The high thermal conductivity of polycrystalline diamond makes it ideally suited for thermal management solutions for gallium nitride (GaN) devices, with a diamond layer grown on an aluminum nitride (AlN) interlayer atop the GaN stack. However, this application is limited by the thermal barrier at the interface between diamond and substrate, which has been associated with the transition region formed in the initial phases of growth. In this work, in situ spectroscopic ellipsometry (SE) is employed to monitor early-stage microwave plasma-enhanced chemical vapor deposition diamond growth on AlN. An optical model was developed from ex situ spectra and applied to spectra taken in situ during growth. Coalescence of separate islands into a single film was marked by a reduction in bulk void fraction prior to a spike in sp2 fraction due to grain boundary formation. Parameters determined by the SE model were corroborated using Raman spectroscopy and atomic force microscopy.
RESUMEN
Integrating diamond with GaN high electron mobility transistors (HEMTs) improves thermal management, ultimately increasing the reliability and performance of high-power high-frequency radio frequency amplifiers. Conventionally, an amorphous interlayer is used before growing polycrystalline diamond onto GaN in these devices. This layer contributes significantly to the effective thermal boundary resistance (TBReff) between the GaN HEMT and the diamond, reducing the benefit of the diamond heat spreader. Replacing the amorphous interlayer with a higher thermal conductivity crystalline material would reduce TBReff and help to enable the full potential of GaN-on-diamond devices. In this work, a crystalline Al0.32Ga0.68N interlayer has been integrated into a GaN/AlGaN HEMT device epitaxy. Two samples were studied, one with diamond grown directly on the AlGaN interlayer and another incorporating a thin crystalline SiC layer between AlGaN and diamond. The TBReff, measured using transient thermoreflectance, was improved for the sample with SiC (30 ± 5 m2 K GW-1) compared to the sample without (107 ± 44 m2 K GW-1). The reduced TBReff is thought to arise from improved adhesion between SiC and the diamond compared to the diamond directly on AlGaN because of an increased propensity for carbide bond formation between SiC and the diamond. The stronger carbide bonds aid transmission of phonons across the interface, improving heat transport.
RESUMEN
In this work we have demonstrated the growth of nanocrystalline diamond on boron nitride ceramic. We measured the zeta potential of the ceramics to select the diamond seeds. Diamond was then grown on the seeded ceramics using a microwave chemical vapour deposition system. A clear difference was found between the samples which were seeded with nanodiamond and the ones not seeded before growth. Raman spectroscopy confirmed the excellent quality of the diamond film. Dielectric measurements showed an increase in the dielectric constant of the material after diamond growth. The diamond was also doped with boron to make it superconducting. The film had a transition temperature close to 3.4 K. Similar strategies can be applied for the growth of diamond on other types of ceramics.