Mechanical and corrosion resistance of a new nanostructured Ti-Zr-Ta-Nb alloy.

In this work, a multi-elementary Ti-10Zr-5Nb-5Ta alloy, with non-toxic alloying elements, was used to develop an accumulative roll bonding, ARB-type procedure in order to improve its structural and mechanical properties. The alloy was obtained by cold crucible semi-levitation melting technique and then was ARB deformed following a special route. After three ARB cycles, the total deformation degree per layer is about 86%; the calculated medium layer thickness is about 13 µm. The ARB processed alloy has a low Young's modulus of 46 GPa, a value very close to the value of the natural cortical bone (about 20 GPa). Data concerning ultimate tensile strength obtained for ARB processed alloy is rather high, suitable to be used as a material for bone substitute. Hardness of the ARB processed alloy is higher than that of the as-cast alloy, ensuring a better behaviour as a implant material. The tensile curve for the as-cast alloy shows an elastoplastic behaviour with a quite linear elastic behaviour and the tensile curve for the ARB processed alloy is quite similar with a strain-hardening elastoplastic body. Corrosion behaviour of the studied alloy revealed the improvement of the main electrochemical parameters, as a result of the positive influence of ARB processing. Lower corrosion and ion release rates for the ARB processed alloy than for the as-cast alloy, due to the favourable effect of ARB thermo-mechanical processing were obtained.

In vitro biocompatibility and corrosion resistance of a new implant titanium base alloy.

One objective of this work was to study the corrosion resistance of the new implant Ti-10Zr-5Ta-5Nb alloy in physiological fluids of different pH values, simulating the extreme functional conditions. Another objective was in vitro biocompatibility evaluation of the new alloy using human fetal osteoblast cell line hFOB 1.19. Cytocompatibility was assessed by determination of possible material cytotoxic effects, cell morphology and cell adhesion. The thermo-mechanical processing of the new implant alloy consisted in plastic deformation (almost 90%) performed by hot rolling accompanied by an initial and final heat treatment. The new Ti-10Zr-5Ta-5Nb alloy presented self-passivation, with a large passive potential range and low passive current densities, namely, a very good anticorrosive resistance in Ringer solution of acid, neutral and alkaline pH values. Cell viability was not affected by the alloy substrate presence and a very good compatibility was noticed.

Accidental ethyl mercury poisoning with nervous system, skeletal muscle, and myocardium injury.

Four case reports are presented of patients who ate the meat of a hog inadvertently fed seed treated with fungicides containing ethyl mercury chloride. The clinical, electrophysiological, and toxicological, and in two of the patients the pathological data, showed that this organic mercury compound has a very high toxicity not only for the brain, but also for the spinal motoneurones, peripheral nerves, skeletal muscles, and myocardium.