellagic acid in real samples.

One-step synthesis of blue emission copper nanoclusters for the detection of furaltadone and temperature.

Polyvinyl pyrrolidone (PVP), playing roles as a templating agent, can be applied to prepare blue-emitting copper nanoclusters (Cu NCs@PVP) on the basis of a rapid chemical reduction synthesis method. The Cu NCs@PVP displayed a blue emission wavelength at 430 nm and the corresponding quantum yield (QY) could reach 10.4%. Subsequently, the as-synthesized Cu NCs@PVP were used for the trace analysis of furaltadone based on the inner filter effect (IFE) between Cu NCs@PVP and furaltadone, which caused the fluorescence to be effectively quenched. Additionally, this proposed determination platform based on the Cu NCs@PVP for furaltadone sensing possessed an excellent linear range from 0.5 to 100 µM with a lower detection limit of 0.045 µM (S/N = 3). Meanwhile, the Cu NCs@PVP also could be applied for the sensing of temperature. Furthermore, the practicability of the sensing platform has been successfully verified by measuring furaltadone in real samples, affirming its potential to increase fields for the determination of furaltadone.

One facile fluorescence strategy for sensitive determination of baicalein using trypsin-templated copper nanoclusters.

Herein, we established a fluorescent detection platform for baicalein (Bai) based on copper nanoclusters, which were prepared by using copper sulfate as the precursor, trypsin (Tryp) as the template and hydrazine hydrate as the reducing agent. The entire preparation and testing process were rapid, facile and green. Many characterization methods, such as UV-vis absorption spectroscopy, fluorescence spectroscopy, fourier transform infrared spectroscopy (FT-IR), fluorescence lifetime, transmission electron microscope (TEM) and X-ray photoelectron spectroscopy (XPS), were applied for the analysis of trypsin-templated copper nanoclusters (Cu NCs@Tryp). The Cu NCs@Tryp released green fluorescence at maximum emission wavelength of 457 nm under maximum excitation wavelength of 377 nm. More importantly, the fluorescence of Cu NCs@Tryp was efficiently quenched by Bai. According to this phenomenon, a facile, rapid and selective turn-off fluorescence probe for Bai sensing was developed. Under the optimized testing conditions, the ln(F0/F) value and concentration of Bai displayed excellent linear relationship changing from 0.5 to 60 µM (R2 = 0.9969), and the detection limit was 0.078 µM. Furthermore, the Cu NCs@Tryp has been successfully employed to measure the amount of Bai in bovine serum samples with satisfactory recoveries.