RESUMEN
This paper proposes molecular and supramolecular concepts for potential application in perovskite solar cells. New air-stable symmetrical imine, with thiadiazole moieties PPL2: (5E,6E)-N2,N5-bis(4-(diphenylamino)benzylidene)-1,3,4-thiadiazole-2,5-diamine), as a hole-transporting material was synthesised in a single-step reaction, starting with commercially available and relatively inexpensive reagents, resulting in a reduction in the cost of the final product compared to Spiro-OMeTAD. Moreover, camphorsulfonic acid (CSA) in both enantiomeric forms was used to change the HOMO-LUMO levels and electric properties of the investigated imine-forming complexes. Electric, optical, thermal, and structural studies of the imine and its complexes with CSA were carried out to characterise the new material. Imine and imine/CSA complexes were also characterised in depth by the proton Nuclear Magnetic Resonance 1H NMR method. The position of nitrogen in the thidiazole ring influences the basicity of donor centres, which results in protonation in the imine bond. Simple devices of ITO/imine (with or without CSA(-) or CSA(+))/Ag/ITO architecture were constructed, and a thermographic camera was used to find the defects in the created devices. Electric behaviour was also studied to demonstrate conductivity properties under the forward current. Finally, the electrical properties of imine and its protonated form with CSA were compared with Spiro-OMeTAD. In general, the analysis of thermal images showed a very similar response of the samples to the applied potential in terms of the homogeneity of the formed organic layer. The TGA analysis showed that the investigated imine exhibits good thermal stability in air and argon atmospheres.
RESUMEN
The A-site cation-ordered GdBa0.5Sr0.5Co2-xCuxO5+δ (GBSCC) double perovskites are evaluated regarding the development of high-performance oxygen electrodes for reversible solid oxide cells (rSOCs). The aims are to maximally decrease the content of toxic and expensive cobalt by substitution with copper while at the same time improving or maintaining the required thermomechanical and electrocatalytic properties. Studies reveal that compositions with 1 ≤ x ≤ 1.15 are particularly interesting. Their thermal and chemical expansions are decreased, and sufficient transport properties are observed. Complementary density functional theory calculations give deeper insight into oxygen defect formation in the considered materials. Chemical compatibility with La0.8Sr0.2Ga0.8Mg0.2O3-δ (LSGM) and Ce0.9Gd0.1O2-δ (GDC) solid electrolytes is evaluated. It is documented that the GdBa0.5Sr0.5Co0.9Cu1.1O5+δ oxygen electrode enables obtaining very low electrode polarization resistance (Rp) values of 0.017 Ω cm2 at 850 °C as well as 0.111 Ω cm2 at 700 °C, which is lower in comparison to that of GdBa0.5Sr0.5CoCuO5+δ (respectively, 0.026 and 0.204 Ω cm2). Systematic distribution of relaxation times analyses allows studies of the electrocatalytic activity and distinguishing elementary steps of the electrochemical reaction at different temperatures. The rate-limiting process is found to be oxygen atom reduction, while the charge transfer at the electrode/electrolyte interface is significantly better with LSGM. The studies also allow elaborating on the catalytic role of the Ag current collector as compared with Pt. The electrodes manufactured using materials with x = 1 and 1.1 permit reaching high power outputs, exceeding 1240 mW cm-2 at 850 °C and 1060 mW cm-2 at 800 °C, for the LSGM-supported cells, which can also work in the electrolysis mode.
RESUMEN
Planar perovskite solar cells were fabricated on F-doped SnO2 (FTO) coated glass substrates, with 4,4'-((1E,1'E)-((1,2,4-thiadiazole-3,5-diyl)bis(azaneylylidene))bis(methaneylylidene))bis(N,N-di-p-tolylaniline) (bTAThDaz) as hole transport material. This imine was synthesized in one step reaction, starting from commercially available and relatively inexpensive reagents. Electrochemical, optical, electrical, thermal and structural studies including thermal images and current-voltage measurements of the full solar cell devices characterize the imine in details. HOMO-LUMO of bTAThDaz were investigated by cyclic voltammetry (CV) and energy-resolved electrochemical impedance spectroscopy (ER-EIS) and were found at -5.19 eV and -2.52 eV (CV) and at -5.5 eV and -2.3 eV (ER-EIS). The imine exhibited 5% weight loss at 156 °C. The electrical behavior and photovoltaic performance of the perovskite solar cell was examined for FTO/TiO2/perovskite/bTAThDaz/Ag device architecture. Constructed devices exhibited good time and air stability together with quite small effect of hysteresis. The observed solar conversion efficiency was 14.4%.